基于Logistic回归模型的钛合金件激光直接成形工艺参数分析

如果使用激光金属直接成形方法制备金属零件时，能够通过最优的工艺参数来有效地控制金属成形件内部的不同区域及成形件与基板间的温度梯度和能量分布，使成形件内部产生缺陷的几率减小，会极大地提升成形件的力学性能。针对激光金属直接成形方法制备金属零件内部是否存在缺陷的二分类问题，通过使用正交旋转实验设计的方法进行工艺实验，得到不同参数下的钛合金激光金属直接成形试样是否存在内部缺陷情况。对实验结果进行Logistic回归建模，使用Logistic回归模型计算的工艺参数进行验证实验，样件内部未发现内部缺陷，说明Logistic回归模型结果与实际结果有较高的一致性。Logistic回归模型对激光金属直接成形工艺参数的选择具有积极的指导意义。

Abstract

When machining metal parts with laser metal deposition shaping (LMDS) method, if the temperature gradients and energy distributions of different areas inside cladding layer and that between cladding layer and substrate can be effectively controlled with optimal process parameters, then the probability of internal defects of cladding layer can be reduced, and the mechanical properties will be greatly improved. To the problem whether the metal parts made by LMDS contain internal defects, rotatable orthogonal experiments are designed for acquiring the distributions of internal defects of the metal parts under different process parameters. A logistic regression model is built based on these experimental data. Finally an authentication test is taken with the process parameters calculated by the logistic regression model, and no internal defects are found. The results show that the logistic regression model is in good agreement with the actual situation. The logistic regression model proposed in this paper is proved to have the guiding significance for selecting LMDS process parameters.

参考文献

[1] 王华明. 金属材料激光表面改性与高性能金属零件激光金属直接成形技术研究进展［J］. 航空学报, 2002, 23(5): 473～478

Wang Huaming. Research progress on laser surface modifications of metallic materials and laser rapid forming of high performance metallic components［J］. Acta Aeronauticaet Astronautica Sinica, 2002, 23(5): 473～478

[2] 王华明, 张述泉, 王向明. 大型钛合金结构件激光直接制造的进展与挑战［J］. 中国激光, 2009, 36(12): 3204～3209

Wang Huaming, Zhang Suquan, Wang Xiangming. Progress and challenges of laser direct manufacturing of large titanium structural components［J］. Chinese J. Lasers, 2009, 36(12): 3204～3209

[3] 李鹏. 基于激光熔覆的三维金属零件激光直接制造技术研究［D］. 武汉: 华中科技大学, 2005

Li Peng. Direct Laser Fabrication of 3-Dimentional Metal Parts Based on Laser Cladding［D］. Wuhan: Huazhong University of Science and Technology, 2005

[4] 张凤英, 陈静, 谭华等. 钛合金激光快速成形过程中缺陷形成机理研究［J］. 稀有金属材料与工程, 2007, 36(2): 211～215

Zhang Fengying, Chen Jing, Tan Hua et al.. Research on forming mechanism of defects in laser rapid formed titanium alloy［J］. Rare Metal Materials and Engineering, 2007, 36(2): 211～215

[5] 张霜银, 林鑫, 陈静等. 工艺参数对激光快速成形TC4钛合金组织及成形质量的影响［J］. 稀有金属材料与工程, 2007, 36(10): 1839～1843

Zhang Shuangyin, Lin Xin, Chen Jing et al.. Influence of processing parameter on the microstructure and forming characterizations of Ti-6Al-4V titanium alloy after laser rapid forming processing［J］. Rare Metal Materials and Engineering, 2007, 36(10): 1839～1843

[6] 杨光, 刘伟军, 王维等. 钛合金激光快速成形工艺研究［J］. 制造技术与机床, 2010, (6): 50～53

Yang Guang, Liu Weijun, Wang Wei et al.. Research on process of titanium alloy laser rapid prototyping［J］. Manufacturing Technology & Machine Tool, 2010, (6): 50～53

[7] 张丽君, 高勃, 王忠义等. 激光快速成形纯钛与瓷的结合性能研究［J］. 中国激光, 2009, 36(5): 1273～1277

Zhang Lijun, Gao Bo, Wang Zhongyi et al.. Evaluation of bond characteristics between poreelain and titanium fabricated by rapid laser forming［J］. Chinese J. Lasers, 2009, 36(5): 1273～1277

[8] 关泰红, 高勃, 吕晓卫等. 激光快速成形工艺参数对生物陶瓷复合涂层物相组成的影响［J］. 中国激光, 2009, 36(10): 2717～2721

Guan Taihong, Gao Bo, Lü Xiaowei et al.. Effect of technologic parameters on phases of bioceramic coating prepared by laser rapid forming［J］. Chinese J. Lasers, 2009, 36(10): 2717～2721

[9] 王济川, 郭志刚. Logistic回归模型——方法与应用［M］. 北京: 高等教育出版社. 2001

Wang Jichuan, Guo Zhigang. Logistic Regression Models: Methods and Application［M］. Beijing: Higher Education Press, 2001

[10] 耿金花, 高齐圣, 任敬喜等. 基于Logistic回归的社区满意度模型［J］. 控制与决策, 2007, 22(11): 1305～1308

Geng Jinhua, Gao Qisheng, Ren Jingxi et al.. Community satisfaction model based on logistic regression［J］. Control and Decision, 2007, 22(11): 1305～1308

[11] 国家标准化技术委员会.量和单位GB/T7233.1-2009［S］. 北京: 中国标准出版社, 2009

National Standardization Technical Committee. GB/T7233.1-2009. Quantities and Units GB/T7233.1-2009［S］. Beijing: China Standard Press, 2009

孔源, 刘伟军, 王越超, 王靖震, 杨光. 基于Logistic回归模型的钛合金件激光直接成形工艺参数分析[J]. 中国激光, 2011, 38(11): 1103005. Kong Yuan, Liu Weijun, Wang Yuechao, Wang Jingzhen, Yang Guang. Analysis of Process Parameters about Direct Laser Metal Deposition Shaping Process of Titanium Alloys Based on Logistic Regression Model[J]. Chinese Journal of Lasers, 2011, 38(11): 1103005.

基于Logistic回归模型的钛合金件激光直接成形工艺参数分析

关于本站 Cookie 的使用提示

全站搜索

基于Logistic回归模型的钛合金件激光直接成形工艺参数分析

相关论文

相关资讯

关于本站 Cookie 的使用提示

全站搜索