Effect of reduction co-sintering on the photoluminescence properties of phosphor in glass in boro-bismuthate glass

  • 摘要
  • 论文信息
  • 参考文献
  • 被引情况
  • PDF全文
分享:

Abstract

Phosphor in glass (PiG) employing Ce:Y3Al5O12 (YAG)-doped boro-bismuthate glass via low-temperature co-sintering technology was successfully prepared, using Bi2O3-B2O3-ZnO glass as the base material. The photoluminescence (PL) of PiG co-sintered at times ranging from 20 min to 60 min at 700°C was investigated. As a result, the relative PL intensity of PiG under a reducing atmosphere of CO showed significant enhancement of about 7–14 times that under air atmosphere sintering for 20–50 min. The PL intensity decreased gradually with the co-sintering time, which may be due to the corrosion of the YAG lattice structure.

Newport宣传-MKS新实验室计划
补充资料

DOI:10.3788/COL201917.101601

所属栏目:Materials

基金项目:This work was supported by the Science and Technology Planning Project of Zhejiang Province, China (No. 2018C01046) and the Enterprise-funded Latitudinal Research Projects (Nos. J2016-141, J2017-171, J2017-293, and J2017-243).

收稿日期:2019-06-06

录用日期:2019-08-02

网络出版日期:2019-09-12

作者单位    点击查看

Qiaoyu Zheng:School of Science, Shanghai Institute of Technology, Shanghai 201418, China
Yang Li:School of Material Science and Engineering, Shanghai Institute of Technology, Shanghai 201418, China
Wenjuan Wu:School of Science, Shanghai Institute of Technology, Shanghai 201418, China
Jun Zou:School of Science, Shanghai Institute of Technology, Shanghai 201418, ChinaInstitute of New Materials & Industrial Technology, Wenzhou University, Wenzhou 325024, China
Bobo Yang:School of Science, Shanghai Institute of Technology, Shanghai 201418, ChinaInstitute of Beyond Lighting, Academy for Engineering and Technology, Fudan University, Shanghai 200433, China
Mingming Shi:School of Science, Shanghai Institute of Technology, Shanghai 201418, China

联系人作者:Yang Li(liyang123@sit.edu.cn); Jun Zou( zoujun@sit.edu.cn);

备注:This work was supported by the Science and Technology Planning Project of Zhejiang Province, China (No. 2018C01046) and the Enterprise-funded Latitudinal Research Projects (Nos. J2016-141, J2017-171, J2017-293, and J2017-243).

【1】D. Q. Chen, W. D. Xiang, X. J. Liang, J. S. Zhong, H. Yu, M. Y. Ding, H. W. Lu and Z. G. Ji. Effect of reduction co-sintering on the photoluminescence properties of phosphor in glass in boro-bismuthate glass. J. Europ. Ceram. Soc. 35, (2014).

【2】C. C. Lin and R. S. Liu. Effect of reduction co-sintering on the photoluminescence properties of phosphor in glass in boro-bismuthate glass. J. Phys. Chem. Lett. 2, (2011).

【3】W. H. Zhang, Y. P. Zhang, S. Y. Ouyang, Z. X. Zhang and H. P. Xia. Effect of reduction co-sintering on the photoluminescence properties of phosphor in glass in boro-bismuthate glass. Mater. Lett. 160, (2015).

【4】M. Y. Chen, R. J. Yu, Z. G. Tian and X. Z. Bai. Effect of reduction co-sintering on the photoluminescence properties of phosphor in glass in boro-bismuthate glass. Chin. Opt. Lett. 4, (2006).

【5】H. Li, X. J. Xu, Y. Li, S. Wu, P. J. Tian and Y. Tian. Effect of reduction co-sintering on the photoluminescence properties of phosphor in glass in boro-bismuthate glass. J. Alloys Comp. 684, (2016).

【6】J. Xu, Dhia A. Hassan, R. J. Zeng and D. L. Peng. Effect of reduction co-sintering on the photoluminescence properties of phosphor in glass in boro-bismuthate glass. J. Europ. Ceramic Soc. 36, (2016).

【7】L. L. Yi, H. He, Y. Dong, W. S. Hu, Y. H. Jin and W. Q. Sun. Effect of reduction co-sintering on the photoluminescence properties of phosphor in glass in boro-bismuthate glass. Chin. Opt. Lett. 9, (2011).

【8】X. B. Luo, R. Hu, S. Liu and K. Wang. Effect of reduction co-sintering on the photoluminescence properties of phosphor in glass in boro-bismuthate glass. Progress Energy Combust. Sci. 56, (2016).

