中国激光, 2019, 46 (5): 0501003, 网络出版: 2019-11-11
1064 nm激光和355 nm激光同时辐照DKDP晶体的耦合预处理效应 下载: 893次
Coupling Conditioning Effect of DKDP Crystals Under Simultaneous Irradiation by 1064 nm laser and 355 nm Laser
图 & 表
图 2. R-on-1激光损伤概率曲线。(a) 1ω ;(b) 3ω 和不同定值能量密度的1ω
Fig. 2. R-on-1 laser damage probability curves. (a) 1ω ; (b) 3ω and 1ω with different fixed fluences
图 3. 损伤针点的典型散射图像(晶体厚度为10 mm)。(a)能量密度为105.3 J/cm2的1ω ;(b)能量密度为30.9 J/cm2的3ω ;(c)能量密度为34.1 J/cm2的3ω 和能量密度为12.3 J/cm2的1ω ;(d)能量密度为34.1 J/cm2的3ω 和能量密度为29.4 J/cm2的1ω
Fig. 3. Typical scatter images of damage pinpoint (crystal thickness of 10 mm). (a) 1ω at energy density of 105.3 J/cm2; (b) 3ω at energy density of 30.9 J/cm2; (c) 3ω at energy density of 34.1 J/cm2 and 1ω at energy density of 12.3 J/cm2; (d) 3ω at energy density of 34.1 J/cm2 and 1ω at energy density of 29.4 J/cm2
吴金明, 赵元安, 汪琳, 彭小聪, 杨留江, 单翀, 邵建达. 1064 nm激光和355 nm激光同时辐照DKDP晶体的耦合预处理效应[J]. 中国激光, 2019, 46(5): 0501003. Jinming Wu, Yuan'an Zhao, Lin Wang, Xiaocong Peng, Liujiang Yang, Chong Shan, Jianda Shao. Coupling Conditioning Effect of DKDP Crystals Under Simultaneous Irradiation by 1064 nm laser and 355 nm Laser[J]. Chinese Journal of Lasers, 2019, 46(5): 0501003.