A 0.1 mol.% CoF2-doped Na5Lu9F32 single crystal with high quality in the size of ～10mm×100mm was grown by the Bridgman method. Three peaks located at 504, 544, and 688 nm and a broad band in the range of 1200–1600nm centered at 1472 nm were observed in the absorption spectra. The absorption peak position suggests cobalt ions in the divalent state in the grown crystal. Moreover, the cobalt ions are confirmed to locate in the distorted cubic crystal structure. Upon excitation of 500 nm light, a sharp emission peak at 747 nm ascribed to the T22(H1)→4A2(F) transition was observed for the crystal. The Co2+-doped Na5Lu9F32 crystal shows a potentially promising material for the application of a passively Q-switched laser operating in the near-infrared range.
Rare earth ions and transition metal ions are known as two mainly luminous centers[1,2]. Unlike rare earth ions, transition metal ions show broad luminescence characteristics due to the exposure of outer orbital to the crystal field. Interest in crystals doped with transition metal ions is related to their potential application in the design of tunable solid-state lasers[3,4]. The reported laser operation in a -doped single crystal leads to intense research efforts to explore new crystals containing transition metal ions[5]. Cobalt (Co) with two valence states (, ) is well recognized as an important transitional active luminescent ion and is a luminescent center for solid materials capable of producing visible (VIS) and infrared fluorescence emission[6,7]. Materials doped with ions are used for tunable laser applications[8] in the VIS and near-infrared (NIR) regions due to their intense and broad luminescence. Recently, passive -switch material operating in the NIR eye-safe spectral range gains particular interest, as it can be employed in the fabrication of a compact and low-cost laser generating nanosecond pulses for various applications. A ion exhibiting a broad absorption band in the range of when doped into different host materials makes -doped materials promising candidates for passive -switched lasers, for instance, -doped yttrium aluminum garnet (), -doped yttrium scandium gallium garnet (), and transparent glass-ceramics[9,10].
Glass, glass-ceramic, and single crystals are the main solid hosts for active transition metal ions. Single crystals display superior optical performance and physical–chemical properties in general. A single crystal with a rigid cyclic symmetric structure shows higher luminous efficiency when doped with transition metal ions compared to glass hosts. Meanwhile, glass-ceramics tend to exhibit lower transmission that is ascribed to the scattering of nanoparticles inside. Moreover, many single crystals are thermally, mechanically, and chemically stable.
Very recently, rare-earth-doped single crystals as promising laser and up-conversion materials have received enormous research attention[11,12]. The excellent properties, such as broad range transparency and low minimum phonon energy, make crystal a potential solid-state luminous material for wide band tunable laser applications. Moreover, the comparable ion radius between (74 pm) and (85 pm) opens the possibility of the substitution of ions by the ion.
In this work, we report the growth of a Co-ion-doped single crystal by the Bridgman method. Our result suggests that the Co ion in the single crystal is in a divalent state. The spectroscopic properties of the grown crystal were investigated by absorption and emission spectra measurements. We also discussed the possible crystal sites for ions from the structure of the single crystal and measured spectra.
A single crystal of Co-doped (99.99% purity) was grown by an improved Bridgman technique. The crystal was grown from 99.99% pure raw materials of NaF, , and . The molar composition of the mixed ingredients was . The mixture of the weighted raw materials was thoroughly ground in a mortar for about 0.5 h. Following that, the mixture was heated by the ventilation of anhydrous HF at for to completely remove the residual moisture. A seed of pure single crystal with the <001> direction was placed at the bottom of the homemade platinum (Pt) crucible with a cylinder shape before loading the prepared mixture into the crucible. The crucible was sealed completely to avoid contamination from water and oxygen in the air and to prevent the volatilization of the melt during crystal growth. The detailed growing process by the Bridgman approach has been reported[13].
