氧化石墨烯与水溶性酞菁铜的表面增强拉曼散射光谱特性研究

Surface Enhanced Raman Scattering Spectrum Study on Graphene Oxide and Water Soluble Copper Phthalocyanine
作者单位
1 光电技术与系统教育部重点实验室, 重庆大学, 重庆 400044
2 重庆师范大学物理与电子工程学院, 重庆 400044
摘要
采用氧化石墨烯(GO)作为表面增强拉曼散射的基底, 水溶性酞菁铜(TSCuPc)作为探针分子, 实验探究了氧化石墨烯薄膜的层数和TSCuPc薄膜的厚度对拉曼散射增强的影响。 首先配制了不同浓度的GO溶液, 利用旋涂法在玻璃基底上制备了不同层数的GO膜, 然后通过调节TSCuPc薄膜的旋涂转速, 制备了GO和TSCuPc的复合薄膜。 实验结果表明, 当增加GO薄膜层数时, 由GO和TSCuPc产生的π—π共轭所感应的分子极化率和由GO含氧官能团感应的局域电场均增大, 因此TSCuPc分子的拉曼强度增大, 且随着层数的增加, 增强呈现饱和趋势; 而随着TSCuPc薄膜厚度的增加, 由于其自身分子间也存在π—π共轭, TSCuPc分子的拉曼光谱强度呈近似线性增加, 且由TSCuPc薄膜厚度引起的首层效应并不是很明显。 选用的可以溶液法成膜的TSCuPc分子, 通常被用作有机光电子器件的空穴注入材料, 研究GO与TSCuPc的表面增强拉曼光谱特性, 为优化器件参数以提高有机光电子器件的电荷转移效率等性能具有重要的意义。
Abstract
Graphene oxide (GO) was chosen as the Raman enhancement substrate, and the effect of the number of GO layers and probe molecule water soluble copper phthalocyanine (TSCuPc) films thickness on surface enhanced Raman scattering (SERS) was investigated. In our work, spin-coating method was carried out for preparing GO films with different number of GO layers by using different concentrations, and then different TSCuPc films were prepared by adjusting the speed. The results of the experiments showed that: with the increasing of the layer number of GO films, both the polarizability induced by π—π conjugation and local dipole moment induced by oxygen-containing groups increased, resulting in a stronger Raman enhancement presenting a saturated tendency. Meanwhile, the enhancement of characteristic peaks of TSCuPc linearly increased with the increasing of the thickness of TSCuPc films and compared to the influence of GO layer number, the first-layer effect resulting from the thickness of TSCuPc was less pronounced. The TSCuPc molecule prepared by solution method is generally used for hole injection layer of organic optoelectronic devices and there will be of great significance to improve the hole injection efficiency, transmission efficiency and stability of organic optoelectronic devices by researching the surface enhanced Raman spectrum of GO and TSCuPc.

崔少丽, 杜晓晴, 牛连斌, 曾超, 鲍俊, 李露, 陈伟民. 氧化石墨烯与水溶性酞菁铜的表面增强拉曼散射光谱特性研究[J]. 光谱学与光谱分析, 2017, 37(9): 2763. CUI Shao-li, DU Xiao-qing, NIU Lian-bin, ZENG Chao, BAO Jun, LI Lu, CHEN Wei-min. Surface Enhanced Raman Scattering Spectrum Study on Graphene Oxide and Water Soluble Copper Phthalocyanine[J]. Spectroscopy and Spectral Analysis, 2017, 37(9): 2763.

本文已被 1 篇论文引用
被引统计数据来源于中国光学期刊网
引用该论文: TXT   |   EndNote

相关论文

加载中...

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!