Structural, Optical and Electrochromic Properties of WO3 Thin Films Prepared by Chemical Spray Pyrolysis Versus Spin Coating Technique

Structural, Optical and Electrochromic Properties of WO3 Thin Films Prepared by Chemical Spray Pyrolysis Versus Spin Coating Technique
作者单位
1 Department of Physics, Erzincan University, Erzincan 24000, Turkey
2 Pasinler Vocational School, Atatürk University, Erzurum 25040, Turkey
3 Department of Electrical and Electronics Engineering, Atatürk University, Erzurum 25040, Turkey
摘要
Abstract
In this study, Tungsten Oxide (WO3) thin films were prepared by Chemical Spray Pyrolysis (CSP) and Spin Coating (SC) techniques and it was investigated effects of technique and parameter on the films. WO3 thin films were deposited on ITO (Indium Tin Oxide) coated glasses. The structural, optical and electrochromic properties of the WO3 thin films were characterized by XRD, SEM, UV, and CV measurements. The sharpest (200) peak was observed in the XRD spectra and optical band gaps were calculated around 2.6~3.1 eV via UV-Vis spectra for all of the samples. Micro fibrous reticulated surface (filamentous like) morphology for the films deposited by CSP technique and smooth surface morphology with high optical transmittance for the film deposited by SC Technique were obtained from SEM images. In addition to these results, it was revealed that all the samples exhibit good electrochromic performance.

S. Morko Karadeniz, Demet Tatar, M. Erturul, A. E. Ekinci. Structural, Optical and Electrochromic Properties of WO3 Thin Films Prepared by Chemical Spray Pyrolysis Versus Spin Coating Technique[J]. 光谱学与光谱分析, 2018, 38(9): 2982. S. Morko Karadeniz, Demet Tatar, M. Erturul, A. E. Ekinci. Structural, Optical and Electrochromic Properties of WO3 Thin Films Prepared by Chemical Spray Pyrolysis Versus Spin Coating Technique[J]. Spectroscopy and Spectral Analysis, 2018, 38(9): 2982.

本文已被 1 篇论文引用
被引统计数据来源于中国光学期刊网
引用该论文: TXT   |   EndNote

相关论文

加载中...

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!