Li+、Na+共掺(YxGdyLu1-x-y)2O3∶05%Pr3+荧光粉的制备及发光特性研究

Preparation and luminescence properties of Li+,Na+ co-doped(YxGdyLu1-x-y)2O3∶05%Pr3+ phosphors
庹娟 1,2,3叶颖 1,2,3赵海琴 1,2,3王林香 1,2,3
作者单位
1 新疆师范大学 物理与电子工程学院, 新疆 乌鲁木齐 830054
2 新疆师范大学 新疆矿物发光材料及其微结构实验室, 新疆 乌鲁木齐 830054
3 新疆师范大学 物理学重点学科, 新疆 乌鲁木齐 830054
摘要
用高温固相法制备了Li+, Na+共掺(YxGdyLu1-x-y)2O3∶0.5%Pr3+荧光粉末。用XRD对样品进行结构表征, 用扫描电镜观测了样品的形貌, 测量了样品的激发光谱、发射光谱及发光衰减曲线。结果显示, Li+、Na+和Pr3+的掺杂没有引起(YxGdyLu1-x-y)2O3立方晶相结构的改变。在单一基质中掺杂的Li+、Na+可有效改善晶粒尺寸, 在复合基质中掺杂的Li+、Na+, 不仅可以有效改善晶粒尺寸, 还使得样品有陶瓷化的趋势。在272 nm激发下, 粉末样品在632 nm处均呈现较强的Pr3+红色发射。不同条件下, 1 000 ℃煅烧2 h获得的(Y0.05Gd0.05Lu0.9)2O3∶0.5%Pr3+, 2.5%Li+, 1%Na+荧光粉末的发光最强, 且荧光寿命较短。
Abstract
Li+, Na+ co-doped (YxGdyLu1-x-y)2O3∶05%Pr3+ phosphors were synthesized with a high temperature solid-state reaction. The structures of the samples were characterized by XRD. The excitation spectra, emission spectra and fluorescence lifetime of the samples were measured and analyzed using a fluorescence spectrophotometer. The results show that they are still the cubic phase of the matrix for Li+, Na+ , doped (YxGdyLu1-x-y)2O3∶ Pr3+ samples. The doping of Li+ and Na+ in a single matrix can effectively improve the grain size while the doping of Li+ and Na+ in a composite matrix not only effectively improves the grain size, but also causes the sample to become ceramic. Under excitation at 272 nm, the powder samples present strong red emissions of Pr3+ at 632 nm. Under different conditions, (Y0.05Gd0.05Lu0.9)2O3∶ 05%Pr3+, 25%Li+, 1%Na+ fluorescent powder obtained by calcination at 1 000 ℃ for two hours has the strongest luminescence, while the lifetime of the sample is shorter.

庹娟, 叶颖, 赵海琴, 王林香. Li+、Na+共掺(YxGdyLu1-x-y)2O3∶05%Pr3+荧光粉的制备及发光特性研究[J]. 中国光学, 2019, 12(6): 1279. TUO Juan, YE Ying, ZHAO Hai-qin, WANG Lin-xiang. Preparation and luminescence properties of Li+,Na+ co-doped(YxGdyLu1-x-y)2O3∶05%Pr3+ phosphors[J]. Chinese Optics, 2019, 12(6): 1279.

本文已被 1 篇论文引用
被引统计数据来源于中国光学期刊网
引用该论文: TXT   |   EndNote

相关论文

加载中...

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!