铜含量变化对Cu(In,Ga)Se2薄膜微结构的影响

Influence of various Cu contents on the microstructure of Cu(In,Ga)Se2 thin films
作者单位
1 中国科学院上海技术物理研究所 红外物理国家重点实验室, 上海 200083
2 上海太阳能电池研究与发展中心, 上海 200083
摘要
报道了不同的铜含量(Cu/(Ga+In)=0.748~0.982)对Cu(In,Ga)Se2 (CIGS)薄膜微结构的影响.文章中的CIGS薄膜采用磁控溅射金属预置层后硒化的方法制备, 其X射线衍射谱(XRD)中一系列黄铜矿结构CIGS(CH-CIGS)相的衍射峰确认了CH-CIGS相的存在.对CIGS薄膜拉曼光谱的分析表明, 随着铜含量的上升, CIGS薄膜经历了CH-CIGS和有序缺陷化合物(OVC)混合相、CH-CIGS单相、CH-CIGS和CuxSe混合相三种状态.进一步的分析显示, CIGS薄膜拉曼峰的半高宽随铜含量变化, 并在Cu/(Ga+In)=0.9附近时达到最小值, 这说明此时CIGS薄膜具有更好的结晶度和更少的无序性.此外还得到了CIGS薄膜拉曼峰半高宽与铜含量的经验关系公式.这些研究表明拉曼光谱能比XRD更加灵敏地探测CIGS薄膜的微结构, 可望作为一种无损和快速测量方法, 用于对CIGS薄膜晶相和铜含量的初步估计.
Abstract
The influence of different Cu contents (Cu/(Ga+In)=0.748~0.982) on the microstructure of Cu(In,Ga)Se2 (CIGS) thin films was reported. The CIGS thin films were grown via a two-step process including DC sputtering deposition of metallic precursor and following selenization. Presence of a series of chalcopyrite diffraction peaks in the X-Ray diffraction (XRD) patterns confirms the existence of chalcopyrite CIGS (CH-CIGS) phase in these CIGS films. The Raman spectra indicate that as the Cu content increases from low to high, the CIGS film sequentially goes through three phase regimes: coexistence of OVC and CH-CIGS phase, single CH-CIGS phase and coexistence of CuxSe and CH-CIGS phase. Moreover, the full width at half maximum of CIGS Raman peaks changes with Cu/(Ga+In) and reaches its minimum near Cu/(Ga+In)=0.9 due to better crystallinity and less disorder. Some empirical FWHM-Cu/(Ga+In) relationships were also observed. These results show that Raman spectroscopy is more sensitive to the microstructure of CIGS film than XRD, and can be used for preliminary estimation of the crystal phases and Cu content of CIGS film in a fast and non-destructive way.

孙雷, 马建华, 姚娘娟, 黄志明, 褚君浩. 铜含量变化对Cu(In,Ga)Se2薄膜微结构的影响[J]. 红外与毫米波学报, 2017, 36(1): 1. SUN Lei, MA Jian-Hua, YAO Niang-Juan, HUANG Zhi-Ming, CHU Jun-Hao. Influence of various Cu contents on the microstructure of Cu(In,Ga)Se2 thin films[J]. Journal of Infrared and Millimeter Waves, 2017, 36(1): 1.

本文已被 1 篇论文引用
被引统计数据来源于中国光学期刊网
引用该论文: TXT   |   EndNote

相关论文

加载中...

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!