溶剂热法制备铜锌锡硫粉末及光学性能研究

刘立华; 刘九扬; 邰新; 董丽荣; 华中

doi:doi:10.13883/j.issn1004-5929.201604014

光散射学报, 2016, 28 (4): 364, 网络出版: 2017-01-17

溶剂热法制备铜锌锡硫粉末及光学性能研究

Preparation and Optical Properties of Cu₂ZnSnS₄ Powders by Solvothermal Method

论文大纲

刘立华 ^*刘九扬邰新董丽荣华中

作者单位

吉林师范大学功能材料物理与化学教育部重点实验室,四平 136000

溶剂热光学性能 solvothermal Cu2ZnSnS4 Cu2ZnSnS4 optical properties

摘要

以金属氯化物作为金属源,硫脲为硫源,乙二醇为溶剂,聚乙烯吡咯烷酮(PVP)为表面活性剂,采用溶剂热法在较低反应温度下合成了Cu2ZnSnS4(CZTS)粉末。利用X射线衍射仪(XRD)、拉曼光谱(Raman)、扫描电子显微镜(SEM)、高分辨透射电子显微镜(HRTEM)对样品的结构和形貌进行表征。利用紫外-可见光谱(UV-Vis)对样品的光学性能进行研究。结果表明,180 ℃反应25小时的样品均为锌黄锡矿CZTS颗粒,颗粒形貌为表面花状的微球。当体系中PVP含量为0.2 g时,微球尺寸约为2.5 μm。当体系中PVP含量为03 g,0.4 g,0.5 g时,微球尺寸大约为1.1 μm。其中,PVP含量为0.4 g的样品分散性较好,在可见区有明显的吸收,用外延法得到其禁带宽度约为1.45 eV,与太阳能电池所需的最佳禁带宽度接近。

Abstract

Cu2ZnSnS4(CZTS)powders were synthesized at lower temperature by solvothermal method in ethylene glycol with metal chloride as metal precursors,thiourea as sulfur source,and polyvinylpyrrolidone(PVP) as surfactant.The crystal structures and morphology of the samples were characterized by X-ray diffraction (XRD),Raman spectroscopy,Scanning Electron Microscope (SEM),and Transmission Electron Microscopy (TEM).The optical properties of the samples were investigated by UV-Vis spectrum(UV-Vis).The results indicate that kesterite CZTS particles were prepared at 180 ℃ for 25 h.Under this condition,the microspheres with flower-like surface were obtained.The diameters of the microspheres were about 2.5 μm for the sample prepared at 0.2 g of PVP in the reaction system.While the diameters of the microspheres were about 1.1 μm for the samples prepared at 0.3 g,0.4 g and 0.5 g of PVP.The sample prepared at 0.4 g of PVP was more disperse and possessed an obvious absorption in the visible region.The band gap is estimated to be about 1.45 eV by extrapolation.Such a band gap is close to the optimum band gap for solar cell.

参考文献

[1] Sarswat P K,Free M L,Tiwari A.Temperature-dependent study of the Raman a mode of Cu2ZnSnS4 thin films［J］.Phys Status Solidi B,2011,248(9):2170-2174.

[2] Chirila A.Buecheler S,Pianezzi F,et al.Highly efficient Cu(In,Ga)Se2solar cells grown on flexible polymer films［J］.Nat Mater,2011,10(11):857-861.

[3] Jackson P,Hariskos D,Lotter E,et al.New world record efficiency for Cu(In,Ga)Se2thin-film solar cells beyond 20%［J］.Prog Photovolt Res Appl.2011,19(7):894-897.

[4] Guo Qi Jie,Hillhouse H W,Agrawal R.Synthesis of Cu2ZnSnS4 nanocrystal ink and its use for soar cells［J］.J Am Chem Soc,2009,131(33):11672-11673.

[5] Riha S C,Parkinson B A,Prieto A L.Solution-based synthesis and characterization of Cu2ZnSnS4 nanocrystals ［J］.J Am Chem Soc,2009,131(34):12054-12055.

[6] Steinhagen C,Panthani M G,Akhavan V,et al.Synthesis of Cu2ZnSnS4 nanocrystals for use in low-cost photovoltaics［J］.J Am Chem Soc,2009,131(35):12554-12555.

[7] 张亚非,魏浩,郭炜,等.铜锌锡硫太阳电池吸收层薄膜的制备方法［P］.中国专利: 200910195771.

[8] Tanaka T,Nagatomo T,Kawasaki D,et al.Preparation of Cu2ZnSnS4 thin films by hybrid sputtering［J］.J Phys Chem Solids,2005,66(11):1978-1981.

[9] Tanaka T,Yoshida A,Saiki D,et al.Influence of composition ratio on properties of Cu2ZnSnS4 thin films fabricated by co-evaporation［J］.Thin Solid Films,2010,518(21):S29-S33.

[10] Kamoun N,Bouzouita H,Rezig B.Fabrication and characterization of Cu2ZnSnS4 thin films deposited by spray pyrolysis technique［J］.Thin Solid Films,2007,515(15):5949-5952.

[11] Yakuphanoglu F.Nanostructure Cu2ZnSnS4 thin film prepared by sol-gel for optoelectronic applications［J］.Sol Energy,2011,85(10):2518-2523.

[12] Chalapathy R B V,Jung G S,Ko Y M,et al.Reaction path of Cu2ZnSnS4 nanoparticles by a solvothermal method using copper acetate,zinc acetate,tin chloride and sulfur in diethylenetriamine solvent［J］.Current Photovoltaic Research,2013,1(2):109-114.

[13] Zaberca O,Oftinger F,Chane-Ching J Y,et al.Surfactant-free CZTS nanoparticles as building blocks for low-cost solar cell absorbers［J］.Nanotechnology,2012,23(18):185402(1-11).

[14] Ahmed S,Reuter K B,Gunawan O,et al.A high efficiency electrodeposited Cu2ZnSnS4 solar cell ［J］.Adv Energy Mater,2012,2(2):253-259.

[15] Li Z Q,Shi J H,Liu Q Q,et al.Large-scale growth of Cu2ZnSnSe4 and Cu2ZnSnSe4/Cu2ZnSnS4 core/shell nanowires［J］.Nanotechnology,2011,22(26):265615(1-8).

刘立华, 刘九扬, 邰新, 董丽荣, 华中. 溶剂热法制备铜锌锡硫粉末及光学性能研究[J]. 光散射学报, 2016, 28(4): 364. LIU Li-hua, LIU Jiu-yang, TAI Xin, DONG Li-rong, HUA Zhong. Preparation and Optical Properties of Cu₂ZnSnS₄ Powders by Solvothermal Method[J]. The Journal of Light Scattering, 2016, 28(4): 364.

溶剂热法制备铜锌锡硫粉末及光学性能研究

关于本站 Cookie 的使用提示

全站搜索

溶剂热法制备铜锌锡硫粉末及光学性能研究

相关论文

相关资讯

关于本站 Cookie 的使用提示

全站搜索