高功率激光熔凝AZ91HP镁合金组织和性能

高亚丽; 王存山; 刘红宾; 姚曼

中国激光, 2007, 34 (7): 1019, 网络出版: 2007-08-17

高功率激光熔凝AZ91HP镁合金组织和性能

Microstructure and Properties of AZ91HP Magnesium Alloy Treated by High Power Laser Melting

论文大纲

高亚丽 ^1,*王存山 ¹刘红宾 ¹姚曼 ²

作者单位

¹ 大连理工大学1三束材料改性国家重点实验室, 辽宁大连 116023

² 大连理工大学材料学院, 辽宁大连 116023

激光技术镁合金激光熔凝组织性能 laser technique magnesium alloy laser melting microstructure property

摘要

在真空条件下对AZ91HP镁合金进行了高功率激光熔凝处理。研究结果表明,在高功率激光快速扫描下,熔凝层主要由分布于α-Mg枝晶间的板条状β-Mg17Al12构成,硬质相β-Mg17Al12含量较原始镁合金有所增加。随激光功率增加,熔凝层树枝晶尺寸逐渐增大,且长度方向上的增加幅度约为宽度方向上增加幅度的10倍。由于枝晶细化和β-Mg17Al12的强化作用,与原始镁合金相比,熔凝层的硬度约提高90%左右,耐磨性提高78%,耐蚀性显著提高。

Abstract

AZ91HP magnesium alloy was treated by laser melting in vacuum. The results showed that with high power laser and rapidly scanning speed, the melted layers mainly consisted of α-Mg dendrite and lath-shaped β-Mg17Al12 distributing in the inter-dendrite, and the melted layer contained more β-Mg17Al12 than that of as-received Mg alloy. With the increase of laser powers, the grain dimension of the melted layer increased, and the increased amplitude along the long direction was 10 times of that along the width direction. Because of the grain refinement and the enhancement of the hard phase β-Mg17Al12, the microhardness of the melted layer was increased by 90%, the wear resistance was increased by 78%, and the corrosion resistance was significantly improved compared with as-received Mg alloy.

参考文献

[1] . . Development and application of magnesium alloys in China[J]. Materials of Mechanical Engineering, 2001, 25(1): 6-10.

[2] . . Development of surface treatment for magnesium alloys[J]. Materials Protection, 2002, 35(3): 1-4.

[3] J. Dutta Majumdar, R. Galun, B. L. Mordike et al.. Effect of laser surface melting on corrosion and wear resistance of a commercial magnesium alloy [J]. Materials Science and Engineering A, 2003, 361(1-2):119～129

[4] G. Abbas, Z. Liu, P. Skeldon. Corrosion behaviour of laser-melted magnesium alloys [J]. Applied Surface Science, 2005, 247(1-4):347～353

[5] Sorin Ignat, Pierre Sallamand, Dominnique Grevey et al.. Magnesium alloys (WE43 and ZE41) characterisation for laser applications [J]. Applied Surface Science, 2004, 233(1-4):382～391

[6] Ghazanfar Abbas, Lin Li, Uzma Ghazanfar et al.. Effect of high power diode laser surface melting on wear resistance of magnesium alloys [J]. Wear, 2006, 260(1-2):175～180

[7] Liu Hongbin, Wang Cunshan, Gao Yali. Laser cladding amorphous composite coating of Cu-Zr-Al on magnesium alloy surface [J]. Chinese J. Lasers, 2006, 33(5):709～713
刘红宾,王存山,高亚丽. 镁合金表面激光熔覆Cu-Zr-Al非晶复合涂层[J]. 中国激光, 2006, 33(5):709～713

[8] D. Dube, M. Fiset, A. Couture et al.. Characterization and performance of laser melted AZ91D and AM60B [J]. Materials Science and Engineering A, 2001, 299(1-2):38～45

[9] Chen Zhenhua, Xia Weijun, Yan Hongge et al.. Deformed Magnesium [M]. Beijing: Chemical Industry Press, 2005. 58
陈振华,夏伟军,严红革等. 变形镁合金[M]. 北京：化学工业出版社, 2005. 58

[10] Shu Delin. Metal Mechanical Property 2 [M]. Beijing: China Machine Press, 1999. 171
束得林. 金属力学性能2[M]. 北京:机械工业出版社, 1999. 171

[11] . Zhou. Evaluation of microstructual effects on corrosion behavior of AZ91D magnesium alloy[J]. Corrosion Science, 2000, 42: 1433-1455.

[12] . . Corrosion behavior of AZ21, AZ501 and AZ91 in sodium chloride[J]. Corrosion Science, 1998, 40(10): 1769-1791.

[13] Xu Ping. Effect of Ce, Nd, Sr on the microstructure and corrosion property of magnesium alloy AZ91 [D]. Wuhan University of Technology, 2005
徐萍. Ce,Nd,Sr对AZ91镁合金显微组织和腐蚀性能的影响[D]. 武汉理工大学, 2005

[14] . High-frequency induction for surface alloying of magnesium alloy ZM5 and its corrosion behavior[J]. Rare Metal Materials and Engineering, 2003, 32(3): 191-193.

高亚丽, 王存山, 刘红宾, 姚曼. 高功率激光熔凝AZ91HP镁合金组织和性能[J]. 中国激光, 2007, 34(7): 1019. 高亚丽, 王存山, 刘红宾, 姚曼. Microstructure and Properties of AZ91HP Magnesium Alloy Treated by High Power Laser Melting[J]. Chinese Journal of Lasers, 2007, 34(7): 1019.

高功率激光熔凝AZ91HP镁合金组织和性能

关于本站 Cookie 的使用提示

全站搜索

高功率激光熔凝AZ91HP镁合金组织和性能

相关论文

相关资讯

关于本站 Cookie 的使用提示

全站搜索