沉淀法制备Li+、Na+掺杂Gd2O3:Eu3+荧光粉及发光特性研究

Luminescence Properties of Li+、Na+ Doped Gd2O3:Eu3+ Phosphor Prepared by Precipitation Methods
作者单位
新疆师范大学物理与电子工程学院 矿物发光及其微结构重点实验室 理论物理自治区重点学科,乌鲁木齐 830054
摘要
用沉淀法制备Li+、Na+和Eu3+共掺Gd2O3荧光粉,并与微波-固相法制备的样品进行了比较。通过测量该粉体的XRD、激发光谱和发射光谱,比较了样品的微观结构和讨论了不同合成条件对Gd2O3:Eu3+荧光粉发光特性的影响。结果显示在相同的条件下,对于未掺入Li+的Gd2O3:Eu3+样品比较,沉淀法制备样品的发光强度是微波-固相法制备样品的1.68倍;掺入Li+的Gd2O3:Eu3+样品比较,沉淀法制备样品的发光强度是微波—固相法制备样品的1.82倍。当使用草酸作为沉淀剂,掺杂浓度为Li+(4.5 mol%)、Na+(4.5 mol%)、Eu3+(4.5 mol%),在800 ℃ 煅烧2 h后获得样品的发光强度,是Gd2O3:Eu3+荧光粉的5.91倍。
Abstract
The Gd2O3:Eu3+phosphor co-doped with Li+ and Na+ were prepared by precipitation method and compared with the samples prepared by microwave solid state phase method.The X ray diffraction,the excitation spectra and the emission spectra of the samples were measured.The microstructure of the samples was analyzed,and the effect of different synthesis conditions on the photoluminescence properties of Gd2O3:Eu3+phosphor was discussed.The results showed that without adding Li+ ions,the luminous intensity of the sample obtained by precipition increased about 1.68 times compared with the sample prepared by the microwave solid phase method.Adding Li+ions,the luminous intensity of the sample obtained by precipition increased 1.82 times compared with it obtained by the microwave solid phase method.The emission of the sample with 4.5 mol% Li+,4.5 mol% Na+ and 4.5 mol% Eu3+ co-doped Gd2O3 increased 5.91 times than that of the sample without adding Li+ and Na+ ions by C2H2O4 precipitation.

李敏, 王林香, 庹娟. 沉淀法制备Li+、Na+掺杂Gd2O3:Eu3+荧光粉及发光特性研究[J]. 光散射学报, 2017, 29(1): 92. LI Min, WANG Linxiang, TUO Juan. Luminescence Properties of Li+、Na+ Doped Gd2O3:Eu3+ Phosphor Prepared by Precipitation Methods[J]. The Journal of Light Scattering, 2017, 29(1): 92.

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!