基于MoO3/Au/MoO3透明电极的有机太阳能电池

Organic Solar Cells Based on MoO3/Au/MoO3 Transparent Electrode
作者单位
重庆邮电大学 光电工程学院, 重庆 400065
摘要
以透明导电薄膜MoO3/Au/MoO3代替铟锡氧化物(ITO)作为有机太阳能电池(OSCs)的阳极, 研究了一系列结构为MoO3/Au/MoO3的透明电极和MoO3(y nm)/Au(x nm)/MoO3(y nm)/CuPc(25 nm)/C60(40 nm)/BCP(8 nm)/Al(100 nm)的有机太阳能电池。研究表明, MoO3/Au/MoO3电极的光电特性可通过改变各层薄膜厚度加以调控, 在MoO3薄膜厚度为40 nm、Au薄膜厚度为10 nm时性能最优, 且以该薄膜为电极的有机太阳能电池器件的性能接近于电极为ITO的有机太阳能电池器件。
Abstract
Transparent conductive film MoO3/Au/MoO3 was used as the anode of organic solar cells (OSCs) instead of indium tin oxide (ITO). A series of MoO3/Au/MoO3 transparent electrodes and OSCs with the structure of MoO3(y nm)/Au(x nm)/MoO3(y nm)/CuPc(25 nm)/C60(40 nm)/BCP(8 nm)/Al(100 nm) were fabricated. The results show that the photoelectric characteristics of MoO3/Au/MoO3 electrode can be controlled by changing the film thickness of each layer, the optimum performance of OSC is achieved when the thickness of MoO3 film is 40 nm and the thickness of Au film is 10 nm. Besides, the performance of the OSC with MoO3/Au/MoO3 electrode is close to that of OSC with ITO electrode.

王振, 柳菲, 郑新, 王培, 甘林, 汪静静. 基于MoO3/Au/MoO3透明电极的有机太阳能电池[J]. 发光学报, 2017, 38(10): 1332. WANG Zhen, LIU Fei, ZHENG Xin, WANG Pei, GAN Lin, WANG Jing-jing. Organic Solar Cells Based on MoO3/Au/MoO3 Transparent Electrode[J]. Chinese Journal of Luminescence, 2017, 38(10): 1332.

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!