发光学报, 2018, 39 (7): 948, 网络出版: 2018-08-30
Dy3+、Tm3+共掺杂Ca2MgSi2O7的发光特性
Luminescent Properties of Dy3+、Tm3+ Co-doped Ca2MgSi2O7
Tm3+荧光粉 光致发光 白光LED 叠加激发谱带 Ca2MgSi2O7∶Dy3+ Ca2MgSi2O7∶Dy3+ Tm3+ phosphor photoluminescence white light LED superposition excitation band
摘要
采用高温固相法合成了系列Ca2MgSi2O7∶Dy3+,Tm3+发光材料。对样品进行了XRD结构表征, 测量了激发光谱、发射光谱、色温和荧光寿命。研究结果表明, Ca2MgSi2O7∶Tm3+在355 nm激发下显示出蓝色发光, 在CIE1931中的色坐标为x=0.165 9, y=0.082 2, 色纯度为89%。通过Dy3+和Tm3+的叠加激发谱带激发, 即在349, 353, 365 nm激发下, Ca2MgSi2O7∶Dy3+,Tm3+显示出青白、冷白和暖白光, 相关色温值分别为5 193, 9 672, 4 685 K。300~500 nm区域间可以有效地激发Ca2MgSi2O7∶Dy3+,Tm3+, 并在400~600 nm之间产生蓝光和黄光复合产生的白光, 表明该体系可用作白光LED的发光材料。
Abstract
A series of Ca2MgSi2O7∶Dy3+,Tm3+ luminescent materials were synthesized by high temperature solid phase method. The samples were characterized by XRD structure, and the excitation spectra, emission spectra, color temperature and fluorescence lifetime were measured. The results show that Ca2MgSi2O7∶Tm3+ exhibits blue luminescence under the excitation of 355 nm. The color coordinate in CIE1931 is x=0.165 9, y=0.082 2, and the color purity is 89%。Excited by the superposition excitation bands of Dy3+ and Tm3+ (349, 353, 365 nm), Ca2MgSi2O7∶Dy3+,Tm3+ phosphors show bright white, cool white and warm white light, and the correlation color values are 5 193, 9 672, 4 685 K, respectively. In conclusion, Ca2MgSi2O7∶Dy3+and Tm3+ can be effectively excited by 300-500 nm regions and emit white light produced by blue and yellow light combinations between 400-600 nm, shows that the system can be used as a luminescent material for white LED.
胡莲莲, 艾尔肯·斯地克, 万英, 苏晓娜, 王琇. Dy3+、Tm3+共掺杂Ca2MgSi2O7的发光特性[J]. 发光学报, 2018, 39(7): 948. HU Lian-lian, AIERKEN Sidike, WAN Ying, SU Xiao-na, WANG Xiu. Luminescent Properties of Dy3+、Tm3+ Co-doped Ca2MgSi2O7[J]. Chinese Journal of Luminescence, 2018, 39(7): 948.