基于太赫兹时域光谱的玻璃纤维缺陷深度检测及数据分析

Defects Depth Inspection and Data Analysis of Glass Fiber Based on THz-TDS
作者单位
1 中国计量大学机电工程学院,浙江 杭州 310018
2 中国计量大学质量与安全工程学院,浙江 杭州 310018
摘要
太赫兹波对很多介电材料和非极性的液体具有透射性且THz 波辐射的光子能量低,近年来在无损检测领域得到了较快的发展和应用。基于透射式THz-TDS 系统在室温下对包含不同深度缺陷信息的车载气瓶玻璃纤维增强复合材料检测,获得了0.2~1.8 THz 范围内样品的时域波形,分析其峰峰值、最大值、延迟时间、折射率和吸收系数,结果表明,随着样品缺陷深度的增加,峰峰值、最大值和延迟时间都有明显的变化规律,同时样品的折射率和吸收系数也不同。可以通过分析时域波形的变化以及折射率和吸收系数的变化,获得缺陷的深度信息。
Abstract
Terahertz wave is able to penetrate dielectric material and non-polar liquids, and its photonenergy is low. It was widely used in nondestructive testing fields. The vehicle gas cylinder glass fiberreinforced composite material of including different defects depth information was detectednondestructively at room temperature by the transmission THz-TDS system. The time domain waveformof the sample was gained and its peak-to-peak value, maximum value, the delay time, refractive index andabsorption coefficient were analyzed from 0.2 THz to 1.8 THz. The results show that with the increase ofthe sample defects depth, peak-to-peak value, maximum value and the delay time has obvious variationtrend. Additionally, the refractive index and absorption coefficient of the sample are different. The methodcan be applied to gain the information of the defects depth by analyzing the variation of time domain wave,refractive index and absorption coefficient.

郭小弟, 王强, 谷小红, 陈锡爱, 范昕炜. 基于太赫兹时域光谱的玻璃纤维缺陷深度检测及数据分析[J]. 红外技术, 2016, 38(7): 602. GUO Xiaodi, WANG Qiang, GU Xiaohong, CHEN Xiai, FAN Xinwei. Defects Depth Inspection and Data Analysis of Glass Fiber Based on THz-TDS[J]. Infrared Technology, 2016, 38(7): 602.

本文已被 6 篇论文引用
被引统计数据来源于中国光学期刊网
引用该论文: TXT   |   EndNote

相关论文

加载中...

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!