 Yb∶CaF2透明陶瓷的制备与性能研究

刘 强 刘 阳 韦家蓓 谢腾飞 李 江

[摘要]采用共沉淀法合成5at%Yb∶CaF2纳米粉体。该粉体为纯立方CaF2相,平均颗粒尺寸为45 nm。Yb∶CaF2纳米粉体呈立方体状,具有较好的分散性。通过真空预烧结合热等静压烧结(HIP)后处理制备5at%Yb∶CaF2透明陶瓷,研究了真...

 PDF全文人工晶体学报 | 2020, 49(05):799

 One-order-higher Cr4+ conversion efficiency in Cr4+:YAG transparent ceramics for a high-frequency passively Q-switched laser

Yingshuang Shan Le Zhang Tianyuan Zhou Cen Shao Lei Zhang Yuelong Ma Qing Yao Zhigang Jiang Farida A. Selim Hao Chen

[摘要]

 PDF全文Photonics Research | 2019, 7(08):933-938

 Defects and solarization in YAG transparent ceramics

Le Zhang Jiadong Wu Petr Stepanov Micah Haseman Tianyuan Zhou David Winarski Pooneh Saadatkia Sahil Agarwal Farida A. Selim Hao Yang Qitu Zhang Yun Wang Chingping Wong Hao Chen

[摘要]

 PDF全文Photonics Research | 2019, 7(05):549-557

 Overview of ytterbium based transparent ceramics for diode pumped high energy solid-state lasers

Samuel Paul David Venkatesan Jambunathan Antonio Lucianetti Tomas Mocek

[摘要]

 PDF全文High Power Laser Science and Engineering | 2018, 6(04):e62

 Nd∶YAG透明陶瓷尺寸对激光性能的影响

雷卉 庞振华 任豪

[摘要]以Nd∶YAG透明陶瓷为增益介质, 搭建了一套激光性能评估系统, 研究了Nd∶YAG透明陶瓷的尺寸对激光性能的影响。实验结果表明, 当Nd∶YAG透明陶瓷的尺寸较小时, 在相同抽运功率下, 激光输出功率随着尺寸的增加而增大, 但...

 PDF全文激光与光电子学进展 | 2017, 54(12):121407

 端面抽运Nd∶YAG陶瓷1.83 μm激光

尉鹏飞 甘海波 俞 叶 段延敏 张 栋 章 健 朱海永

[摘要]报道了基于Nd∶YAG透明陶瓷4F3/2-4I15/2跃迁实现1.83 μm激光输出的研究。采用简单紧凑的平凹腔结构,结合对腔镜镀膜参数的设计,控制其他能级跃迁谱线对应波长激光的透射损耗来抑制较强能级跃迁对应的激光振荡。在入...

 PDF全文强激光与粒子束 | 2017, 29(04):041005

 Ce∶YAG透明陶瓷的制备及性能研究

曾群 修光捷 王飞 周佳宁

[摘要]以高纯Al2O3、Y2O3 和 CeO2 为原料, 采用固相法制备Ce∶YAG(掺铈钇铝石榴石)透明陶瓷, 研究了稀土离子掺杂浓度以及烧结温度对陶瓷样品光学性能的影响。结果表明: 陶瓷片透过率随着烧结温度的升高而增大, 1 750 ℃烧结...

 PDF全文发光学报 | 2016, 37(06):650

 固相法制备Ce,Cr∶YAG透明陶瓷及其荧光性能研究

修光捷 曾群 王飞 姚春凤

[摘要]以高纯Al2O3、Y2O3、Cr2O3和 CeO2 为原料, 采用固相法制备了Ce, Cr∶YAG透明陶瓷。通过XRD测试和荧光测试, 研究了0.5%Ce3+, 0.1%Cr3+掺杂的YAG透明陶瓷片的晶相结构和光学性能。结果表明:1 750 ℃烧结获得的该陶瓷片...

 PDF全文发光学报 | 2016, 37(10):1213

 基于YAG透明陶瓷制作衍射光栅元件的研究

李豪伟 龚勇清 夏侯命玖 肖孟超 罗宁宁

[摘要]研究并制作了以钇铝石榴石(YAG)透明陶瓷为基底材料的衍射光栅元件。通过磁控溅射技术在YAG透明陶瓷表面溅射一层均匀致密的金属铬, 获得带有硬掩模的陶瓷样品。借助接触式曝光系统进行光刻, 反复试验, 获得带有衍射光...

 PDF全文应用光学 | 2015, 36(01):98

 高超音速中波红外窗口材料思考

潘枝峰 毛小建 张红刚 李晓凯 冯明辉 张龙

[摘要]针对未来高超音速飞行器的发展趋势,阐述了红外窗口材料所面临的技术挑战。从高温透过范围、红外辐射系数、高温力学性能以及抗热冲击等角度分析比较了几种常见的中波红外材料,基于此认为Y2O3陶瓷是未来高超音速中波...

