研究了镀铬后试样与普通试样在经过激光诱导复合毛化处理后显微硬度与金相的情况。通过对放电坑组织的分析,可以看出放电坑的熔凝组织分为两层:熔凝层和相变硬化层,热影响层在光学显微镜下不明显。熔凝层的最高硬度在900HV左右,大大高于45#钢基体200HV和镀Cr后300HV的硬度。在相变硬化层中,硬度随着相对表面距离的增大而逐渐下降。

标    签 激光 复合毛化 镀铬 laser texturing chromium plating
 

In this work, laser-guided discharge and alloying were combined together to get the both advantage of the two. It was also found that the structure of material melted in 45# steel were divided into two layers: the melted layer and the phase-change hardened layer. The heat-affecting layer was not clear to see. The highest part of structure’s rigidity reached 900HV which was much higher than the 45# steel (200HV) and 45# plating with Cr.

中图分类号
 
      

所属栏目

基金项目

收稿日期 2009-12-16

修改稿日期


引用该论文 Zhang Kuang. Surface Chromium Plating in Laser-guided Discharge Texturing[J]. 应用激光, 2010, 30(2): 105～107 (in chinese)
张匡. 45#钢镀铬激光诱导放电复合毛化条件下的金相初步研究[J]. 应用激光, 2010, 30(2): 105～107 【1】关振中主编.激光加工工艺手册[M].北京:中国计量出版社,1998:338-400.
 
【2】YAG激光毛化技术的深度开发[R].北京:中国科学院,2000.
 
【3】李怀学,张坤,陈光南,等.镀铬/高能束复合表面处理研究进展[J].材料保护,2007,40(4):39-41,49
 

 一种基于激光测距的汽车安全报警装置研究

 高能量密度下激光粒子加速等研究的最新进展和展望

 激光核聚变的发展

 高能量密度下激光粒子加速等研究的最新进展和展望

 一种快速有效的基于激光视觉的焊缝跟踪实时图像处理方式

 海上激光斜程传输的大气透过率研究

 激光 点亮未来的医食住行

 高能量密度下激光粒子加速等研究的最新进展和展望

 激光点焊技术浅析

 第四届太平洋国际激光与光学应用会议-PICALO 2010

 高能量密度下激光粒子加速等研究的最新进展和展望

 激光光子复合治疗面部毛细血管扩张症疗效观察