基于傅里叶红外光谱的生物质环境协调功能材料制备机理及性能研究

Study on Preparation Mechanism and Property of Biomass Environmental Coordination Function Material with Fourier Transform Infrared Spectrum
张浩 1,2
作者单位
1 安徽工业大学建筑工程学院, 安徽 马鞍山 243032
2 安徽工业大学冶金减排与资源综合利用教育部重点实验室, 安徽 马鞍山 243032
摘要
以废弃核桃壳为载体材料、 癸酸为相变材料, 采用微波加热法制备癸酸/多孔活性炭功能材料。 采用傅里叶红外光谱仪对癸酸/多孔活性炭功能材料制备过程各阶段的合成物质进行测试, 即活性炭前驱体制备阶段、 多孔活性炭制备阶段和癸酸/多孔活性炭功能材料制备阶段。 研究癸酸/多孔活性炭功能材料制备过程中多孔活性炭复杂网络结构形成机理、 癸酸嵌入方式、 癸酸与多孔活性炭的嵌合机理, 阐明微波加热法制备癸酸/多孔活性炭功能材料的相关机理。 同时采用动态水分吸附分析仪、 差示扫描量热仪和环境测试舱对癸酸/多孔活性炭功能材料的湿性能、 热性能和吸附性能进行测试。 结果表明: 癸酸/多孔活性炭功能材料具有发达的孔结构和复杂的网络结构, 其中部分孔隙吸附癸酸, 部分孔隙吸附甲醛分子, 孔隙表面具有亲水性的官能团吸附水分子。 癸酸/多孔活性炭功能材料具有较好的湿性能、 热性能和吸附性能, 其在相对湿度40%~60%, 平衡含湿量为0063 1~0257 0 g·g-1; 相变温度为2742~3396 ℃, 相变焓为5214~5267 J·g-1; 经过4 h对甲醛气体的吸附效率为5057%。
Abstract
Decanoic acid/porous activated carbon function material was made with microwave oven method from waste walnut shell and decanoic acid as the carrier and the phase change material respectively in this paper. Synthetic materials in different preparation stages (ie. precursor activated carbon preparation stage, porous activated carbon preparation stage and decanoic acid/porous activated carbon function material preparation stage) were measured with Fourier transform infrared spectrum. Complex network structure forming mechanism of porous activated carbon, decanoic acid embed mode, chimeric mechanism of decanoic acid and porous activated carbon were researched, respectively, in order to explain how to prepare decanoic acid/porous activated carbon function material with microwave oven method. Meanwhile, moisture property, thermal property and absorption property of this function material were tested by dynamic was used to vapor sorption, differential scanning calorimeter and environmental test chamber. The results show that the decanoic acid/porous activated carbon function material has developed pore structure and complex network composition, which adsorb the decanoic acid and formaldehyde molecules. Besides, the pore surface has some hydrophilic functional groups, which can adsorb the water molecules. The decanoic acid/porous activated carbon function material has good moisture property, thermal property and absorption property. Experiments suggest that the equilibrium moisture content can reach 0063 1~0257 g·g-1 in the relative humidity ranges from 40% to 60%. While the phase transition temperature reaches 2742~3396 ℃, the phase change enthalpy is 5214~5267 J·g-1. Besides, the adsorption efficiency of formaldehyde gas can reach 5057% after 4 h.

张浩. 基于傅里叶红外光谱的生物质环境协调功能材料制备机理及性能研究[J]. 光谱学与光谱分析, 2017, 37(2): 412. ZHANG Hao. Study on Preparation Mechanism and Property of Biomass Environmental Coordination Function Material with Fourier Transform Infrared Spectrum[J]. Spectroscopy and Spectral Analysis, 2017, 37(2): 412.

本文已被 2 篇论文引用
被引统计数据来源于中国光学期刊网
引用该论文: TXT   |   EndNote

相关论文

加载中...

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!