中国激光, 2020, 47 (3): 0302009, 网络出版: 2020-03-12   

油气管道激光除漆对基材组织和硬度的影响 下载: 788次

Laser Removal of Coating on Oil and Gas Pipelines: Effects on Microstructure and Hardness of Substrate
作者单位
中国民航大学机场学院, 天津 300300
摘要
为了研究激光对油气管道外防腐层剥离的可行性,以及漆层清除对基体性能的影响,采用短脉冲激光器对X65管线钢上的环氧树脂防腐层进行激光除漆实验。采用三维形貌测试仪对除漆后的表面进行测试,并使用扫描电镜与能谱分析仪对试样的表面和横截面进行测试分析。两个试样经不同工艺参数的激光扫描后,漆层基本全部剥离,基体表面呈现出密集的火山口形貌,表层以下出现了带状区和裂纹区;试样A、B表层以下带状区的厚度分别约为20 μm和10 μm,裂纹区厚度分别约为100 μm和90 μm,表层硬度均小幅提升。本研究所采用的激光参数既满足了钢管除漆的要求,又对表层起到了强化作用。管道激光除漆技术在技术上是可行的,值得深入研究。
Abstract
To study the feasibility of laser exfoliation of the external coating of oil and gas pipelines and the effects of coating removal on the properties of the substrate, laser coating removal experiments were conducted on the epoxy resin coating on the X65 pipeline steel using a short-pulse laser. After coating removal, the pipe external surfaces were tested using a three-dimensional morphology tester. The surface and cross-section of each sample were tested and analyzed using scanning electron microscopy and energy spectrum analysis. After the two samples were irradiated using different laser technical parameters, the coating layers were almost completely exfoliated. At the same time, dense crater morphology was evident on the surface and strip-shaped and crack regions appeared below the surface. The strip-shaped regions beneath the surface were about 20 μm and 10 μm thick for samples A and B, respectively, while the crack regions were about 100 μm and 90 μm thick, respectively, and the hardness of both the samples'' surfaces increased slightly. The laser technical parameters used in this research not only meet the requirements of laser coating removal for steel pipes but also strengthen the surface. Thus, coating removal is technologically feasible for steel pipelines and valuable for further investigation.

江国业, 雷璞, 刘宇平, 李敏, 庞铭, 胡艳娇. 油气管道激光除漆对基材组织和硬度的影响[J]. 中国激光, 2020, 47(3): 0302009. Jiang Guoye, Lei Pu, Liu Yuping, Li Min, Pang Ming, Hu Yanjiao. Laser Removal of Coating on Oil and Gas Pipelines: Effects on Microstructure and Hardness of Substrate[J]. Chinese Journal of Lasers, 2020, 47(3): 0302009.

本文已被 5 篇论文引用
被引统计数据来源于中国光学期刊网
引用该论文: TXT   |   EndNote

相关论文

加载中...

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!