激光技术, 2015, 39 (5): 702, 网络出版: 2015-09-10   

z轴单层行程对激光熔覆成形的影响

Effect of single z-increment on laser cladding forming
作者单位
1 大连理工大学 可持续设计与制造研究所, 大连 116024
2 大连理工大学 材料科学与工程学院, 大连 116024
摘要
为了探究z轴单层行程Δz与单层熔覆层高度的匹配对激光熔覆成形的影响,采用了在不同的z轴单层行程Δz的情况下进行激光熔覆成形试验的方法,通过理论分析和实验验证,得到了不同z轴单层行程Δz与单层熔覆层高度以及离焦量的关系曲线.结果表明,z轴单层行程Δz存在一个以第2层熔覆层高度为基准的最佳的取值范围,在此范围内,熔覆过程能够通过自身存在的反馈调节达到z轴单层行程Δz与单层熔覆层高度相等的稳定成形状态.该研究给出z轴单层行程Δz选取时的推荐值为0.5d2≤Δz≤0.6d2.
Abstract
To study effect of the matching of z-axis single increment (Δz) with single cladding layer height on laser cladding forming,experiments of laser cladding forming were carried out at different Δz.The relationship curves of different Δz,single cladding layer height and defocusing were obtained after theoretical analysis and experimental verification.The results show that the optimal range of Δz is based on the second cladding layer height.In this range,the process of cladding would reach a steady forming state by feedback regulation.A recommended value of Δz (0.5d2≤Δz≤0.6d2) is provided.

王鑫林, 邓德伟, 胡恒, 宋弘韬, 张洪潮. z轴单层行程对激光熔覆成形的影响[J]. 激光技术, 2015, 39(5): 702. WANG Xinlin, DENG Dewei, HU Heng, SONG Hongtao, ZHANG Hongchao. Effect of single z-increment on laser cladding forming[J]. Laser Technology, 2015, 39(5): 702.

本文已被 3 篇论文引用
被引统计数据来源于中国光学期刊网
引用该论文: TXT   |   EndNote

相关论文

加载中...

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!