【9】H. Lin, B. Wang, J. Xu, R. Zhang, H. Chen, Y. L. Yu and Y. S. Wang. Effect of reduction co-sintering on the photoluminescence properties of phosphor in glass in boro-bismuthate glass. ACS Appl. Mater. Interfaces. 6, (2014).

【10】Y. S. Qi, L. Zhao, W. J. Bian, X. H. Xu and J. B. Qiu. Effect of reduction co-sintering on the photoluminescence properties of phosphor in glass in boro-bismuthate glass. Chin. Opt. Lett. 15, (2017).

【11】E. F. Schubert and J. K. Kim. Effect of reduction co-sintering on the photoluminescence properties of phosphor in glass in boro-bismuthate glass. Science. 308, (2005).

【12】K. Han, S. H. Lee, Y. G. Choi, W. B. Lm and W. J. Chung. Effect of reduction co-sintering on the photoluminescence properties of phosphor in glass in boro-bismuthate glass. J. Non-Crystal. Solids. 445, (2016).

【13】W. N. Gao, Y. Shen, Y. Bo, W. P. Zhang, Y. Bi and Z. Y. Xu. Effect of reduction co-sintering on the photoluminescence properties of phosphor in glass in boro-bismuthate glass. Chin. Opt. Lett. 15, (2017).W. N. Gao, Y. Shen, Y. Bo, W. P. Zhang, Y. Bi and Z. Y. Xu. Effect of reduction co-sintering on the photoluminescence properties of phosphor in glass in boro-bismuthate glass. Chin. Opt. Lett. 15, (2017).

【14】R. Zhang, H. Lin, Y. L. Yu, D. Q. Chen, J. Xu and Y. S. Wang. Effect of reduction co-sintering on the photoluminescence properties of phosphor in glass in boro-bismuthate glass. Laser Photon. Rev. 8, (2014).

【15】X. J. Zhang, J. B. Wang, C. B. Zhu, J. H. Zhang, R. Zou, B. F. Lei, Y. L. Liu and M. M. Wu. Effect of reduction co-sintering on the photoluminescence properties of phosphor in glass in boro-bismuthate glass. ACS Appl. Mater. Interfaces. 7, (2015).

【16】E. K. Ji, Y. H. Song, M. J. Lee and D. H. Yoon. Effect of reduction co-sintering on the photoluminescence properties of phosphor in glass in boro-bismuthate glass. Mater. Lett. 157, (2015).

【17】J. G. Zhong, X. H. Zhang and Z. X. Ju. Effect of reduction co-sintering on the photoluminescence properties of phosphor in glass in boro-bismuthate glass. Chin. Opt. Lett. 6, (2008).J. G. Zhong, X. H. Zhang and Z. X. Ju. Effect of reduction co-sintering on the photoluminescence properties of phosphor in glass in boro-bismuthate glass. Chin. Opt. Lett. 6, (2008).

【18】C. C. Tsai, Y. C. Hsu, S. B. Huang, Y. J. Lin, J. Wang, M. H. Chen, C. W. Lee, H. L. Hu and W. H. Cheng. Effect of reduction co-sintering on the photoluminescence properties of phosphor in glass in boro-bismuthate glass. IEEE Trans. Device Mater. Reliab. 9, (2009).

【19】Y. H. Kim, N. M. Viswanath, S. Unithrattil, H. J. Kim and W. B. Im. Effect of reduction co-sintering on the photoluminescence properties of phosphor in glass in boro-bismuthate glass. ECS J. Solid State Sci. Technol. 7, (2018).

【20】Y. Peng, Y. Mou, Q. L. Sun, H. Cheng, M. X. Chen and X. B. Luo. Effect of reduction co-sintering on the photoluminescence properties of phosphor in glass in boro-bismuthate glass. J. Alloys Compd. 790, (2019).

【21】Y. Peng, Y. Mou, Y. Zhou, H. Li, X. Z. Wang, M. X. Chen and X. B. Luo. Effect of reduction co-sintering on the photoluminescence properties of phosphor in glass in boro-bismuthate glass. J. Alloys Compd. 768, (2018).

【22】Y. Peng, Y. Mou, H. Wang, Y. Zhou, H. Li, M. X. Chen and X. B. Luo. Effect of reduction co-sintering on the photoluminescence properties of phosphor in glass in boro-bismuthate glass. J. Eur. Ceram. Soc. 38, (2018).

【23】Z. T. Li, H. Y. Wang, B. H. Yu, X. R. Ding and Y. Tang. Effect of reduction co-sintering on the photoluminescence properties of phosphor in glass in boro-bismuthate glass. Chin. Opt. Lett. 15, (2017).

