选区激光熔化GH4169组织与冲击韧性分析 下载: 850次

Microstructure and Impact Toughness of GH4169 Samples Fabricated by Selective Laser Melting
作者单位
中国航发北京航空材料研究院3D打印研究与工程技术中心, 北京100095
摘要
采用选区激光熔化(SLM)技术制备了GH4169冲击韧性试样,并对其微观组织进行观察。结果表明:在优选的SLM工艺参数范围内,成形试样中定向凝固的细化柱状晶组织均匀排列,在功率P=260 W、扫描速度ν=0.9 m/s的条件下,GH4169试样的室温韧性值为43.9 J/cm 2,且随着激光功率和扫描速度的增大,冲击韧性值不断降低,冲击试样断口有明显的穿晶断裂特征。
Abstract
In this study, impact toughness samples of GH4169 are prepared by selective laser melting (SLM), and the microstructures of these samples are observed. The results show that in the preferred range of the SLM process parameters, the samples form a uniform orientation of the solidified columnar grain refinement arrangement. For a power of P=260 W and scanning speed of ν=0.9 m/s, the impact toughness of the GH4169 samples at room temperature is 43.9 J/cm 2, and with the increase of laser power and scanning speed, the impact toughness continuously decreases, and the fracture of the impact sample has obvious transgranular characteristics.

黄帅, 郭绍庆, 张国会, 周标, 闫泰起, 陈冰清, 张学军. 选区激光熔化GH4169组织与冲击韧性分析[J]. 激光与光电子学进展, 2020, 57(5): 051405. Shuai Huang, Shaoqing Guo, Guohui Zhang, Biao Zhou, Taiqi Yan, Bingqing Chen, Xuejun Zhang. Microstructure and Impact Toughness of GH4169 Samples Fabricated by Selective Laser Melting[J]. Laser & Optoelectronics Progress, 2020, 57(5): 051405.

本文已被 3 篇论文引用
被引统计数据来源于中国光学期刊网
引用该论文: TXT   |   EndNote

相关论文

加载中...

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!