应用激光, 2017, 37 (4): 586, 网络出版: 2017-10-12   

248 nm准分子激光刻蚀钠钙玻璃微通道低裂损工艺研究

The Study on Low Cracking of Soda-lime Glass Micro-Groove Etched by 248 nm Excimer Laser
作者单位
北京工业大学激光工程研究院, 北京 100124
摘要
248 nm准分子激光直接刻蚀钠钙玻璃微通道来制作生物芯片具有较大优势和潜力, 但目前存在易发生碎裂、微通道底面处粗糙度高等问题。采用248 nm准分子激光束以静态刻蚀及扫描直写刻蚀两种方式刻蚀钠钙玻璃来对低裂损工艺进行研究。首先通过实验研究了激光加工玻璃的工艺参数与玻璃微通道的刻蚀质量之间的关系, 然后分析了248 nm准分子激光刻蚀钠钙玻璃的裂损刻蚀机理, 最后通过变换工艺参数来设计新的加工工艺流程以改善加工质量。实验结果表明, 随着刻蚀处激光能量密度的增加, 玻璃微通道的边缘裂损程度增大, 并且刻蚀表面粗糙度增大, 刻蚀质量下降; 另外发现激光刻蚀后的粗糙表面可以增加玻璃材料对入射激光能量的吸收率, 从而降低了激光刻蚀玻璃材料的阈值, 较低的激光能量密度可降低刻蚀面的粗糙度。最后工艺流程改进实验, 所加工的微通道质量得到改善, 玻璃微通道边缘裂损尺寸小于5 μm, 底面粗糙度Ra值可降低至1.5 μm, 研究结果将对激光加工玻璃微结构的质量改善提供一定的参考。
Abstract
The soda-lime glass micro-groove is etched directly by 248 nm excimer laser to produce Bio-chip, which have great advantage and potentiality, but there are many problems now, such as it is easy to crack and the roughness of the groove bottom surface is very poor. Based on 248 nm excimer laser, two ways of processing soda-lime glass are used to study the low carcking in this paper, which are static etching and scanning etching. Firstly, the relationship between the process parameter and the quality of the glass micro-groove is studied by experiment, and then the mechanism of glass cracking processed by 248 nm excimer laser is analyzed. Finally, we have improved the process of etching glass micro-groove to improve the quality, which is changing the process parameter. From the experiment results, as the laser fluence increasing, the crack degree at the glass micro-groove edge is increasing and the roughness on the etching surface is also increasing, so the quality of the glass micro-groove is more and more poorer. The rough surface etched by laser can increase the absorption of incident laser energy, so the threshold of the laser etching glass material can be reduced, and the roughness of the etching surface can reduced by the lower laser fluence. From the experiment of process improved, the quality of the glass micro-groove is improved, the crack size at the glass micro-groove edge is less than 5 μm, the roughness of the bottom surface Ra can be reduced to 1.5 μm. So the results of this paper will provide a reference to improve the quality of laser processing glass microstructure.

杨桂栓, 陈虹, 陈涛. 248 nm准分子激光刻蚀钠钙玻璃微通道低裂损工艺研究[J]. 应用激光, 2017, 37(4): 586. Yang Guishuan, Chen Hong, Chen Tao. The Study on Low Cracking of Soda-lime Glass Micro-Groove Etched by 248 nm Excimer Laser[J]. APPLIED LASER, 2017, 37(4): 586.

本文已被 1 篇论文引用
被引统计数据来源于中国光学期刊网
引用该论文: TXT   |   EndNote

相关论文

加载中...

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!