光子学报, 2017, 46 (1): 0116002, 网络出版: 2017-02-09   

银铜双原子MACE法可控制备倒金字塔多晶黑硅的结构与性能

Structures and Properties of Black Multicrystalline Silicon with a Structure of Invert Pyramid Prepared Controllably by Ag and Cu Dually Assisted Chemical Etching Method
作者单位
1 南京航空航天大学 材料科学与技术学院 江苏省能量转换材料与技术重点实验室, 南京 210016
2 江苏辉伦太阳能科技有限公司, 南京 210061
摘要
采用一步银铜双原子金属辅助化学腐蚀法, 室温下在多晶硅表面制备纳米陷光结构, 再利用纳米结构修正溶液在温度为50℃时对硅片进行各向异性重构, 可控制备出不同尺寸的倒金字塔陷光结构.用分光光度计测量了多晶硅表面的反射率, 用扫描电镜观察了多晶硅表面形貌, 用少子寿命测试仪测量了多晶硅钝化后的少子寿命.结果表明: 影响倒金字塔结构尺寸的主要影响因素是制备态黑硅纳米结构的深度, 当深度越深, 最终形成的结构尺寸也越大; 纳米结构修正溶液重构时间越长, 所形成的倒金字塔结构尺寸越大, 反射率也变大; 经原子层沉积钝化后的倒金字塔结构中少子寿命随其尺寸的增大而增加; 当倒金字塔边长为600 nm时综合效果最佳, 反射率为9.87%, 少子寿命为37.82 μs.
Abstract
Using by the method of one step Ag and Cu dual elements based Metal Assisted Chemical Etching(MACE), a nano-light trapping structure was prepared at a room temperature on the surface of the multicrystalline silicon. Then, the silicon wafers were made an anisotropic refactoring using by a Nano Structure Rebuilding (NSR) solution at a temperature of 50℃, so that the invert pyramid light trapping structures with different sizes were prepared. The reflectance and surface morphologies of multicrystalline silicon, and the minority carrier lifetime of the passivated multicrystalline silicon were measured by spectrophotometer, scanning electron microscopy and Sinton WCT-120 tool respectively. The results show that, the main factor to affect the final size of invert pyramid structure is the depth of the as-etched nanostructure. The deeper the depth is, the larger the final size of invert pyramid structure becomes. With the increase of NSR refactoring time, the size of the invert pyramid structure goes larger and the reflectance becomes higher too. While the minority carrier lifetime increases with the increasing of the size of invert pyramids after atomic layer deposition passivating, one should make a balance between anti-reflection result and passivation effect. An invert pyramid with an edge length of 600 nm is found to be an optimal size, corresponding a reflectance of 9.87% and a minority carrier lifetime of 37.82 μs.

郑超凡, 沈鸿烈, 蒲天, 蒋晔, 李玉芳, 唐群涛, 杨楠楠, 金磊. 银铜双原子MACE法可控制备倒金字塔多晶黑硅的结构与性能[J]. 光子学报, 2017, 46(1): 0116002. ZHENG Chao-fan, SHEN Hong-lie, PU Tian, JIANG Ye, LI Yu-fang, TANG Qun-tao, YANG Nan-nan, JIN Lei. Structures and Properties of Black Multicrystalline Silicon with a Structure of Invert Pyramid Prepared Controllably by Ag and Cu Dually Assisted Chemical Etching Method[J]. ACTA PHOTONICA SINICA, 2017, 46(1): 0116002.

本文已被 2 篇论文引用
被引统计数据来源于中国光学期刊网
引用该论文: TXT   |   EndNote

相关论文

加载中...

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!