激光技术, 2019, 43 (2): 212, 网络出版: 2019-07-10   

5mm厚紫铜激光焊接接头组织及性能研究

Study on microstructure and properties of 5mm thick copper laser welded joints
作者单位
1 广东省焊接技术研究所(广东省中乌研究院) 广州 510650
2 广东省现代焊接技术重点实验室, 广州 510650
摘要
为了研究离焦量对5mm厚紫铜激光焊接焊缝成形的影响和组织特征及性能, 采用金相显微镜对焊缝组织及形貌进行分析, 并对接头进行了拉伸及电导率测试。结果表明, 在高离焦量绝对值时, 易出现飞溅并造成焊缝表面孔洞, 在离焦量0mm~-2mm范围内可获得成形良好的焊缝; 焊缝纵截面柱状晶与焊接方向的角度由两侧的90°逐步降低为中间的0°, 靠近焊缝上表面的柱状晶长度约为靠近下表面的柱状晶长度2.96倍, 热影响区晶粒发生粗化, 且离焦量+1mm对应的热影响区宽度最大; 焊透情况下的不同离焦量对应的接头拉伸强度相当, 可达母材的77.3%, 离焦量0mm~-1mm对应的接头延伸率略高于离焦量-1mm~-4mm对应的接头延伸率, 可达母材的54.9%; 焊缝的电导率与母材几乎一样。该研究有利于获得成形良好的紫铜激光焊接接头。
Abstract
In order to study effect of defocus amount on the weld formation, the microstructure characteristics and properties of 5mm thick laser welding copper, metallographic microscope was used to analyze the microstructure and morphology of the weld. The tensile strength and electrical conductivity of the joint were tested. The results show that, when the absolute value of defocus is high, it is easy to spatter and cause holes on the weld surface. A well-formed weld can be obtained within the defocus range of 0mm~-2mm. The angle between the columnar crystal and the welding direction of the longitudinal section of the weld is gradually reduced from 90° on the sides to 0° in the middle. The columnar crystal near the upper surface of the weld is about 2.96 times the length of the columnar crystal near the bottom surface. The grain size of heat affected zone coarsen. And the width of heat affected zone corresponding to defocus +1mm is the largest. Under the penetration condition, the tensile strength of the joints corresponding to the different defocus amounts is equal, up to 77.3% of base metal. The joint elongation with defocus 0mm~-1mm is slightly higher than that with defocus -1mm~-4mm, up to 54.9% of base metal. The electrical conductivity of the weld is almost the same as that of the base metal. The study is beneficial to obtain good shaped laser welded joints of copper.

陈永城, 罗子艺, 韩善果, 蔡得涛, 哈斯金·弗拉基斯拉夫. 5mm厚紫铜激光焊接接头组织及性能研究[J]. 激光技术, 2019, 43(2): 212. CHEN Yongcheng, LUO Ziyi, HAN Shanguo, CAI Detao, VLADYSLAV Khaskin. Study on microstructure and properties of 5mm thick copper laser welded joints[J]. Laser Technology, 2019, 43(2): 212.

本文已被 1 篇论文引用
被引统计数据来源于中国光学期刊网
引用该论文: TXT   |   EndNote

相关论文

加载中...

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!