RIE模式干法刻蚀ADS产品铝腐蚀改善研究

Improvement of aluminum corrosion of ADS products by RIE etching mode dry etching
作者单位
北京京东方光电科技有限公司, 北京 100176
摘要
Full-in-cell(FIC)产品信号线SD层结构为Mo-Al-Mo结构, 使用Reactive Ion Etching(RIE)模式干法刻蚀设备进行N+ Etch时, 氯的化合物会吸附在信号线中的Al线侧壁及光刻胶的表面, 当玻璃基板离开刻蚀腔体接触到空气, 遇到水分发生水解反应, 对Al线造成腐蚀, 严重影响产品特性。本文在RIE刻蚀模式腔体内采用刻蚀条件变更改善Al腐蚀现象, 通过对刻蚀的前处理步骤, 后处理步骤以及去静电步骤的参数包括压强、功率和时间以及气体流量比进行实验设计并对数据进行分析。实验结果表明当后处理步骤2 000 W, O2/SF6比例为2 000 mL·min-1/50 mL·min-1, 压强为200 mt(1 mt=0.133 Pa), Time为15 s为最优条件, 可以彻底改善Al腐蚀现象。此条件TFT特性方面更加优越, Dark Ion为1.91 μA, Photo Ioff为4.1 pA。
Abstract
Full-in-cell (FIC) product signal line SD-layer is Mo-Al-Mo structure, when using Reactive Ion Etching (RIE) mode dry etching device for N + etching, the chlorine compounds absorbed on the side wall surface of the Al and photoresist line, when the glass substrate is etched away from the chamber exposed to air, the moisture encountered hydrolysis reaction, which will cause corrosion of Al wire and seriously affect the product characteristics. In this paper, the Al etching phenomenon is improved by changing the etching conditions in the RIE etching mode cavity. Related experimental design and data analysis of the parameters of the pretreatment step, the post-treatment step and the de-static step including the pressure, power and time and the gas ratio is discussed. The experimental results show that the Al corrosion can be improved when the post-treatment step is 2 000 W, the ratio of O2 / SF6 is 2 000 mL·min-1/ 50 mL·min-1, the pressure is 200 mt and the time is 15 s. This condition is more advantageous in terms of TFT characteristics, Dark Ion is 1.91 μA, Photo Ioff is 4.1 pA.

蒋会刚, 高建剑, 王晏酩, 赵海生, 王辉, 吴超. RIE模式干法刻蚀ADS产品铝腐蚀改善研究[J]. 液晶与显示, 2017, 32(7): 518. JIANG Hui-gang, GAO Jian-jian, WANG Yan-ming, ZHAO Hai-sheng, WANG Hui, WU Chao. Improvement of aluminum corrosion of ADS products by RIE etching mode dry etching[J]. Chinese Journal of Liquid Crystals and Displays, 2017, 32(7): 518.

本文已被 1 篇论文引用
被引统计数据来源于中国光学期刊网
引用该论文: TXT   |   EndNote

相关论文

加载中...

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!