高功率CO<sub>2</sub>激光钎焊金刚石颗粒

杨卫红; 唐霞辉; 秦应雄; 刘天明; 阮海洪

中国激光, 2007, 34 (4): 569, 网络出版: 2007-04-25

高功率CO₂激光钎焊金刚石颗粒

High Power CO₂Laser Brazing of Diamond Grits

论文大纲

杨卫红 ^*唐霞辉秦应雄刘天明阮海洪

作者单位

华中科技大学光电子科学与工程学院, 湖北武汉 430074

激光技术高功率CO2激光激光钎焊金刚石颗粒结合机制热损伤 laser technique high power CO2 laser laser brazing diamond grits combination mechanism thermal damage

摘要

采用高功率横流CO2激光扫描钎料合金与金刚石颗粒。研究了激光工艺参数对钎焊层结合性能及金刚石热损伤的影响,分析了钎焊层与金刚石结合机制及金刚石颗粒在激光作用下的热损伤机制。研究结果表明,激光功率和扫描速度是影响金刚石热损伤及表面浸润的主要因素。在氩气保护下,粉末厚度为0.5 mm,激光光斑直径3 mm,功率为800 W,扫描速度为8.39 mm/s时,可获得金刚石颗粒、钎料合金、金属基体三者具有最佳结合性能的钎焊层。合金粉末对金刚石颗粒浸润良好,并发生冶金化学反应,生成TiC和SiC。当激光输入能量太高时,金刚石颗粒开始与外界的氧发生氧化反应,在自由能方程中的气体分压下,金刚石一直氧化,直到与氧化物处于平衡状态。这一过程表现为金刚石颗粒石墨化,逐步氧化烧损变成气体。

Abstract

High power transverse flow CO2 laser was used to scan the brazing alloy and diamond grits. The influence of laser technological parameters on brazing layer combination performance and diamond grits thermal damage was researched, and the thermal damage mechanism of laser brazed diamond and the combination mechanism of brazing layer and diamond grits were analyzed. The research results showed that laser power and scanning speed were the main factors for diamond thermal damage and surface wetting. On the conditions of 0.5 mm brazing layer thickness, argon shield, 800 W laser power, and 8.39 mm/s scanning speed, the best combination performance among the diamond grits, brazing alloy and metallic base can be achieved. Brazing alloy wetted the diamond grits well and reacted with them to form TiC and SiC. Under high laser energy input, oxidation take placed between diamond grits and oxygen outside, diamond would be oxidized all along on the condition of branch gas pressure about free equation until the balance established between diamond and oxide, during this process, diamond grits would be carbonized or burn out and gasified.

参考文献

[1] . . Experimental research of brazing monolayer diamond grinding wheel[J]. China Mechanical Engineering, 2001, 12(12): 1423-1424.

[2] . Trenker, H. Seidemann. High-vacuum brazing of diamond tools[J]. Industrial Diamond Review, 2002, 62(592): 49-52.

[3] . A. Khalid, U. E. Klotz, H.-R. Elsener et al.. On the interfacial nanostructure of brazed diamond grits[J]. Scripta Materialia, 2004, 50(8): 1139-1143.

[4] Huang Hui, Zhu Huoming, Xu Ximing. Diamond grain brazing in air [J]. Welding & Joining, 2004, (1):35～36
黄辉,朱火明,徐西明. 空气中钎焊金刚石磨粒[J]. 焊接, 2004, (1):35～36

[5] Guan Yancong,Chen Yuquan, Yao Deming. Research of the soldering and brazing process for diamond abrasive slices [J]. Machinery Manufacturing Engineer, 2005, (6):51～52
关砚聪,陈玉全,姚德明. 钎焊金刚石磨料片工艺的研究[J]. 现代制造工程, 2005, (6):51～52

[6] Chen Hongxin, Jia Tianqing, Huang Min et al.. Visible-infrared femtosecond laser-induced optical breakdown of 6H SiC [J]. Acta Optica Sinica, 2006, 26(3):467～470
陈洪新,贾天卿,黄敏等. 飞秒激光的波长对SiC材料烧蚀的影响[J]. 光学学报, 2006, 26(3):467～470

[7] Zheng Qiguang, Tao Xingzhi, Yang Yang et al.. Study on laser deep penetration welding of metallic materials [J]. Chinese J. Lasers, 1991, A18(2):123～124
郑启光,陶星芝,杨杨等. 高功率CO2激光深穿透焊接的研究[J]. 中国激光, 1991, A18(2):123～124

[8] . . Action of carbide former in base materials for diamond tool with Cabalt matrix[J]. Journal of Synthetic Crystal, 1993, 22(1): 73-78.

[9] Yanbin Chen, Zhenglong Lei, Lin Wu et al.. Influence of shielding gas pressure on welding characteristics in CO2 laser-MIG hybrid welding process [J]. Chin. Opt. Lett., 2006, 4(1):33～35

[10] Li Lijun, Jin Xiangzhong, Hong Lei. Laser welding of diamond saw blades [J]. Applied Laser, 1997, 17(5):5～6
李力钧,金湘中,洪蕾. 金刚石圆锯片的激光焊接[J]. 应用激光, 1997, 17(5):5～6

杨卫红, 唐霞辉, 秦应雄, 刘天明, 阮海洪. 高功率CO₂激光钎焊金刚石颗粒[J]. 中国激光, 2007, 34(4): 569. 杨卫红, 唐霞辉, 秦应雄, 刘天明, 阮海洪. High Power CO₂Laser Brazing of Diamond Grits[J]. Chinese Journal of Lasers, 2007, 34(4): 569.

高功率CO₂激光钎焊金刚石颗粒

关于本站 Cookie 的使用提示

全站搜索

高功率CO2激光钎焊金刚石颗粒

相关论文

相关资讯

关于本站 Cookie 的使用提示

全站搜索

高功率CO₂激光钎焊金刚石颗粒