激光沉积成形熔池尺寸分析与预测

激光沉积制造过程中, 单道沉积宽度主要受激光熔池宽度的制约, 稳定的熔池是保证成形精度的前提。为了建立工艺参数激光功率、扫描速度以及送粉速率与熔池尺寸之间的经验模型, 采用非匀速段关光控制及卡尔曼滤波技术对采集的熔池测量数据进行去噪处理, 以实现成形过程熔池宽度的精确检测, 为熔池宽度预测精度提供了保证。基于正交试验建立了多元回归模型, 其拟合优度可达94%, 最大误差不超过4.5%。经单一变量试验方法验证, 结果表明熔池宽度与激光功率呈正相关, 与扫描速度呈负相关, 实验结果与回归分析结果具有较好的一致性。

Abstract

During laser deposition manufacturing process, the forming width of the single track is mainly controlled by the melt pool width. However, high geometric accuracy is premised on the stable size of the melt pool. In order to establish an empirical model described relationship between the melt pool width and main process parameters (laser power, scanning speed, and powder feeding rate), turn off laser control in uneven speed stage was used and Kalman filtering was applied to denoise the measured data of the melt pool width. An empirical model between the process parameters of laser deposition and the width of molten pool was established based on orthogonal experimental design with a goodness-of-fit of 94%, and the maximum error was less than 4.5%. The results of single variable experiments conducted to the model show that the melt pool width has a positive correlation to the laser power and a negative to the scanning speed. The experimental results were in good agreement with the regression analysis.

参考文献

[1] Alaa Elwany, Gustavo Tapia. A review on process monitoring and control in metal-based additive manufacturing [J]. Manufacturing Science and Engineering, 2014, 136(6): 1-10.

[2] Shi Qimin, Gu Dongdong, Xia Mujian, et al. Effects of laser processing parameters on thermal behavior and melting/solidification mechanism during selective laser melting of Tic/Inconel718 composites [J]. Optics & Laser Technology, 2016, 84: 9-22.

[3] Zhong Chongliang, Andres Gasser, Jochen Kittel, et al. Improvement of material performance of Inconel718 formed by high deposition-rate laser metal deposition [J]. Material and Design, 2016, 98: 128-134.

[4] Yu Jun, Lin Xin, Chen Junjie, et al. Mechanics and energy analysis on molten pool spreading during laser solid forming [J]. Applied Surface Science, 2010, 256: 4612-4620.

[5] Jiang Shujuan, Liu Weijun, Xiang Fei. Research on measuring and control system of metal powder laser shaping [C]//International Conference on Mechatronics and Automation, 2006: 1717-1721.

[6] Han Lijun, Liou F W, Srinvas Musti. Thermal behavior and geometry model of melt pool in laser material process[J]. Department of Mechanical and Aerospace, 2005, 127: 1005-1014.

[7] Ravi G A, Hao X J, Wain N, et al. Direct laser fabrication of three dimensional components using SC420 stainless steel [J]. Materials and Design, 2013, 47: 731-736.

[8] Amitava De, Tarasankar Debroy. Heat transfer and material flow during laser assisted multi-layer additive manufacturing [J]. Journal of Applied Physics, 2014, 116(116): 124905.

[9] Lie Tang, Robert G. Melt pool temperature control for laser matal depisition processes-Part1: Online temperature control [J]. Journal of Manufacturing Science and Engineering, 2010, 132: 0110101-0110109.

[10] Qiu Chunlei, Ravi G A, Chris Dance, et al. Fabrication of large Ti-6Al-4V structures by direct laser deposition [J]. Journal of Alloys and Compounds, 2015, 692: 351-361.

[11] Parisa Farahmand, Liu Shuang, Zheng Zhe, et al. Laser cladding assisted by induction heating of Ni–WC composite enhanced by nano-WC and La2O3[J]. Ceramics International, 2014, 40(10): 15421-15438.

[12] Tan Hua, Chen Jing, Lin Xin, et al. Process analysis for laser solid forming of thin-wall structure [J]. International Journal of Machine Tools & Manufacture, 2010, 50(1): 1-8.

[13] S 觟rn Ocylok, Eugen Alexeev, Stefan Mann, et al. Correlation of melt pool geometry and process parameters during laser metal deposition by coaxial process monitoring [J]. Physics Procedia, 2014, 56: 228-238.

[14] Song Lijun, Vijayavel Bagavath-Singh, Bhaskar Dutta, et al. Control of melt pool temperature and deposition height during direct metal deposition process [J]. Int J Adv Manuf Technol, 2012, 58(1): 247-256.

[15] Tabernero I, Lamikiz A, Martínez S, et al. Geometric modelling of added layers by coaxial laser cladding [J]. Physics Procedia, 2012, 39: 913-920.

[16] Ding Yaoyu, James Warton, Radovan Kovacevic. Development of sensing and control system for robotized laser-based direct metal addition system [J]. Additive Manufacturing, 2016, 10: 24-35.

[17] 彭丁聪.卡尔曼滤波的基本原理及应用 [J]. 软件导刊, 2009, 8(11): 32-35.

Peng Dingcong. Basic principle and application of Kalman filter [J]. Software Guide, 2009, 8(11): 32-35. (in Chinese)

[18] Liu Jichang, Li Lijun. Effects of process variables on laser direct formation of thin wall [J]. Science Direct, 2007, 39: 231-236.

[19] Onwubolu G C, Davim J P, Carlos Oliveira, et al. Prediction of clad angle in laser cladding by powder using response surface methodology and scatter search[J]. Optics & Laser Technology, 2007, 39: 1130-1134.

钦兰云, 徐丽丽, 杨光, 刘奇, 王维. 激光沉积成形熔池尺寸分析与预测[J]. 红外与激光工程, 2018, 47(11): 1106009. Qin Lanyun, Xu Lili, Yang Guang, Liu Qi, Wang Wei. Analysis and prediction of melt pool size in laser deposition manufacturing[J]. Infrared and Laser Engineering, 2018, 47(11): 1106009.

激光沉积成形熔池尺寸分析与预测

关于本站 Cookie 的使用提示

全站搜索

激光沉积成形熔池尺寸分析与预测

相关论文

相关资讯

关于本站 Cookie 的使用提示

全站搜索