激光与光电子学进展, 2019, 56 (21): 211402, 网络出版: 2019-11-02   

激光表面重熔蠕墨铸铁气门座微观特性分析和裂纹抑制研究 下载: 706次

Microscopic Characteristic Analysis and Crack Suppression of Laser-Surface Remelting of Vermicular-Graphite Cast-Iron Valve Seats
作者单位
中国民航大学机场学院, 天津 300300
摘要
利用额定功率为3 kW的Nd∶YAG固体激光器开展激光重熔蠕墨铸铁气门座实验,通过扫描电镜、显微硬度仪,采用荧光粉探伤方法分析激光表面重熔蠕墨铸铁气门座的宏观形貌、显微组织、硬度分布以及重熔层是否存在裂纹。结果表明:经激光表面重熔后,重熔层中部区域组织为枝晶组织,在枝晶组织间弥散分布着针状物和颗粒状物;石墨的扩散降低了材料熔点,由于激光的快速加热和冷却等,重熔层与基体交界处形貌为锯齿形,且在热影响区观察到马氏体壳和莱氏体壳的双壳组织;不同区域的加热和冷却速度的差异导致重熔区表面到基体硬度逐渐降低;调控激光参数可以有效抑制气门座激光重熔层的裂纹。在激光功率为500 W,离焦量为-1 mm,激光扫描速度小于等于5 mm/s的重熔工艺参数下,可以获得无裂纹的重熔层。
Abstract
Experiments on the laser-surface remelting of vermicular-graphite cast-iron valve seats are performed in this study using a Nd∶YAG solid-state laser with a rated power of 3 kW. The macroscopic morphology, microstructure, hardness distribution, and cracks of the remelting layer of the laser-surface remelting of the vermicular-graphite cast-iron valve seats are analyzed using a scanning electron microscope, microhardness tester, and phosphor flaw detection method. The results show that after the surface of the vermicular-graphite cast-iron valve seats is remelted using a laser, the dendritic structures appear in the central region of the remelting layer and the needles and granules are dispersed among the dendritic structures. The morphology of the interface between the remelting layer and substrate is serrated, and the bivalve structure of the martensite and ledeburite shells is observed in the heat-affected zone because of factors such as the diffusion of graphite reducing the melting point of the material in the vicinity of the graphite and rapid heating and cooling of the laser. The hardness from the remelting-zone surface to the substrate gradually decreases because of the differences in the heating and cooling rates in the different regions of laser remelting of the valve seats. The cracks in the laser remelting layer of the valve seats can be restrained by adjusting the laser parameters. A remelting layer without cracks on the surface of the vermicular-graphite cast-iron valve seats of laser remelting can be obtained under the laser remelting process with parameters of laser power P=500 W, defocusing amount Δf=-1 mm, and laser scanning velocity V≤5 mm/s.

庞铭, 谭雯丹. 激光表面重熔蠕墨铸铁气门座微观特性分析和裂纹抑制研究[J]. 激光与光电子学进展, 2019, 56(21): 211402. Ming Pang, Wendan Tan. Microscopic Characteristic Analysis and Crack Suppression of Laser-Surface Remelting of Vermicular-Graphite Cast-Iron Valve Seats[J]. Laser & Optoelectronics Progress, 2019, 56(21): 211402.

本文已被 1 篇论文引用
被引统计数据来源于中国光学期刊网
引用该论文: TXT   |   EndNote

相关论文

加载中...

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!