表面处理工艺对铝合金抗激光损伤能力的影响

Effect of Surface Treatment Technology on Laser Damage Resistance of Aluminium Alloy
作者单位
1 中国科学院上海光学精密机械研究所高功率激光物理重点实验室, 上海 201800
2 上海大学机电工程与自动化学院, 上海 200444
3 电子工程学院脉冲功率激光技术国家重点实验室, 安徽 合肥 230037
摘要
研究了表面处理工艺对铝合金表面抗激光损伤能力的影响。结果表明,在相同纳秒激光脉冲辐照下,与机械抛光相比,化学镀镍、阳极氧化黑和硬质阳极氧化处理的表面损伤阈值较低,而钝化和微弧氧化的损伤阈值较高;相同处理工艺但不同参数对应的损伤阈值不同。通过比较不同工艺表面的相关物理参数,对损伤阈值、形貌和规律进行了分析。结果表明,钝化更适用于高功率激光装置中铝合金表面的处理。
Abstract
The effect of surface treatment technology on laser damage resistance of aluminum alloy is studied. Results show that, under the same nanosecond laser irradiation, the laser-induced damage threshold of nickel-plated metal surface, black anode oxidated surface, or hard anode oxidated surface is lower, while that of inactivated or micro arc oxidized surface is higher, if compared with that of mechanically polished surface; surfaces treated by the same treatment process but with different parameters have different damage thresholds. With the comparison among the relevant physical parameters of different technologies, the damage thresholds, morphologies, and patterns are analyzed and the results indicate that the inactivation technology is more suitable for the aluminum alloy surface treatment in high power laser facility.

时双, 孙明营, 郝艳飞, 张燕, 庞向阳, 章亚男, 刘志刚. 表面处理工艺对铝合金抗激光损伤能力的影响[J]. 中国激光, 2016, 43(12): 1202001. Shi Shuang, Sun Mingying, Hao Yanfei, Zhang Yan, Pang Xiangyang, Zhang Yanan, Liu Zhigang. Effect of Surface Treatment Technology on Laser Damage Resistance of Aluminium Alloy[J]. Chinese Journal of Lasers, 2016, 43(12): 1202001.

本文已被 5 篇论文引用
被引统计数据来源于中国光学期刊网
引用该论文: TXT   |   EndNote

相关论文

加载中...

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!