紫外光强对聚合物分散液晶电光特性的影响

Effect of UV intensities on electro-optic properties of polymer dispersed liquid crystal

  • 摘要
  • 论文信息
  • 参考文献
  • 被引情况
  • PDF全文
分享:

摘要

聚合物分散液晶(PDLC)是液晶微滴分散在聚合物基体中形成的一种具有优异电光性能的材料, PDLC的电光特性对基于PDLC的电光器件的性能具有显著影响。本文对紫外固化光强对PDLC电光特性的影响进行研究。本研究使用紫外照射引发的聚合物诱导相分离方法制备PDLC。在4个不同紫外固化光强(1 mW/cm2、1.8 mW/cm2、3 mW/cm2和9 mW/cm2)条件下制备PDLC样品, 并对4个样品的电光特性如电压-透过率、响应时间和迟滞效应进行研究, 并对实验结果给出了分析。实验结果表明: 随着紫外固化光强的增加, PDLC的阈值电压和饱和电压增加, 开态响应时间ton上升, 关态响应时间toff下降, 同时对于高紫外光强聚合制备的样品迟滞效应也更加明显。本研究表明可以通过改变制备过程中的紫外光强来优化PDLC的电光特性, 从而获得性能优异的基于PDLC的电光器件。

Abstract

Polymer Dispersed Liquid Crystal (PDLC) is a high performance electro-optic material. The electro-optical properties of PDLC have great influence on the performance of applications based on PDLC. In this paper, we studied the effect of UV intensities on electro-optic properties of PDLC. PDLC samples are fabricated by polymer induced phase separation (PIPS) method initiated by UV irradiation. Four PDLC samples were prepared using four UV light intensities of 1 mW/cm2,1.8 mW/cm2,3 mW/cm2 and 9 mW/cm2. The electo-optical properties of voltage-transmittance curve, response time and hysteresis effect are studied. With the increase of the UV intensity, the threshold voltage and saturation voltage increase. The rise time increases while the decay time decreases for high intensity UV irradiation. The hysteresis effect also becomes severe. This work suggests that it is possible to optimize the electro-optical properties of PDLC by adjusting the UV intensities and obtain PDLC based devices that possess good electro-optical performance.

Newport宣传-MKS新实验室计划
补充资料

中图分类号:TP141.9;O753+.2

DOI:10.3788/yjyxs20183308.0631

所属栏目:材料与器件

基金项目:国家自然科学基金青年科学基金(No.61704090); 江苏省自然科学基金青年基金(No.BK20170908, No.BK20170903); 江苏省高等学校自然科学研究面上项目(No.17KJB510041, No.17KJB510040); 射频集成与微组装技术国家地方联合工程实验室开放课题(No.KFJJ20170307, No.KFJJ20170204); 南京邮电大学引进人才科研启动基金资助(No.NY217123, No.NY217124);南京邮电大学校级科研基金资助(NY218020)

收稿日期:2018-04-20

修改稿日期:2018-05-05

网络出版日期:--

作者单位    点击查看

陈菲:南京邮电大学 电子与光学工程学院 微电子学院, 江苏 南京 210023
徐荣青:南京邮电大学 电子与光学工程学院 微电子学院, 江苏 南京 210023
李若舟:南京邮电大学 电子与光学工程学院 微电子学院, 江苏 南京 210023南京邮电大学 射频集成与微组装技术国家地方联合工程实验室, 江苏 南京 210023
严静:南京邮电大学 电子与光学工程学院 微电子学院, 江苏 南京 210023南京邮电大学 射频集成与微组装技术国家地方联合工程实验室, 江苏 南京 210023

联系人作者:徐荣青(jing.yan@njupt.edu.cn; 严静|xurq@njupt.edu.cn)

备注:陈菲(1994-), 女, 安徽安庆人, 硕士研究生, 2016年于南京工程学院获得学士学位, 主要从事聚合物分散液晶方面的研究。E-mail: icf_1230@163.com

【1】DOANE J W, GOLEMME A, WEST J L, et al. Polymer dispersed liquid crystals for display application [J]. Journal Molecular Crystals and Liquid Crystals Incorporating Nonlinear Optics, 1988, 165(1): 511-532.

