用溶胶-凝胶法制备的Cu2Bi2Cr2O8薄膜及其光学和铁磁性能研究

Optical and Magnetic Properties of Cu2Bi2Cr2O8 Films by Sol-gel Method

  • 摘要
  • 论文信息
  • 参考文献
  • 被引情况
  • PDF全文
分享:

摘要

以硝酸铜Cu(NO3)2·3H2O、硝酸铬Cr(NO3)3·9H2O、硝酸铋Bi(NO3)3·3H2O和乙二醇为原料,利用溶胶-凝胶工艺在石英衬底上制备了纳米Cu2Bi2Cr2O8薄膜。通过X射线衍射(X-Ray Diffraction, XRD)和拉曼测试对样品进行了表征。结果表明,Cu2Bi2Cr2O8薄膜具有良好的光学特性,其禁带宽度为1.49 eV; 在磁性测试方面,Cu2Bi2Cr2O8薄膜呈现出了良好的铁磁性。

Abstract

Taking Cu(NO3)2·3H2O, Cr(NO3)3·9H2O, Bi(NO3)3·3H2O and ethylene glycol as raw materials, Cu2Bi2Cr2O8 thin films were fabricated on SiO2 substrates by a sol-gel process. The thin film samples were characterized by X-ray Diffraction (XRD) patterns and Raman tests. The results showed that the Cu2Bi2Cr2O8 thin films had good optical properties. Their band gap was 1.49 eV. In the magnetic hysteresis (M-H) loop measurements, the Cu2Bi2Cr2O8 thin films showed their excellent ferromagnetism.

Newport宣传-MKS新实验室计划
补充资料

中图分类号:O469

DOI:10.3969/j.issn.1672-8785.2018.12.002

基金项目:国家自然科学基金项目(61376129; 61474045); 营口理工学院优秀教学团队项目(JT201705); 营口理工学院精品资源共享课项目(JP201713)

收稿日期:2018-10-11

修改稿日期:--

网络出版日期:--

作者单位    点击查看

崔金玉:营口理工学院,辽宁 营口 115014
杨平雄:华东师范大学信息科学技术学院电子系, 上海 200241极化材料与器件教育部重点实验室, 上海 200241

联系人作者:崔金玉(cjy8103181@126.com)

备注:崔金玉(1972-),女,黑龙江绥化人,副教授,硕士,主要研究方向为原子与分子物理、微电子学与固体电子学。

引用该论文

CUI Jin-yu,YANG Ping-xiong. Optical and Magnetic Properties of Cu2Bi2Cr2O8 Films by Sol-gel Method[J]. INFRARED, 2018, 39(12): 8-11

崔金玉,杨平雄. 用溶胶-凝胶法制备的Cu2Bi2Cr2O8薄膜及其光学和铁磁性能研究[J]. 红外, 2018, 39(12): 8-11

您的浏览器不支持PDF插件,请使用最新的(Chrome/Fire Fox等)浏览器.或者您还可以点击此处下载该论文PDF