激光冲击强化铝合金焊接接头的性能

以水为透明约束层，采用调Q(脉冲高峰值功率)的YAG激光对A6061-T6铝合金熔化极惰性气体保护焊接接头焊趾附近进行了激光冲击强化，并对比研究了A6061-T6铝合金焊接接头在激光冲击强化与焊态下的性能。试验结果表明，激光冲击强化的铝合金焊接接头与焊态下的相比，其冲击强化区的维氏硬度得到明显提高，焊接接头疲劳寿命得到较大幅提升；焊态下的试样疲劳断口位于焊缝或焊缝近旁，激光冲击强化下的试样疲劳断口位于基体金属上；激光冲击强化后在材料近表面获得了较大的残余压应力，其最大值约为-145 MPa；与基体金属相比，激光冲击强化后的表面粗糙度增大。

Abstract

In the present work, laser shock processing (LSP) using a Q-switch YAG laser facility with high pulsed peak power under water environment is implemented near the toes of A6061-T6 Aluminum alloy metal-inert gas (MIG) welded joints. And the properties of A6061-T6 aluminum alloy MIG welded joints is analyzed before and after laser shock processing through the comparative method. The results show that after laser shock processing, Vickers hardness and fatigue life of the welded joints have been significantly improved, fatigue fracture of the welded joint without laser shock processing is located in or near the welded while it is located on the base material after laser shock processing, and a larger near-surface residual compressive stress with a maximum value of about -145 MPa is obtained. Compared with the base material, the surface roughness deteriorates after laser shock processing.

参考文献

[1] Montross C S, Tao Wei, Lin Ye, et al.. Laser shock processing and its effects on microstructure and properties of metal alloys[J]. International Journal of Fatigue, 2002, 24(10): 1021-1036.

[2] Hatamleh O, Lyons J, Forman R. Laser and shot peening effects on fatigue crack growth in friction stir welded 7075-T7351 aluminum alloy joints[J]. International Journal of Fatigue, 2007, 29(3): 421-434.

[3] 邹世坤, 王健, 王华明. 激光冲击处理对焊接接头力学性能的影响(I)[J]. 焊接学报, 2001, 22(3): 79-81.

Zhou Shikun, Wang Jian, Wang Huaming. The effects of laser shock processing on mechanical properties of welded joints (I)[J]. Transactions of the China Welding Institution, 2001, 22(3): 79-81.

[4] 葛茂忠, 项建云, 张永康. 激光冲击处理对AZ31B镁合金焊接件抗应力腐蚀的影响[J]. 中国激光, 2012, 39(12): 1203007.

Ge Maozhong, Xiang Jianyun, Zhang Yongkang. Effect of laser shock processing on resistance to stress corrosion cracking of tungsten Inert-Gas welded AZ31B magnesium alloy[J]. Chinese J Lasers, 2012, 39(12): 1203007.

[5] 李伟, 李应红, 何卫锋, 等. 激光冲击强化技术的发展和应用[J]. 激光与光电子学进展, 2008, 45(12): 15-19.

Li Wei, Li Yinghong, He Weifeng, et al.. Development and application of laser shock processing[J]. Laser & Optoelectronics Progress, 2008, 45(12): 15-19.

[6] See D W, Dulaney J L, Clauer A H, et al.. The air force manufacturing technology laser peening initiative[J]. Surface Engineering, 2002, 18(1): 32-36.

[7] 周建忠, 张兴权, 王广龙, 等. 金属板料激光喷丸成形新技术[J]. 中国工程科学, 2005, 7(11): 94-97.

Zhou Jianzhong, Zhang Xingquan, Wang Guanglong, et al.. A new technology of plastic forming plate by laser peening[J]. Engineering Science, 2005, 7(11): 94-97.

[8] 殷苏民, 张超, 王匀, 等. 激光冲击对不锈钢焊接结构影响的数值分析[J]. 中国激光, 2013, 40(5): 0503005.

Yin Sumin, Zhang Chao, Wang Yun, et al.. Numerical analysis for the structure effect on stainless steel welding treated by laser shock processing[J]. Chinese J Lasers, 2013, 40(5): 0503005.

[9] 闫世兴, 董世运, 徐滨士, 等. Fe314合金熔覆层残余应力激光冲击消除机理[J]. 中国激光, 2013, 40(10): 1003004.

Yan Shixing, Dong Shiyun, Xu Binshi, et al.. Mechanics of removing residual stress of Fe314 cladding layers with laser shock processing[J]. Chinese J Lasers, 2013, 40(10): 1003004.

[10] Berthe L, Fabbro R, Peyre P, et al.. Shock waves from a water-confined laser-generated plasma[J]. J Appl Phys, 1997, 82(6): 2826-2832.

[11] Grevey D, Maiffredy L, Vannes A B. Laser shock on a TRIP alloy: mechanical and metallurgical consequences[J]. Journal of Materials Science, 1992, 27(8): 2110-2116.

徐国建, 钟立明, 王虹, 傅新皓, 王志一, 沓名宗春. 激光冲击强化铝合金焊接接头的性能[J]. 中国激光, 2014, 41(6): 0603007. Xu Guojian, Zhong Liming, Wang Hong, Fu Xinhao, Wang Zhiyi, Muneharu Kutsuna. Performance of Aluminum Alloy Welded Joints by Laser Shock Processing[J]. Chinese Journal of Lasers, 2014, 41(6): 0603007.

激光冲击强化铝合金焊接接头的性能

关于本站 Cookie 的使用提示

全站搜索

激光冲击强化铝合金焊接接头的性能

相关论文

相关资讯

关于本站 Cookie 的使用提示

全站搜索