Chinese Optics Letters, 2018, 16 (6): 061401, Published Online: Jul. 2, 2018  

Investigation of latest generation pulsed fiber laser in dissimilar joining of Al and Mg alloys Download: 542次

Author Affiliations
1 School of Material Science and Engineering, Nanjing University of Science and Technology, Nanjing 210094, China
2 Welding Engineering and Laser Processing Centre, Cranfield University, Bedford MK43 0AL, United Kingdom
Abstract
Dissimilar metal joining of magnesium to aluminum was investigated using the latest generation nanosecond pulsed fiber laser. The tensile shear test shows that the average tensile shear strength of a joint was 86 MPa, which was 75% of the aluminum substrate. The weld interface exhibited a mixture phase (Mg solid solution and Mg17Al12) that improves the strength and toughness of the joint. A thin Mg–Al intermetallic compound layer was formed on both sides of the weld seam toward the Al side. Fracture occurred toward the Al substrate side rather than the Mg–Al interface, indicating a high joining strength at the weld interface.

Qiong Gao, Sonia Meco, Kehong Wang, Qi Zhou, Shun Guo, Supriyo Ganguly. Investigation of latest generation pulsed fiber laser in dissimilar joining of Al and Mg alloys[J]. Chinese Optics Letters, 2018, 16(6): 061401.