原材料Y2O3的结晶性对Y2O2S∶Eu3+发光特性的影响

为进一步提高Y2O2S∶Eu3+的发光性能,采用改善主要原材料Y2O3结晶性的方法,使Y2O2S∶Eu3+红色荧光粉在20 kV和25 kV下发光强度分别增强5％和10％,且不影响色度、粒度、粉体分散性等主要考核指标。提高了粉体的耐电压特性(发射强度与激发电压间的关系特性)。讨论和分析了发射强度增强、电压特性改善的原因:主要原材料Y2O3的结晶性的改善,使得合成的Y2O2S∶Eu3+具有更好的晶体质量,Eu3+离子晶场环境得到进一步改善,从而减弱了无辐射过程及因晶格畸变所造成的能量损失,发光效率得到增强,电压特性得到改善。实验表明,获取高质量多晶Y2O3的最佳分解温度为1400 ℃左右。

Abstract

In order to improve the luminescent character of Y2O2S∶Eu3+, the method of improving crystallinity of primary raw material Y2O3 is used. The emission intensity of red phosphors Y2O2S∶Eu3+ is effectively enhanced 5％ and 10％ respectively at the voltages of 20 kV and 25 kV while the other primary properties of application in chromaticity, granularity and decentralization are not changed. The voltage resistance character (relation between emission intensity and excitation voltage) is elevated. The origins of the emission intensity enhancement and excitation voltage elevation are discussed and analyzed preliminarily. It is likely that the abnormal change and defect of crystal lattice led by the substitution of larger radius Eu3+ ion for smaller radius Y3+ ion are reduced by the better crystal quality of Y2O2S∶Eu3+ from the better crystallinity of raw material Y2O3. Because the crystal field condition of Eu3+ ion is improved, radiationless process and energy loss led by crystal defect are cut down, the emission efficiency of Y2O2S∶Eu3+ phosphors is enhanced and its voltage character is improved. The experiment shows that the decomposing temperature to get the high crystallinity Y2O3 is about 1400 ℃.

参考文献

[1] . . Transient Properties of the Luminescence of Eu3+ and Tb3+ in oxysulfide matrices[J]. J. Electrochem. Soc., 1985, 132: 711-715.

[2] Chi Yuanbin, Liu Shenxin, Wang Lizhong et al.. Emission spectra, energy levels and crystal field for Eu3+∶Gd2O2S under high pressure[J]. Acta Optica Sinica, 1995, 15(1): 1～7 (in Chinese)
池元斌, 刘慎薪, 王立中等. 高压下Eu3+∶Gd2O2S的发射光谱、能级及晶体场[J]. 光学学报, 1995, 15(1): 1～7

[3] . Market, production and investigation of Y2O2S∶Eu red-emitting phosphor for cathode ray tubes[J]. Chinese Rare Earths, 1998, 19(4): 66-69.

[4] Wu Jianhui, Zhang Zhuanfu, Wu Linlin et al.. Precipitation oxalate method and its application in preparing powder materials[J]. Sichuan Nonferrous Metals, 2001, (3): 13～16 (in Chinese)
邬建辉, 张传福, 吴琳琳等. 草酸盐沉淀法在制备粉体材料中的应用[J]. 四川有色金属, 2001, (3): 13～16

[5] . . A study on anti-ageing of Y3(Al,Ga)5O12∶Tb green phosphor material for projection television[J]. J. The Chinese Ceramic Society, 2004, 32(5): 576-579.

[6] . . Characterization of Eu doped Y2O3 nanoparticles prepared in nonionic reverse micro emulsions in relation to their application for field emission display[J]. J. Electrochem Soc., 2000, 147(8): 3139-3142.

[7] . . Synthesis and spectra characteristics of Y2O2S∶Eu3+ red phosphors[J]. J. Hunan Medical College, 1999, 1(1): 3-4.

[8] Yuan Jianhui, Liu Xingren, Lin Hai et al.. Flourescence of Eu3+ ion in silicate glass[J]. Chinese J. Luminescence, 1998, 19(1): 92～94 (in Chinese)
袁剑辉, 刘行仁, 林海等. 镉铝硅酸盐玻璃中Eu3+离子的荧光[J]. 发光学报, 1998, 19(1): 92～94

[9] . . Tree-photon upconversion in Er3+ doped Ca3Al2Ge3O12[J]. Chem. Phys. Lett., 1997, 273: 416-420.

[10] Yuan Jianhui, Liu Xingren. Spectroscopic characteristics of Ce3+ doped Ca3Al2M3O12 (M=Si,Ge) garnets[J]. Spectroscopy and Spectral Analysis, 1998, 18(1): 11～14 (in Chinese)
袁剑辉, 刘行仁. Ca3Al2M3O12(M=Si,Ge)石榴石中Ce3+离子的荧光[J]. 光谱学与光谱分析, 1998, 18(1): 11～14

[11] . . Synthesis of Eu3+-activated yttrium oxysulfide red phosphor by flux fusion method[J]. Material Chemistry and Physics, 2001, 71: 179-189.

[12] Chen Baojiu, Wang Haiyu, Huang Shihua. A study on borate-lead glasses with Eu3+ ion as probe[J]. Acta Optica Sinica, 2001, 21(6): 762～765 (in Chinese)
陈宝玖, 王海宇, 黄世华. 用Eu3+作探针研究硼铅玻璃材料[J]. 光学学报, 2001, 21(6): 762～765

[13] Lu Shaozhe, Li Dan, Huang Shihua. Energy transfer between Eu3+ ions at different crystallographic sites of Y2O3 nanocrystals[J]. Acta Optica Sinica, 2001, 21(9): 1084～1087 (in Chinese)
吕少哲, 李丹, 黄世华. Y2O3纳米晶中两种格位的Eu3+之间的能量传递[J]. 光学学报, 2001, 21(9): 1084～1087

袁剑辉, 张振华, 王晓君, 程玉民. 原材料Y2O3的结晶性对Y2O2S∶Eu3+发光特性的影响[J]. 光学学报, 2005, 25(9): 1243. 袁剑辉, 张振华, 王晓君, 程玉民. Effects of Crystallinity of Raw Material Y2O3 on Luminescent Character of Y2O2S∶Eu3+[J]. Acta Optica Sinica, 2005, 25(9): 1243.

原材料Y2O3的结晶性对Y2O2S∶Eu3+发光特性的影响

关于本站 Cookie 的使用提示

全站搜索

原材料Y2O3的结晶性对Y2O2S∶Eu3+发光特性的影响

相关论文

相关资讯

关于本站 Cookie 的使用提示

全站搜索