硅掺杂氧化锡柔性薄膜晶体管的制备与特性

Preparation and Properties of Flexible Thin Film Transistors with Si-incorporated SnO2 Active Layer
作者单位
华南理工大学 材料科学与工程学院, 高分子光电材料与器件研究所, 发光材料与器件国家重点实验室, 广东 广州 510640
摘要
研究了柔性非晶硅掺杂氧化锡(SiSnO,STO)薄膜晶体管的电学特性及其在弯曲状态下的电学特性。通过射频磁控溅射在聚酰亚胺(Polyimide,PI)衬底上制备出了柔性非晶硅掺杂氧化锡薄膜晶体管。通过对比不同退火温度的器件性能, 发现在300 ℃能获得最佳器件性能, 其饱和迁移率达到2.71 cm2·V-1·s-1, 开关比高于106, 亚阈值摆幅为1.95 V·dec-1, 阈值电压为2.42 V。对器件在不同曲率半径(5, 10, 20, 30 mm)状态下进行输出特性和转移特性测试, 发现其在弯曲状态下仍具有良好的电学性能。
Abstract
A kind of flexible amorphous silicon doped tin oxide(SiSnO, STO) thin film transistor (TFT) with anti-bending property of polyimide as a flexible substrate was prepared by RF magnetron sputtering method. By comparing the performance of the devices with different annealing temperatures, it is found that the best device performance is achieved at 300 ℃, the field effect mobility is 2.71 cm2·V-1·s-1, the switching ratio is higher than 106 and the subthreshold swing is 1.95 V·dec-1, and the threshold voltage is 2.42 V. By measuring the output characteristics and transfer characteristics of the device at different radius of curvature(5, 10, 20, 30 mm), the device is still operating well under the four different radii of curvature.

张建东, 刘贤哲, 张啸尘, 李晓庆, 王磊, 姚日晖, 宁洪龙, 彭俊彪. 硅掺杂氧化锡柔性薄膜晶体管的制备与特性[J]. 发光学报, 2018, 39(7): 968. ZHANG Jian-dong, LIU Xian-zhe, ZHANG Xiao-chen, LI Xiao-qing, WANG Lei, YAO Ri-hui, NING Hong-long, PENG Jun-biao. Preparation and Properties of Flexible Thin Film Transistors with Si-incorporated SnO2 Active Layer[J]. Chinese Journal of Luminescence, 2018, 39(7): 968.

本文已被 1 篇论文引用
被引统计数据来源于中国光学期刊网
引用该论文: TXT   |   EndNote

相关论文

加载中...

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!