强激光与粒子束, 2015, 27 (9): 092005, 网络出版: 2015-11-30  

固化温度对聚苯乙烯空心微球质量的影响

Influence of curing temperature on quality of polystyrene shells
作者单位
1 西南科技大学 材料科学与工程学院, 四川 绵阳 621010
2 中国工程物理研究院 激光聚变研究中心, 四川 绵阳 621900
摘要
在乳液微封装技术制备聚苯乙烯空心微球的工艺中,固化过程是决定微球球形度及壁厚均匀性的关键阶段。基于乳粒发生器制备内径(850±10) μm、壁厚(250±25) μm的复合乳粒,以25 ℃,45 ℃和65 ℃作为固化温度,考察了固化温度对微球球形度和壁厚均匀性的影响。结果表明,固化温度越低,界面张力越高,乳液固化速率越慢,微球球形度和壁厚均匀性越好。当固化温度为25 ℃时,批次微球中球形偏离值优于2 μm的微球产率为90%,壁厚偏差值优于2 μm的微球产率为40%,明显优于固化温度为45 ℃和65 ℃时微球的质量。
Abstract
During the fabrication process of polystyrene (PS) shells by emulsion microencapsulation method, solidification is a critical stage that influences the sphericity and wall thickness uniformity. The diameter and wall thickness of compound droplets prepared by the droplet generator were (850±10) μm and (250±25) μm respectively. To study the effects of curing temperature on the sphericity and wall thickness uniformity, the curing temperature was set at 25 ℃, 45 ℃ and 65 ℃. The experimental results show that lower temperature improves the sphericity and wall thickness uniformity due to higher interfacial tension and slower velocity of emulsion solidification. When the curing temperature was 25 ℃, the batch yield of PS shells with difference between the maximum and minimum radii less than 2 μm is 90%, and with the maximum deviation of wall thickness less than 2 μm is 40%, obviously better than that prepared at 45 ℃ and 65 ℃.

胡阳鹏, 刘梅芳, 陈素芬, 易勇, 张占文. 固化温度对聚苯乙烯空心微球质量的影响[J]. 强激光与粒子束, 2015, 27(9): 092005. Hu Yangpeng, Liu Meifang, Chen Sufen, Yi Yong, Zhang Zhanwen. Influence of curing temperature on quality of polystyrene shells[J]. High Power Laser and Particle Beams, 2015, 27(9): 092005.

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!