【24】S. Fujita, S. Yoshihara, A. Sakamoto, S. Yamamoto and S. Tanabe. Effect of reduction co-sintering on the photoluminescence properties of phosphor in glass in boro-bismuthate glass. Proc. SPIE. 5941, (2005).

【25】G. Dai, Y. B. Chen, J. Lu, Z. H. Shen and X. W. Ni. Effect of reduction co-sintering on the photoluminescence properties of phosphor in glass in boro-bismuthate glass. Chin. Opt. Lett. 7, (2009).

【26】S. Tanabe, S. Fujita, S. Yoshihara, A. Sakamoto and S. Yamamoto. Effect of reduction co-sintering on the photoluminescence properties of phosphor in glass in boro-bismuthate glass. Proc. SPIE. 5941, (2005).

【27】Y. K. Lee, J. S. Lee, J. Heo, W. B. Lm and W. J. Chung. Effect of reduction co-sintering on the photoluminescence properties of phosphor in glass in boro-bismuthate glass. Opt. Lett. 37, (2012).

【28】J. S. Lee, S. Unithrattil, S. Kim, I. J. Lee, H. Lee and W. B. Im. Effect of reduction co-sintering on the photoluminescence properties of phosphor in glass in boro-bismuthate glass. Opt. Lett. 38, (2013).

【29】Y. Li, L. L. Hu, B. B. Yang, M. M. Shi and J. Zou. Effect of reduction co-sintering on the photoluminescence properties of phosphor in glass in boro-bismuthate glass. Chin. Phys. B. 26, (2017).

【30】H. Y. Zhou, J. Zou, Y. Li, W. J. Wu, M. M. Shi, B. B. Yang and Z. M. Wang. Effect of reduction co-sintering on the photoluminescence properties of phosphor in glass in boro-bismuthate glass. J. Non-Crystal. Solids. 475, (2017).

【31】Z. M. Wang, J. Zou, Y. Li, C. Y. Zhang, M. M. Shi, B. B. Yang, H. Y. Zhou, Y. M. Liu and N. X. Liu. Effect of reduction co-sintering on the photoluminescence properties of phosphor in glass in boro-bismuthate glass. J. Mater. Sci.: Mater. Electron. 28, (2017).

【32】L. B. XiaL. B. Xia. Effect of reduction co-sintering on the photoluminescence properties of phosphor in glass in boro-bismuthate glass. Preparation and Properties of YAG:Ce3+ Embedded Glass Ceramic Based on Bismuth Borate Glass for WLED. (2018).

【33】A. D. Sontakke, J. Ueda and S. Tanabe. Effect of reduction co-sintering on the photoluminescence properties of phosphor in glass in boro-bismuthate glass. J. Lumin. 170, (2016).

【34】J. Ueda, S. Tanabe and T. A. Nakanishi. Effect of reduction co-sintering on the photoluminescence properties of phosphor in glass in boro-bismuthate glass. J. Appl. Phys. 110, (2011).

【35】J. Zou, B. B. Yang, J. R. Li, S. M. Zhu, X. L. Qian and F. C. Wang. Effect of reduction co-sintering on the photoluminescence properties of phosphor in glass in boro-bismuthate glass. Ceram. Int. 42, (2016).

【36】E. PaparazzoE. Paparazzo. Effect of reduction co-sintering on the photoluminescence properties of phosphor in glass in boro-bismuthate glass. Mater. Res. Bulletin. 46, (2011).

【37】Y. Tang, S. M. Zhou, X. Z. Yi, D. M. Hao, X. C. Shao and J. Chen. Effect of reduction co-sintering on the photoluminescence properties of phosphor in glass in boro-bismuthate glass. J. Alloys Comp. 745, (2018).

【38】N. S. Sawala and S. K. Omanwar. Effect of reduction co-sintering on the photoluminescence properties of phosphor in glass in boro-bismuthate glass. Res. Chem. Intermediates. 43, (2017).

【39】N. S. Sawala, P. R. Somani and S. K. Omanwar. Effect of reduction co-sintering on the photoluminescence properties of phosphor in glass in boro-bismuthate glass. J. Mater. Sci.: Mater. Electron. 28, (2017).

引用该论文

Qiaoyu Zheng, Yang Li, Wenjuan Wu, Jun Zou, Bobo Yang, Mingming Shi, "Effect of reduction co-sintering on the photoluminescence properties of phosphor in glass in boro-bismuthate glass," Chinese Optics Letters 17(10), 101601 (2019)

您的浏览器不支持PDF插件,请使用最新的(Chrome/Fire Fox等)浏览器.或者您还可以点击此处下载该论文PDF