 PDF全文激光与光电子学进展 | 2014, 51(09):091601

 Nd: YAG陶瓷的烧结性能研究

吉祥波 邓建国 康彬 胥涛 敬畏 余盛全

[摘要]采用注浆成型和真空烧结制备了Nd: YAG激光透明陶瓷,研究了烧结温度和时间对致密化过程的影响。研究结果表明: 在1050~1300 ℃之间坯体发生明显的收缩生成YAM和YAP相; 在1300~1420 ℃,生成YAG相。随着烧结温度的增加...

 PDF全文强激光与粒子束 | 2014, 26(07):071007

 Tape casting of a YAG/Yb:YAG/YAG transparent ceramic for a broadband tunable laser

Chao Wang Wenxue Li Xianghui Yang Dongbi Bai Kangwen Yang Xuewei Ba Jiang Li Yubai Pan Heping Zeng

[摘要]

 PDF全文High Power Laser Science and Engineering | 2014, 2(04):e36

 YAG陶瓷激光器的研究进展

刘亚东 姚志健

[摘要]激光透明陶瓷具有良好的材料和光学特性, 并且具有较大的制备优势, 是有着较好前景的激光材料。与之相对应, 陶瓷激光器近年来引起了人们的广泛关注。主要综述了国内外YAG陶瓷激光器的进展。陶瓷激光器的发展虽然只有短...

 PDF全文激光技术 | 2013, 37(03):326-329

 白光LED用新型MgAl2O4/Ce∶YAG透明陶瓷的发光性能

贺龙飞 范广涵 雷牧云 娄载亮 郑树文 苏晨 肖瑶 陈志武 张涛

[摘要]采用金属醇盐法制备MgAl2O4前驱体, 通过高温煅烧2~4 h得到纯相MgAl2O4粉体, 再将其与YAG∶Ce荧光粉均匀混合, 利用热压烧结并结合热等静压处理得到MgAl2O4/Ce∶YAG透明陶瓷。 利用X射线衍射、紫外-可见分光光度计等测...

 PDF全文发光学报 | 2013, 34(02):133-138

 MgAl2O4/Ce∶YAG透明陶瓷的制备及光学性能

贺龙飞 范广涵 雷牧云 娄载亮 陈志武 肖瑶 郑树文 张涛

[摘要]采用金属醇盐法制备MgAl2O4前躯体, 通过高温煅烧2~4 h得到纯相MgAl2O4粉体, 再将其与YAG∶Ce荧光粉均匀混合, 利用热压烧结并结合热等静压处理得到MgAl2O4/Ce∶YAG透明陶瓷。 利用XRD, SEM, EDS和荧光光谱仪对样品进...

 PDF全文光谱学与光谱分析 | 2013, 33(05):1175-1179

 Preparation of (Tb0.8Y0.2)3Al5O12 transparent ceramic as novel magneto-optical isolator material

Chong Chen Yi Ni Shengming Zhou Hui Lin Xuezhuan Yi

[摘要]

 PDF全文Chinese Optics Letters | 2013, 11(02):021601

 Novel transparent ceramics for solid-state lasers

Hao Yang Jian Zhang Dewei Luo Hui Lin Deyuan Shen Dingyuan Tang

[摘要]

 PDF全文High Power Laser Science and Engineering | 2013, 1(3-4):3-4000138-147

 Ce3+∶BaF2多晶透明陶瓷的热压烧结法制备

翟朋飞 梅炳初 宋京红 李威威 李小女

[摘要]采用沉淀法制备了Ce3+∶BaF2纳米粉体, 研究了反应顺序和F-浓度对沉淀法制备Ce3+∶BaF2粉体的影响, 采用XRD、SEM、TEM、ICP等手段对粉体进行了分析。结果表明:采用阴离子滴入阳离子的反应顺序, 在较高F-浓度下制备的...

 PDF全文发光学报 | 2012, 33(07):698-706

 Effect of heat-treatment on properties of ytterbium and lanthanum co-doped yttria transparent ceramics

Haojia Zhang Qiuhong Yang Shenzhou Lu Dongdong Huang Yonggang Wang Yunhan Li Qing Wang Zhiyi Wei

[摘要]

 PDF全文Chinese Optics Letters | 2012, 10(s2):S21413

 Effects of Nd3+ concentration on properties of yttrium lanthanum oxide transparent ceramics

Shenzhou Lu Qiuhong Yang Haojia Zhang Yonggang Wang Dongdong Huang Qizhen Duan

[摘要]

