一种水性聚氨酯涂层红外发射率的研究

肖圣荣; 张桐; 王智勇; 刘鹏瑞

红外技术, 2016, 38 (2): 0107, 网络出版: 2016-04-05

一种水性聚氨酯涂层红外发射率的研究

The Research on the Infrared Emissivity of Water-borne Polyurethane Coatings

论文大纲

肖圣荣 ^*张桐王智勇刘鹏瑞

作者单位

北京航空材料研究院，北京 100095

水性涂料聚氨酯红外隐身红外发射率 water-borne coatings polyurethane infrared stealthy the infrared emissivity

摘要

：本文以铝粉作为功能填料，分别与水性聚氨酯和溶剂型聚氨酯配合制备了红外低发射率隐身涂层，并采用红外光谱、扫描电镜等手段测试了涂层的力学性能、耐溶剂性能和法向红外发射率性能。结果表明，两种功能涂层在力学性能和耐溶剂性能方面性能相当。水性涂层在3～5 μm 和8～14 μm 窗口内发射率分别为0.33 和0.52，高于溶剂型涂层的0.32 和0.39；涂层的发射率随着铝粉粒径的增大而降低，当粒径约为45 μm 时，涂层的红外发射率可降至0.34@3～5 μm 和0.42@8～14 μm，这与溶剂型聚氨酯涂层的发射率相当。因此，采用水性聚氨酯替代溶剂型聚氨酯制备低污染性、环境友好的红外隐身涂层是有可能的。

Abstract

In this paper, the low infrared emissivity coatings are prepared by adding aluminium powder as a functional filler to two components of water-borne polyurethane and solvent-borne polyurethane respectively. The mechanical properties, the solvent resistance property and the infrared emissivity of the coatings are investigated with infrared spectrums and scanning electron microscopy. The results indicate that mechanical properties and resistance to liquids of such two kinds of coatings are equal. The infrared emissivity of water-borne polyurethane coatings with aluminium powder is 0.33@3～5 μm and 0.52@8～ 14 μm, while the coatings of solvent-borne polyurethane is 0.32 and 0.39; the infrared emissivity of coatings decreases with sizes of aluminium powder increase；when the size of aluminium powder is 45 μm, the infrared emissivity of the coatings is 0.341 and 0.421, which is equal to the solvent-borne polyurethane coatings. Therefore, the low pollution and environmentally friendly properties of water-borne polyurethane probably make it be alternative to the solvent-borne polyurethane for preparing the low infrared emissivity coatings.

参考文献

[1] 乐洪宇. 红外隐身技术与隐身涂料的发展[J]. 战术导弹技术, 2011(5): 121-126.

LE Hong-yu. Development of infrared stealth technology and stealth coating[J]. Tactical Missile Technology, 2011(5): 121-126.

[2] 付伟. 红外隐身原理及其应用技术[J]. 红外与激光工程, 2002, 31(1): 87-93.

FU Wei. Principle and application technology of IR stealth[J]. Infrared and Laser Engineering, 2002, 31(1): 87-93.

[3] 张伟钢, 徐国跃, 薛连海. 低红外发射率材料研究进展[J]. 红外技术, 2015, 37(5):361-367

ZHANG Wei-gang, XU Guo-yue, XUE Lian-hai. Research progress of low infrared emissivity materials[J]. Infrared Technology, 2015, 37(5): 361-367.

[4] 游敏聪, 杜仕国, 施冬梅. 红外隐身涂料黏合剂的应用与研究[J]. 现代涂料与涂装, 2006(7): 50-54.

YOU Yu-cong, DU Shi-guo, SHI Dong-mei. Application and research of the infrared camouflage coatings[J]. Modern Paint & Finishing, 2006(7): 50-54.

[5] CRISTIANE C SANTOS, MARCIA C DDELPECH, FERNANDA M B C. Thermal and mechanical profile of cast films from waterborne polyurethanes based on polyether block copolymers[J]. Journal of Materials Science, 2009, 44(5): 1317-1323.

[6] 李金旗. 用于水性双组分聚氨酯涂料的水性树脂和水可分散聚异氰酸酯[J]. 上海涂料, 2008, 46(10): 21-24.

LI Jin-qi. The aqueous resin and dispersible polyisocyanate for waterborne two-component polyurethane coatings[J]. Shang Hai Coatings, 2008, 46(10): 21-24.

[7] KIM B K, LEE J C. Waterborne polyurethanes and their properties[J]. Journal of Polymer Science Part A: Polymer Chemistry, 1996, 34(2): 1095-1104.

[8] WERNER J B, VALENTINO J. Properties of crosslinked polyurethane dispersions[J]. Progress in Organic Coatings, 2009, 27(4): 1-15.

[9] NTANOV J, BLANK J. Crosslinking of waterborne polyurethane dispersions[J]. Journal of Coating Technology, 1995, 848(67): 88-97.

[10] BRUCHMANN B, WOLFF S, HEIDER W, et al. Preparation of biuret containing polyisocyanate. US, 7022874[P]. 2006-04-04.

[11] 王庭慰, 程从亮, 张其土. 8～14 m 波长低红外发射率涂料的研究[J]. 光学技术, 2005, 31(4): 598-602.

WANG Ting-wei, CHENG Cong-liang, ZHANG Qi-tu. Study on low infrared emissivity of coating in 8～14 m[J]. Optical Technique, 2005, 31(4): 598-602.

[12] 陈红. 水性聚氨酯涂料技术进展[J]. 涂料工业, 2006, 36(3): 47-51.

CHEN Hong. Progress on waterborne Polyurethane coatings[J]. Paint & Coatings Industry, 2006, 36(3): 47-51.

[13] 叶圣天, 刘朝辉, 贾艺凡, 等. 填料表面改性技术在红外隐身涂料中的应用[J]. 红外技术, 2015, 37(12): 1058-1062.

YE Sheng-tian, LIU Zhao-hui, JIA Yi-fan, et al. Research on surface modification of fillers in infrared stealth coatings[J]. Infrared Technology, 2015, 37(12): 1058-1062.

[14] 汪金花, 张兴元, 戴家兵. 不同软段聚氨酯的红外光谱定量分析 [J]. 分析化学研究报告, 2007(7): 964-968.

WANG Jin-hua, ZHANG Xing-yuan, DAI Jia-bing. Quantitative analysis of polyurethane with different soft segments[J]. Chinese Journal of Analytical Chemistry, 2007(7): 964-968.

肖圣荣, 张桐, 王智勇, 刘鹏瑞. 一种水性聚氨酯涂层红外发射率的研究[J]. 红外技术, 2016, 38(2): 0107. XIAO Shengrong, ZHANG Tong, WANG Zhiyong, LIU Pengrui. The Research on the Infrared Emissivity of Water-borne Polyurethane Coatings[J]. Infrared Technology, 2016, 38(2): 0107.

一种水性聚氨酯涂层红外发射率的研究

关于本站 Cookie 的使用提示

全站搜索

一种水性聚氨酯涂层红外发射率的研究

相关论文

相关资讯

关于本站 Cookie 的使用提示

全站搜索