The crystal was obtained by removing the Pt crucibles, and the obtained crystal was transparent with a purple color. The crystal grown by the Bridgman approach was about 100 mm in length and 10 mm in diameter, as shown in Fig. 1(a). The opaque part a few centimeters long at the top of the crystal could be the excess NaF in the starting material. The crystal was cut into slices with a thickness of 2 mm along the growth direction for optical characterizations and polished.
Fig. 1. (a) Photograph of -doped single crystal. Left: the boule of the crystal; right: polished slice. (b) XRD pattern of the . (c) Standard line pattern of the (No. 27-0725).
The X-ray diffraction (XRD) measurements to identify the phase composition of the crystal were recorded by a Bruker D8 Advance (Germany). The XRD data were collected within range of at a scan speed of . The absorption spectra measurements for the samples were measured by a Cary 5000 UV/VIS/NIR spectrophotometer (Agilent Co. America). Emission spectra and excitation spectra of the samples were recorded by an F-4500 spectrophotometer (Hitachi High-Technologies Co., Tokyo, Japan). All of the measurements were performed at room temperature and in atmospheric conditions.
Figure 1(b) shows the XRD pattern of the as-grown single crystal, and Fig. 1(c) shows a standard card of . It is obvious that the diffraction peaks of the as-grown crystal match perfectly with those of the standard (JCPDS card No. 27-0725), and no diffraction peaks due to other crystalline phases were detected, indicating that they have the same crystal structure. It implies that the introduction of a small amount of Co ions did not transform the phase structure of the matrix crystals. The lattice parameters of the as-grown cubic crystals could be calculated according to the XRD pattern data as follows: .
Figure 2(a) displays the absorption spectra of the Co-ion-doped and undoped crystals in the wavelength range from 300 to 1800 nm, measured at room temperature. Figure 2(b) is an enlarged absorption spectrum of Co-doped crystal in the range of 400 to 800 nm. Three absorption peaks at 504, 544, and 688 nm in the VIS range and a broad absorption band centered at 1472 nm from the wavelength of 1200 to 1600 nm can be observed in Fig. 2(a). Meanwhile, no characteristic absorption peaks of Co ions were observed for the undoped crystal sample. The transmittance of the undoped polished slice with 2 mm thickness in the VIS range was about 89%.
Fig. 2. (a) Absorption spectra of Co doped single crystals. (b) Enlarged absorption spectra from 400 to 800 nm.
It was also found that the absorption intensities increase gradually from the lower part of the crystal, corresponding to the initial growing stage to the upper part of the final growing stage. Considering that the thickness of the sample is identical, the increase of absorption indicates more Co ions were doped into the crystal on the initial growth stage. The observation of color in Fig. 1(a) is consistent with this assumption, where the single crystal becomes purpler in the lower part. Hence, the effective segregation coefficient of Co ions in is smaller than 1.
The Co ion has two stable valence states of and in different hosts. and are both possible when Co ions are doped into the crystal. The valence of the Co ion is dependent on the coordination environment it locates[14]. The investigation of the absorption features for the and ions indicates Co ions in the trivalent state show two distinct absorption peaks centered at 714 and 435 nm, respectively[15,16].
No observation of such peaks can be found in the absorption spectra in this work (Fig. 2). Hence, one may ascribe the measured absorption peaks to ions. Additionally, the entire process of crystal growth was accomplished in a closed environment, which is helpful for Co ions to form [17]. Moreover, the 504, 544, 688, and 1472 nm bands in Fig. 2 can be attributed to , , , and transitions, respectively, which are very similar to the absorption characteristics of in other hosts[18]. This experimental result suggests the Co ion in the crystal is in a divalent state.
Co cations can substitute and crystal sites when doped into the crystal. To clearly illustrate the crystal site of the Co ion, the schematic of the cell structure of cubic single crystal is displayed in Fig. 3, inferred from Ref. [19]. The compound in the microscopic condition has a cubic cell with the unit cell parameter (space group Fm3m).
Fig. 3. Schematic cell structure of cubic single crystal.
