718塑料模具钢激光合金化与氮化组织性能的比较
The Research of Microstructure and Property of Laser Alloying on the Surface of 718 Steel Compared with Nitriding
摘要
在718钢表面进行了超细碳化钨(WC)激光合金化的实验, 利用金相显微镜、维氏硬度计等设备检测了合金化层的组织和性能。通过与氮化试样的比较, 表明激光合金化可以得到晶粒细化, 深度大, 硬度高, 与基体结合牢固的表面强化层。塑料注射成型模具大量使用 718钢作为型芯、型腔等零部件的成型材料。上述成型零部件在磨损、侵蚀和注塑压力的共同作用下, 表面容易发生尺寸、形状的变化而影响成型精度。采用激光合金化强化后, 在 718钢表面形成优良的耐磨层, 大大提高了模具的使用寿命。
Abstract
The experiment of laser alloying on the surface of 718 steel was made. Tungsten carbide (WC) powder was used asalloying material. The microstructure and property of laser alloying layer and nitriding layer are studied. The comparison betweenthem shows that laser alloying layer has better properties such as minute crystals, deeper layer, higher hardness and goodmetallurgical bonding with base metal. 718 steel is widely used in the field of plastic mold manufacture, especially mold core andcavity. Abrasion, corrosion and pressure result in change of mold size and shape which can greatly affect molding precision. Usinglaser alloying, the good wear layer would be made on the surface of 718 steel and greatly increase the mold useful life.
参考文献
[1] 郭幼丹. 塑料模具的磨损机制与失效机理的研究[J]. 机械设计与制造, 2007(1): 139-141.
[2] 冯晓曾编. 模具用钢和热处理[M]. 北京: 机械工业出版社, 1984: 56-75.
[3] 张迪, 单际国. 高能束熔覆技术的研究现状及发展趋势[J]. 激光技术, 2001, 25(1): 39-42.
[4] 王秀彦, 王秀凤. 激光模具表面强化的应用研究[J]. 锻压机械, 2000, 45(4): 3-6.
[5] 张伟, 姚建华. 海水泵轴激光修复试验研究[J]. 应用激光, 2004, 24(6): 342-344.
[6] 王存山. 40Cr钢搭接激光淬火组织研究 [J]. 应用激光, l998, 18(4): 149-150.
[7] 王振华,揭晓华. 718塑料模具钢激光相变硬化层的性能研究[J]. 热加工工艺, 2008, 37(6): 22-24.
张伟, 石淑琴, 陈云祥, 姚建华, 王瑞权, 林波. 718塑料模具钢激光合金化与氮化组织性能的比较[J]. 应用激光, 2011, 31(2): 117. Zhang Wei, Shi Shuqin, Chen Yunxiang, Yao Jianhua, Wang Ruiquan, Lin Bo. The Research of Microstructure and Property of Laser Alloying on the Surface of 718 Steel Compared with Nitriding[J]. APPLIED LASER, 2011, 31(2): 117.