Cr4+:YAG可饱和吸收特性测量
Measurement of Cr4+:YAG Saturable Absorption
摘要
测量了Cr4+:YAG材料的可饱和吸收特性,用多种数据分析方法处理了实验结果,Cr4+:YAG的基态吸收截面σgs=11×10-19cm2,激发态吸收截面σes=1.2×10-19cm2。
Abstract
The saturable absorption in Cr~4+: YAG was measured. The ground and excited-state absorption cross sections of σgs=11×10-19 cm2, σes=1.2×10-19 cm2 were obtained by experiments and different model calculations for different samples.