SiNx/SiOxNy叠层结构防潮能力的研究

Research on Moisture Barrier Property of SiNx/SiOxNy Stacks Structure
作者单位
1 北京理工大学 光电学院, 北京 100081
2 北京京东方光电科技有限公司, 北京 100176
摘要
研究了等离子体增强化学气相沉积(PECVD)工艺参数对SiNx及SiOxNy防潮能力的影响, 并测试了SiNx/SiOxNy叠层薄膜的水汽渗透速率(WVTR)。实验结果表明: 单层SiNx薄膜和SiOxNy薄膜都存在临界厚度, 当膜厚大于临界值时, 继续增大厚度不会明显改善薄膜的WVTR。当沉积温度从50℃提高到250℃, SiNx薄膜的WVTR从0.031g/(m2·day)降至0.010g/(m2·day)。SiOxNy沉积时, 增大N2O通入量对薄膜的WVTR影响不明显, 但可以有效改善薄膜的弯曲性能。最后, 4个SiNx/SiOxNy叠层膜的WVTR下降到了4.4×10-4g/(m2·day)。叠层膜防潮能力的显著提升归因于叠层结构可以有效解耦层与层之间的缺陷, 延长水汽渗透路径。
Abstract
The influences of process parameters on the moisture barrier properties of SiNx and SiOxNy prepared by plasma enhanced chemical vapor deposition (PECVD) were investigated, and the water vapor permeation rate (WVTR) of SiNx/SiOxNy stacks film was tested. The results show that both the single-layer SiNx film and the SiOxNy film have a critical thickness. When the film thickness is greater than the critical value, increasing the thickness does not significantly improve the WVTR of the film. When the deposition temperature increased from 50℃ to 250℃, the WVTR of the SiNx film decreased from 0.031g/(m2·day) to 0.010g/(m2·day). When SiOxNy is deposited, increasing the N2O flux does not affect the WVTR of the film, but it can effectively improve the bending properties of the film. Finally, the WVTR of the four stacks SiNx/SiOxNy films fell to 4.4×10-4g/(m2·day). The significant improvement in moisture barrier capacity of the film is attributed to the fact that the stackstructure can effectively decouple the defects between the layers and extend the water vapor permeation path.

许海飞, 喻志农, 程锦, 栗旭阳, 陈永华, 李言, 薛建设. SiNx/SiOxNy叠层结构防潮能力的研究[J]. 半导体光电, 2019, 40(5): 643. XU Haifei, YU Zhinong, CHENG Jin, LI Xuyang, CHEN Yonghua, LI Yan, XUE Jianshe. Research on Moisture Barrier Property of SiNx/SiOxNy Stacks Structure[J]. Semiconductor Optoelectronics, 2019, 40(5): 643.

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!