掺磷TiO2优化TiO2/MBA/Ag三明治结构的SERS性能

Phosphorus Doping to Improve the Surface-Enhanced Raman Scattering Property of TiO2 in TiO2/MBA/Ag Sandwich Structure

  • 摘要
  • 论文信息
  • 参考文献
  • 被引情况
  • PDF全文
分享:

摘要

本文以磷酸为磷源,通过溶胶水热法制备磷掺杂TiO2,利用Lee和Meisel的方法制备银溶胶,以4-巯基苯甲酸(MBA)为探针分子,通过构建TiO2/MBA/Ag三明治结构,研究磷掺杂二氧化钛对该基底表面增强拉曼(SERS)性能的提升。通过TEM、XRD、XPS、DRS和拉曼光谱图表征二氧化钛的形貌结构、化学组成、光学和拉曼性能,结果表明,制备出的磷掺杂二氧化钛为锐钛矿型纳米颗粒,粒径范围6~12 nm,XPS显示磷以P5+替代了Ti4+,形成O-P-O键掺入TiO2的晶格中,当磷的掺杂量在1.77%时,TiO2/MBA/Ag三明治体系具有最佳的SERS信号,这是因为适量的磷掺杂降低了TiO2的能带间隙,丰富TiO2的表面态,这能促进TiO2向MBA分子的电荷转移。

Abstract

In this paper,P doping TiO2 were synthesized by using H3PO4 as phosphorus source via a facile sol-hydrothermal process,and silver nanoparticles were synthesized by Lee and Meisel method.We choose 4-Mercaptobenzoic acid(4-MBA)as the probe molecule to build TiO2/MBA/Ag sandwich structures as active substrates for surface-enhanced Raman scattering(SERS).The samples were characterized for morphology,structure,optical property and surface chemical composition by Transmission Electron Microscope(TEM),X-Ray Diffraction(XRD),X-Ray Photoelectron Spectroscopy(XPS),UV-visible Diffuse Reflectance Spectra(DRS)and Raman spectroscopy.It shows that the crystal size of TiO2 was about 6-12 nm and P doping could not influence the phase of the crystal.XPS revealed that P5+ replace Ti4+ and doping into the crystal lattice by forming O-P-O.The Raman result shows that P doped TiO2 has a higher intensity of Raman signals in P-TiO2/MBA/Ag sandwich structures than that in pure TiO2/MBA/Ag,the 1.77% P-TiO2 own the strongest Raman signals than any other samples,this is due to phosphorus doping which narrow the energy band gap of TiO2 and abundant the surface states,these were profitable for TiO2 to MBA molecule charge transfer process.

Newport宣传-MKS新实验室计划
补充资料

DOI:10.13883/j.issn1004-5929.201703005

所属栏目:表面增强拉曼散射技术

基金项目:国家自然科学基金(31560466)、广西自然科学基金项目(2016GXNSFAA380108)

收稿日期:2017-01-05

修改稿日期:2017-02-22

网络出版日期:--

作者单位    点击查看

鲍闻渊:广西科技大学 生物与化学工程学院,广西柳州545006广西科技大学 广西糖资源绿色加工重点实验室,广西柳州545006广西蔗糖产业协同创新中心,广西南宁530004广西科技大学 广西高校糖资源加工重点实验室,广西柳州545006
李利军:广西科技大学 生物与化学工程学院,广西柳州545006广西科技大学 广西糖资源绿色加工重点实验室,广西柳州545006广西蔗糖产业协同创新中心,广西南宁530004广西科技大学 广西高校糖资源加工重点实验室,广西柳州545006
冯军:广西科技大学 生物与化学工程学院,广西柳州545006广西科技大学 广西糖资源绿色加工重点实验室,广西柳州545006广西蔗糖产业协同创新中心,广西南宁530004广西科技大学 广西高校糖资源加工重点实验室,广西柳州545006
刘腾:广西科技大学 生物与化学工程学院,广西柳州545006广西科技大学 广西糖资源绿色加工重点实验室,广西柳州545006广西蔗糖产业协同创新中心,广西南宁530004广西科技大学 广西高校糖资源加工重点实验室,广西柳州545006
程昊:广西科技大学 生物与化学工程学院,广西柳州545006广西科技大学 广西糖资源绿色加工重点实验室,广西柳州545006广西蔗糖产业协同创新中心,广西南宁530004广西科技大学 广西高校糖资源加工重点实验室,广西柳州545006
黄文艺:广西科技大学 生物与化学工程学院,广西柳州545006广西科技大学 广西糖资源绿色加工重点实验室,广西柳州545006广西蔗糖产业协同创新中心,广西南宁530004广西科技大学 广西高校糖资源加工重点实验室,广西柳州545006

