基于分层远程荧光膜白光LED的制备及光谱性能研究

Preparation and Spectral Properties of White Light Emitting LED Based on Layered Remote Phosphor Film
作者单位
1 轻工业部南京电光源材料科学研究所, 江苏 南京 210015
2 南京工业大学电光源材料研究所, 江苏 南京 210015
3 南京大学电子科学与工程学院, 江苏 南京 210093
4 南京工业大学材料科学与工程学院, 江苏 南京 210009
5 南京工业大学能源科学与工程学院, 江苏 南京 211800
摘要
基于荧光粉分层和远程荧光封装技术, 采用热压法制备出双层远程荧光膜, 并封装出白光LED。 通过荧光分光光度计和可见光光谱分析系统研究了绿色和红色远程荧光膜不同分层顺序及不同发射波长对于白光LED光谱性能的影响。 研究发现: 蓝-绿-红(B-G-R)膜层封装形式相较于蓝-红-绿(B-R-G)辐射发光效率提高了31.69%, 色保真度和色域指数均随着红色远程荧光膜波长的增加而升高, 发射波长为660 nm时制备的白光LED色保真度最高值达到91, 色域指数最高值达到104, 辐射发光效率值则与波长成反比关系; 色保真度随着绿色远程荧光膜波长的增加逐渐降低, 色域指数则先降低后升高, 发射波长为530 nm制备的白光LED具有最高的辐射发光效率, 达到300.7 lm·W-1。 研究所得出的相关结论对于实际的应用具有一定的参考意义。
Abstract
Based on layered phosphor and remote phosphor packaging technology, double layer remote phosphor film were prepared by hot pressing method, and the films then were packaged into white LED. Fluorescence spectrophotometer and the visible spectrum analysis system were used to study the influence on the white LED spectral properties of the layer order of green and red remote phosphor films and emission wavelength. Results showed that the luminescent efficiency of radiation of blue-green-red type package structure compared to the blue-red-green type package structure was improved by 31.69%, and the color fidelity and color gamut index increased with the increasing of red remote phosphor film wavelength. With emission wavelength 660nm, the color fidelity and color gamut index of prepared white LED reached the highest value 91 and 104 respectively. In contrast, luminescent efficiency of radiation was inversely proportional to the wavelength; color fidelity decreased with the increasing of green remote phosphor film wavelength, and color gamut index raised first, then decreased, when emission wavelength was 530 nm, with the luminescent efficiency of radiation of prepared white LED reaching the highest value 300.7 lm·W-1. Finally, the related conclusions of present study had a certain reference value for the actual application.

卓宁泽, 张娜, 陈永浩, 蒋鹏, 程少文, 朱月华, 王海波. 基于分层远程荧光膜白光LED的制备及光谱性能研究[J]. 光谱学与光谱分析, 2018, 38(8): 2337. ZHUO Ning-ze, ZHANG Na, CHEN Yong-hao, JIANG Peng, CHENG Shao-wen, ZHU Yue-hua, WANG Hai-bo. Preparation and Spectral Properties of White Light Emitting LED Based on Layered Remote Phosphor Film[J]. Spectroscopy and Spectral Analysis, 2018, 38(8): 2337.

本文已被 1 篇论文引用
被引统计数据来源于中国光学期刊网
引用该论文: TXT   |   EndNote

相关论文

加载中...

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!