发光学报, 2016, 37 (1): 22, 网络出版: 2016-03-22
乙醇对纳米多孔氧化铝薄膜热释光的影响
Effect of Ethanol on Thermoluminescence of Nanoporous Alumina Films
二次阳极氧化法 乙醇 Al2O3: C薄膜 热释光 two-step anodization ethanol carbon-doped nanoporous alumina films thermoluminescence
摘要
以乙醇-草酸混合溶液为电解液, 用二次阳极氧化法制备纳米多孔Al2O3: C薄膜。 在制备过程中, 碳的掺杂浓度可控。实验结果表明, 随着碳浓度的增加, 热释光强度逐渐增大; 随着退火温度的升高, 320 ℃左右的主热释光峰的强度先升高后降低。在退火温度为500 ℃时, 主热释光峰的强度达到最大。纯草酸溶液制备的Al2O3薄膜的热释光剂量响应曲线在10~50 Gy是线性的, 在50~100 Gy呈超线性; 而乙醇-草酸混合溶液制备的Al2O3: C薄膜在10~100 Gy基本呈线性。
Abstract
The carbon-doped nanoporous alumina films were prepared by two-step anodic oxidation in ethanol-oxalic acid mixture. This kind of doping method can effectively control the doping concentration of carbon. The thermoluminescence (TL) measurements show that the TL intensity of the films prepared in ethanol-oxalic acid mixture has been significantly improved comparing with the film prepared in oxalic acid, and the TL intensity increases with the carbon concentration. The TL intensity at 320 ℃ first increases then decreases with the elevated annealing temperature and reaches a maximum value at 500 ℃. The films prepared in oxalic acid show a linear dose response in the dose range of 10-50 Gy and a superlinear dose response in the range of 50-100 Gy, while the films prepared in ethanol-oxalic acid mixture show a linear dose response in the range of 10-100 Gy.
窦巧娅, 王倩, 邓保霞, 吴丽, 吉旭. 乙醇对纳米多孔氧化铝薄膜热释光的影响[J]. 发光学报, 2016, 37(1): 22. DOU Qiao-ya, WANG Qian, DENG Bao-xia, WU Li, JI Xu. Effect of Ethanol on Thermoluminescence of Nanoporous Alumina Films[J]. Chinese Journal of Luminescence, 2016, 37(1): 22.