联系人作者:鲍闻渊(baowenyuan125@sina.com)

备注:鲍闻渊(1991-),男,湖北荆州人,硕士,主要从事表面增强拉曼分析研究。

【1】Ji W,Zhao B,Ozaki Y.Semiconductor materials in analytical applications of surface enhanced Raman scattering[J].J Raman Spectrosc,2016,47(1):51-58.

【2】Li W,Liang R,Hu A,et al.Generation of oxygen vacancies in visible light activated one-dimensional iodine TiO2 photocatalysts[J].RSC Adv,2014,4(70):36959-36966.

【3】Yang L,Ruan W,Jiang X,et al.Contribution of ZnO to charge-transfer induced surface-enhanced Raman scattering in Au/ZnO/PATP assembly[J].J Phys Chem C,2008,113(1):117-120.

【4】Tarakeshwar P,Finkelstein-Shapiro D,Hurst S J,et al.Surface-enhanced Raman scattering on semiconducting oxide nanoparticles:oxide nature,size,solvent,and pH effects[J].J Phys Chem C,2011,115(18):8994-9004.

【5】Yang L,Zhang Y,Ruan W,et al.Improved surface-enhanced Raman scattering properties of TiO2,nanoparticles by Zn dopant[J].J Raman Spectrosc,2010,41(7):721-726.

【6】Xue X,Ji W,Mao Z,et al.SERS study of Co-doped TiO2 nanoparticles[J].Chem Res Chin Univ,2013,29(4):751-754.

【7】Xue X,Ji W,Mao Z,et al.Effects of Mn doping on surface enhanced Raman scattering properties of TiO2 nanoparticles.[J].Spectrochimi Acta A,2012,95(5):213-217.

【8】Lee P C,Meisel D.Adsorption and surface-enhanced Raman of dyes on silver and gold sols[J].J Phys Chem,1982,86:17(17):3391-3395.

【9】孙宇星,雷瑞盈,李玮伟,等.磷掺杂对二氧化钛结构以及催化活性的影响[J].哈尔滨商业大学学报(自然科学版),2014(5):542-544(Sun Yuxing,Lei Ruiying,Li Weiwei,et al.Study on effect of doping of phosphate in titania on crystallite size and structure of anatase[J].Journal of Harbin University of Commerce(Natural Sciences Edition),2014(5):542-544).

【10】Jiang X,Li X,Jia X,et al.Surface-enhanced Raman scattering from synergistic contribution of metal and semiconductor in TiO2/MBA/Ag(Au)and Ag(Au)/MBA/TiO2 assemblies[J].J Phys Chem C,2012,116(27):14650-14655.

【11】江欣,秦晓宇,宫梦娣,等.金属镍掺杂改进纳米TiO2的表面增强拉曼散射性能[J].高等学校化学学报,2014(3):488-492(Jiang Xin,Qin Xiaoyu,Gong Mengdi,et al.Improvement of surface-enhanced Raman scattering properties of TiO2 nanoparticles by metal Ni doping[J].Chem J Chinese U,2014(3):488-492).

引用该论文

BAO Wenyuan,LI Lijun,FENG Jun,LIU Teng,CHENG Hao,HUANG Wenyi. Phosphorus Doping to Improve the Surface-Enhanced Raman Scattering Property of TiO2 in TiO2/MBA/Ag Sandwich Structure[J]. The Journal of Light Scattering, 2017, 29(3): 210-215

鲍闻渊,李利军,冯军,刘腾,程昊,黄文艺. 掺磷TiO2优化TiO2/MBA/Ag三明治结构的SERS性能[J]. 光散射学报, 2017, 29(3): 210-215

您的浏览器不支持PDF插件,请使用最新的(Chrome/Fire Fox等)浏览器.或者您还可以点击此处下载该论文PDF