【2】STEIN R S, SRINIVASARAO M. Light-scattering studies of liquid crystal dispersions [J]. SPIE, 1993, 1911: 132-153.

【3】黄子强.液晶显示原理[M].2版.国防工业出版社, 2008: 78-192.
HUANG Z Q. Principle of Liquid Crystal Display [M]. 2nd ed. Beijing: National Defense Industry Press, 2008: 78-192. (in Chinese)

【4】顾玲娟, 郑继红, 陈刚, 等.聚合物分散液晶(PDLC)光开关研究[J].光学仪器, 2002, 24(3): 28-33.
GU L J, ZHENG J H, CHEN G, et al. The study of polymer-dispersed liquid crystal (PDLC) optical switching [J]. Optical Instruments, 2002, 24(3): 28-33. (in Chinese)

【5】MURRAY J, MA D K, MUNDAY J N. Electrically controllable light trapping for self-powered switchable solar windows [J]. ACS Photonics, 2016, 4(1): 1-7.

【6】LIU J H, WU F T. Synthesis of photoisomeric azobenzene monomers and model compound effect on electric-optical properties in PDLC films [J]. Journal of Applied Polymer Science, 2010, 97(3): 721-732.

【7】高峰, 钱俊, 刘慧慧, 等.阻聚剂对聚合物分散液晶电光性能的影响[J].液晶与显示, 2013, 28(4): 495-500.
GAO F, QIAN J, LIU H H, et al. Effect of polymerization inhibitor on electro-optical properties of polymer dispersed liquid crystal films [J]. Chinese Journal of Liquid Crystals and Displays, 2013, 28(4): 495-500. (in Chinese)

【8】胡晓阳, 杜鑫, 汪映寒.聚合物基体分子量及极性对聚合物分散液晶迟滞效应的影响[J].液晶与显示, 2010, 25(1): 53-56.
HU X Y, DU X, WANG Y H. Influence of polymer matrix molecule weight and polarity on hysteresis effect of polymer dispersed liquid crystals [J]. Chinese Journal of Liquid Crystals and Displays, 2010, 25(1): 53-56. (in Chinese)

【9】SONG P, CAO H, WANG F F,et al. The UV polymerisation temperature dependence of polymer-dispersed liquid crystals based on epoxies/acrylates hybrid polymer matrix components [J]. Liquid Crystals, 2012, 39(9): 1131-1140.

【10】AHMAD F, JAMIL M, LEE J W, et al. The effect of UV intensities and curing time on polymer dispersed liquid crystal (PDLC) display: a detailed analysis study [J]. Electronic Materials Letters, 2016, 12(5): 685-692.

【11】LI W B, CAO H, KASHIMA M, et al. Control of the microstructure of polymer network and effects of the microstructures on light scattering properties of UV-cured polymer-dispersed liquid crystal films [J]. Journal of Polymer Science Part B: Polymer Physics, 2008, 46(19): 2090-2099.

【12】RAO L H, YAN J, WU S T, et al. Critical field for a hysteresis-free BPLC device [J]. Journal of Display Technology, 2011, 7(12): 627-629.

【13】XU D M, YAN J, YUANJ M, et al. Electro-optic response of polymer-stabilized blue phase liquid crystals [J]. Applied Physics Letters, 2014, 105(1): 011119.

【14】DRZAICP S. Reorientation dynamics of polymer dispersed nematic liquid crystal Films [J]. Liquid Crystals, 1988, 3(11): 1543-1559.

引用该论文

CHEN Fei,XU Rong-qing,LI Ruo-zhou,YAN Jing. Effect of UV intensities on electro-optic properties of polymer dispersed liquid crystal[J]. Chinese Journal of Liquid Crystals and Displays, 2018, 33(8): 631-637

陈菲,徐荣青,李若舟,严静. 紫外光强对聚合物分散液晶电光特性的影响[J]. 液晶与显示, 2018, 33(8): 631-637

您的浏览器不支持PDF插件,请使用最新的(Chrome/Fire Fox等)浏览器.或者您还可以点击此处下载该论文PDF