光子学报, 2020, 49 (4): 0414004, 网络出版: 2020-04-24
激光冲击690高强钢位错组态与晶粒细化的实验研究 下载: 659次
Experimental Study on Dislocation Configuration and Grain Refinement of 690 High Strength Steel Treated by Laser Shock Processing
图 & 表
图 1. SEM image of 690 high strength steel with power density of 5.09 GW/cm2
Fig. 1. SEM image of 690 high strength steel with power density of 5.09 GW/cm2
图 2. TEM image of 690 high-strength steel matrix
Fig. 2. TEM image of 690 high-strength steel matrix
图 3. TEM image of 690 high strength steel with power density of 5.09 GW/cm2
Fig. 3. TEM image of 690 high strength steel with power density of 5.09 GW/cm2
图 4. HRTEM image and corresponding IFFT filtered image of the precipitated phase
Fig. 4. HRTEM image and corresponding IFFT filtered image of the precipitated phase
图 6. HRTEM image of 690 high strength steel matrix by laser shock processing
Fig. 6. HRTEM image of 690 high strength steel matrix by laser shock processing
图 7. Dislocation configurations in the matrix of laser shocked 690 high strength steel
Fig. 7. Dislocation configurations in the matrix of laser shocked 690 high strength steel
图 8. Schematic diagram of screw dislocation motion at different cutting heights
Fig. 8. Schematic diagram of screw dislocation motion at different cutting heights
图 9. TEM image and selective electron diffraction pattern of different regions of the surface of 690 high-strength steel by laser shock
Fig. 9. TEM image and selective electron diffraction pattern of different regions of the surface of 690 high-strength steel by laser shock
图 10. Dislocation change characteristics of IFFT filtered image on the surface of 690 high-strength steel by multiple strong laser shock
Fig. 10. Dislocation change characteristics of IFFT filtered image on the surface of 690 high-strength steel by multiple strong laser shock
表 1690高强钢化学成分与机械性能
Table1. Chemical composites of 690 high-strength steel and mechanical capacity
|
曹宇鹏, 杨聪, 施卫东, 花国然, 李彬, 李荣. 激光冲击690高强钢位错组态与晶粒细化的实验研究[J]. 光子学报, 2020, 49(4): 0414004. Yu-peng CAO, Cong YANG, Wei-dong SHI, Guo-ran HUA, Bin LI, Rong LI. Experimental Study on Dislocation Configuration and Grain Refinement of 690 High Strength Steel Treated by Laser Shock Processing[J]. ACTA PHOTONICA SINICA, 2020, 49(4): 0414004.