光纤激光焊接5052铝合金镁元素烧损研究

张宏圭; 金湘中; 陈根余; 张明军; 邹宇峰

doi:doi:10.3969/j.issn.1001-3806.2012.06.001

激光技术, 2012, 36 (6): 713, 网络出版: 2012-11-07

光纤激光焊接5052铝合金镁元素烧损研究

Study on the burning loss of magnesium element in fiber laser welding aluminum alloy 5052

论文大纲

张宏圭金湘中 ^*陈根余张明军邹宇峰

作者单位

湖南大学汽车车身先进设计制造国家重点实验室, 长沙 410082

激光技术镁元素烧损激光焊接铝合金光谱信号 laser technique magnesium element burning loss laser welding aluminum alloy spectral signals

摘要

为了研究铝合金激光焊接过程中镁元素的蒸发烧损, 采用特殊设计的实验装置采集了激光深熔焊接5052铝合金过程中孔内等离子体的光谱信号, 并用电子探针显微分析仪检测了焊缝中的镁元素。发现激光焊接工艺参量对工件表面的镁元素等离子体信号强度的影响很大, 小孔中各位置的光谱强度是变化的, 在小孔的径向方向MgⅠ的相对强度逐渐减小, 而在小孔的深度方向先增加后降低; 焊缝区镁元素含量的变化趋势与光谱强度的变化趋势相反。结果表明, 采用光谱仪能够监测激光焊接铝合金过程中镁元素的烧损; 小孔中不同位置处镁元素的烧损主要由各位置吸收的激光能量决定, 材料吸收的激光能量越高, 镁元素的烧损越大。

Abstract

In order to study the burning loss of magnesium element in laser welding aluminum alloy, a specially-designed device was first used to collect the spectral signals emitted from the keyhole plasma in deep penetration laser welding aluminum alloy 5052. Then, the content of magnesium element in the welds was tested by an electron probe micro analyzer. Under the experimental conditions, the welding parameters heavily affect the spectral intensity of magnesium element plasma. The spectral intensity is not uniformly distributed in the keyhole region. In the radial direction, the spectral intensity of MgⅠ decreases from the center to the edge of the keyhole; in the depth direction, from the top to the bottom of the keyhole, the spectral intensity of MgⅠ increases first and then decreases. The Mg content changes inversely with the spectral intensity in the keyhole region. Therefore, spectral analysis technology can be used to monitor the burning loss of magnesium element in laser welding aluminum. It can be concluded that Mg loss in the keyhole region is determined by laser intensity absorbed there. The higher the absorbed laser intensity, the bigger the Mg loss.

参考文献

[1] EL-BATAHGY A, KUTSUNA M. Laser beam welding of AA5052,AA5083 and AA6061 aluminum alloys［J］.Advances in Materials Science and Engineering, 2009,2009: 974182.

[2] BROWN K R, VENIE M S, WOODS R A. The increasing use of aluminum in automotive applications［J］.Journal of Metals, 1995, 47(7): 20-23.

[3] KUO T Y, LIN H C. Effects of pulse level of Nd∶YAG laser on tensile properties and formability of laser weldments in automotive aluminum alloys［J］.Materials Science and Engineering,2006,A416(1/2): 281-289.

[4] WANG H L, HUANG W L, ZHOU Z Y, et al. Laser welding of aluminum alloy 2007［J］.Laser Technology,2003,27(2): 24-26(in Chinese).

[5] LI H, HUANG A G, LI J, et al. Investigation on solidification crack of laser welding ZL114A aluminum alloy［J］. Laser Technology, 2010, 34(2): 154-156(in Chinese).

[6] ZHAO H, WHITE D R, DEBROY T. Current issues and problems in laser welding of automotive aluminum alloy［J］. International Materials reviews, 1999, 44(6): 238-266.

[7] NATSUNA A, KATAYAMA S, KOJIMA K. CO2 laser weld ability of aluminum alloys (report 1): effect of welding conditions on melting characteristics ［J］. Welding International, 1998, 12(7): 519-528.

[8] MOON D W, METZBOWER E A. Laser beam welding of aluminum alloy 5456［J］.Welding Journal Research supplement, 1983, 62: 53-58.

[9] WANG X J. Laser welding of aluminum alloys 5083 and 5052［J］. Journal of Gansu University of Technology, 1994, 20(4): 1-6 (in Chinese).

[10] JANDAGHI M, PARVINAR P, TORKAMANY M J, et al. Measurement of the composition change in Al5754 alloy during long pulsed Nd∶YAG laser welding based on LIBS［J］. Journal of Physics, 2009, D42(20): 205301-205308.

[11] PASTOR M, ZHAO H, MARTUKANITZ R P, et al. Porosity, underfill and magnesium loss during continuous wave Nd∶YAG laser welding of thin plates of aluminum alloys 5182 and 5754［J］. Welding Research Supplement, 1999, 78(6): 207-216.

[12] SIBLLANO T, ANCONA A, BERARDI V, et al. Correlation spectroscopy as a tool for detecting losses of ligand elements in laser welding of aluminium alloys［J］. Optics and Lasers in Engineering, 2006, 44 (12): 1324-1335.

[13] SIBILLANO T, ANCONA A, BERADI V, et al. A study of the shielding gas influence on the laser beam welding of AA5083 aluminum alloys by in-process spectroscopic investigation［J］. Optics and Lasers in Engineering, 2006, 44 (10): 1039-1051.

[14] CHENG Y Y, JIN X Z, LI S C, et al. Fresnel absorption and inverse bremsstrahlung absorption in an actual 3-D keyhole during deep penetration CO2 laser welding of aluminum 6016［J］. Optics & Laser Technology, 2012, 44 (5): 1426-1436.

张宏圭, 金湘中, 陈根余, 张明军, 邹宇峰. 光纤激光焊接5052铝合金镁元素烧损研究[J]. 激光技术, 2012, 36(6): 713. ZHANG Hong-gui, JIN Xiang-zhong, CHEN Gen-yu, ZHANG Ming-jun, ZOU Yu-feng. Study on the burning loss of magnesium element in fiber laser welding aluminum alloy 5052[J]. Laser Technology, 2012, 36(6): 713.

光纤激光焊接5052铝合金镁元素烧损研究

关于本站 Cookie 的使用提示

全站搜索

光纤激光焊接5052铝合金镁元素烧损研究

相关论文

相关资讯

关于本站 Cookie 的使用提示

全站搜索