 PDF全文Chinese Optics Letters | 2012, 10(s2):S21604

 Recent progress of laser performance in Nd-doped yttrium lanthanum oxide transparent ceramics

Qiuhong Yang Shenzhou Lu Haojia Zhang Qing Wang Zhiyi Wei Zhiguo Zhang

[摘要]

 PDF全文Chinese Optics Letters | 2012, 10(s2):S21417

 Investigation of emission properties of Tm3+:Y2O3 transparent ceramic

Qing Yi Taiju Tsuboi Shengming Zhou Yosuke Nakai Hui Lin Hao Teng

[摘要]

 PDF全文Chinese Optics Letters | 2012, 10(09):091602

 宽带激光烧结制备YAG透明陶瓷

庞驰 刘智勇 刘其斌

[摘要]采用共沉淀法合成钇铝石榴石(YAG)纳米粉体,经干压成型后进行宽带激光烧结,获得YAG透明陶瓷。利用X射线衍射(XRD)、扫描电镜(SEM)对YAG粉体及陶瓷进行表征,研究结果表明,前驱体经1100 ℃焙烧2 h后获得了纯相YAG粉体...

 PDF全文中国激光 | 2011, 38(01):0106001

 Lu2O3∶Eu3+纳米粉末及透明陶瓷的制备及其发光性能

王林香 祝恒江 尹民

[摘要]采用共沉淀法和溶剂热法制备了Lu2O3∶Eu3+纳米粉体,通过X射线衍射谱、傅里叶变换红外光谱和扫描电镜照片,比较了两种方法制备的Lu2O3∶Eu3+粉末的微观结构,测量和比较合成粉体的激发与发射光谱。将获得的Lu2O3∶Eu...

 PDF全文发光学报 | 2011, 32(09):913-919

 Synthesis and Luminescent Properties of LuAG∶Ce3+ Transparent Ceramics by Solvo-Thermal Method

N/A

[摘要]

 PDF全文光谱学与光谱分析 | 2011, 31(02):308-315

 激光烧结制备Nd:Y2O3透明陶瓷的研究

季凌飞 李智 蒋毅坚

[摘要]以微米级普通商业粉为原料, 采用CO2激光烧结技术获得可见光区透光率约60%、红外区透光率可达80%的Nd:Y2O3陶瓷。经1250°C预烧后的平均粉径约400 nm的原料粉素坯, 在~292 W/cm2的激光功率密度下烧结200~300s, 可...

 PDF全文应用激光 | 2011, 31(01):1-5

 透明陶瓷透光性能的影响因素

应建新 张彬 崔鑫 徐学珍

[摘要]研究了影响激光透明陶瓷透光性能的主要因素,讨论了陶瓷内部气孔和杂质颗粒等散射粒子、晶界结构中晶界折射率与晶粒折射率的差异以及晶界表面粗糙度等因素对陶瓷透光性能的影响,并定量分析了激光陶瓷透过率随气孔尺...

 PDF全文强激光与粒子束 | 2011, 23(03):581-585

 不同粉料制备Nd∶(Y0.9La0.1)2O3透明陶瓷及其性能

陆神洲 杨秋红 张浩佳

[摘要]分别采用液相法和固相法制备的纳米粉,制得透明性良好的Nd∶(Y0.9La0.1)2O3透明陶瓷,并测试了各样品的结构,光谱及光学性能.结果表明:该陶瓷具有相同的光谱性能;但液相法复合纳米粉制备的透明陶瓷光学性能优于固相反应...

 PDF全文光子学报 | 2010, 39(09):1553-1556

 Tb3+,Yb3+共掺Y2O3透明陶瓷的制备及其下转换近红外发光研究

林辉 周圣明 侯肖瑞 李宇焜 李文杰 滕浩 贾婷婷

[摘要]采用真空烧结制备了透明度良好的Tb3+,Yb3+共掺的(Tb0.01Y0.99-xYbx)2O3 (摩尔分数x=0,0.02,0.05,0.1)透明陶瓷。在484 nm的蓝光激发下,通过Tb3+离子的敏化作用,实现了Yb3+离子的下转换近红外发光。由Tb3+到Yb3+...

 PDF全文光学学报 | 2010, 30(12):3547-3551

 透明Nd:YAG激光陶瓷的研究与应用进展

唐杰 张林 魏成富 杨梨容 李晓武 廖承志

[摘要]综述了近年来, 特别是近两年来国内外透明Nd:YAG激光陶瓷的研究与应用情况, 重点对我国的透明Nd:YAG激光陶瓷研究近况进行了分析, 指出了透明Nd:YAG激光陶瓷是目前陶瓷研究的热点。提出了透明Nd:YAG激光陶瓷研究中尚存...

 PDF全文强激光与粒子束 | 2010, 22(08):1930-1934