Figure 3 suggests and have a similar structure. The blue balls located at the centers of eight small cubes represent ions, while the green and red balls located at the surface and vertex of the crystal cell are and ions, respectively. The probability of and ions occupying the surface of the crystal cell is and , respectively, while the possibility for a vertex is and , respectively. The coordination number for both and is eight surrounded by ions. ions located at the surface and vertex can have different crystal fields regardless if it possesses the same coordination number. Substitution is more likely to occur if the cation has a similar radius and valence to Co ions. The radii for , , , , and are 97.7, 118, 90, 54.5, and 131 pm, respectively. It is evident that the size of is the nearest to that of , suggesting that the possible crystal site for substitution is a ion. The coordination number of the cation in the ionic crystal structure is determined by the ratio of the radius between the positive ion and negative ion[20]. The ratio in the range of is suitable to form a stable cubic crystal structure. The ionic ratio between and is 0.687 in the single crystal, which slightly deviates from the recommended range. When the Co ion replaces the Lu sites, the mismatch in charge and ion radius can lead to a distorted cubic shape, resulting in miraculous transformations in the absorption spectra. It may also explain the obtained crystal in a purple color instead of the commonly observed pink.
The crystal field theory mainly discusses the energy level splitting of the orbit of the transition elements under the influence of the electric field arising from the ligand charge and the effect on the crystal structure and properties. Numerous research efforts have been devoted to investigating the lattice parameters of -doped octahedral and tetrahedral crystals centered at an oxygen ion[2123" target="_self" style="display: inline;">–23]. However, studies focused on the lattice parameters of the ion in the coordination center of ions are limited. Moreover, there is even less research on the parameters of the lattice field in the cubic structure, in which is doped into the coordination center with eight ions.
The parameter of the octahedral crystal field and the Racah parameter for a -doped crystal can be calculated by the following equations[24]: where and are the energy difference of the first and third excited states compared to the ground state, respectively. It can be confirmed from Fig. 2 that the absorption peak at 688 nm is attributed to the transition. Hence, can be determined to be . The Fourier transform infrared (FTIR) spectrum from 400 to was measured to determine the value. A weak absorption band at was observed due to the transition. Therefore, the value was estimated to be . The ratio is the same for the in lattices as for the free ion (). By solving Eqs. (1) and (2), the crystal field and Racah parameters were obtained: , and . The ratio between and is equal to , which indicates the -doped crystal belongs to the weak field site crystal. The similarity of the lattice field intensity for the -doped and is another indication of comparable structure for these crystals. Parameters of , , and of some other -doped crystals are listed in Table 1.
Table 1. Dq, B, Dq/B Parameters of Co2+-doped Crystals
Figure 4 illustrates the excitation spectra of Co-doped monitored at the wavelength of 750 nm. An excitation peak centered at 507 nm implies that the sample can be excited most efficiently by the excitation light at the 507 nm wavelength.
Figure 5 shows the photoluminescence intensity of the crystal excited at 500 nm. An emission peak due to the transition in the range of 728 to 770 nm is observed. The direct exposure of the orbital to the crystal field makes Co ions sensitive to the surrounding environment. Strong coupling between photons and electrons is expected under excitation, which can lead to the broadening of emission and absorption spectra[25].
Fig. 5. Emission spectra of crystal excited by 500 nm light.
A Co–ion-doped single crystal was prepared by the Bridgman method under suitable growth conditions. The Co ions in the divalent state are confirmed to locate in the distorted cubic crystal structure surrounded by eight ions. The estimation of the lattice field parameter and Racah parameter validates that the single crystal belongs to the weak field site crystal. The excellent spectroscopic properties suggest that the grown crystal may be a potential passive -switch material in the NIR range.
Lizhi Fang, Jianxu Hu, Haiping Xia, Jianli Zhang, Yongsheng Zhu, Baojiu Chen. Investigation of the growth and optical properties of a Co2+-doped Na5Lu9F32 single crystal[J]. Chinese Optics Letters, 2018, 16(6): 061601.