发光学报, 2018, 39 (5): 643, 网络出版: 2018-06-29   

Si,Lu掺杂Ca0.8Zn0.2TiO3∶Pr3+荧光粉的光学性能改善

Improved Luminescence Properties of Ca0.8Zn0.2TiO3∶Pr3+ Phosphors Doped with Si and Lu
作者单位
湖南师范大学化学化工学院 资源精细化与先进材料湖南省高校重点实验室, 湖南 长沙 410081
摘要
采用高温固相法合成Ca0.8Zn0.2TiO3∶0.2%Pr3+,Si4+和Ca0.8Zn0.2TiO3∶0.2%Pr3+,Si4+,Lu3+荧光粉。通过X射线衍射仪、电子顺磁共振光谱仪、显微拉曼光谱仪和荧光光谱仪等表征了该系列荧光粉的物相组成、微观结构和发光性质。结果表明, 以β-Si3N4为硅源制备的荧光粉具有最佳的光学性能。加入ZnO后, 荧光粉由CaTiO3、Zn2TiO4和Ca2Zn4Ti16O38三相组成, 其中CaTiO3为主相。电子顺磁共振谱证实了Pr4+存在, Lu3+的添加使[Pr4+Ti3+O3]+簇显著增加, 电子顺磁共振谱和拉曼光谱均证实Si4+、Lu3+的掺杂使局部TiO6簇对称性提高, 有利于Pr3+发光中心的能量传递。在336 nm激发下, 荧光粉展示了很强的位于612 nm的红光发射(归属于Pr3+的 1D2 →3H4跃迁)及理想的红光色坐标(x=0.670, y=0.330)。Si4+和Lu3+的添加显著增强了370 nm激发下红光发射, Ca0.8Zn0.2TiO3∶0.2%Pr3+,3.2%Si4+荧光粉的余辉寿命最长。
Abstract
Ca0.8Zn0.2TiO3∶0.2%Pr3+,Si4+ and Ca0.8Zn0.2TiO3∶0.2%Pr3+,Si4+,Lu3+ phosphors were synthesized by high temperature solid-state method. Crystalline phase, microstructure and luminescence properties of phosphors were characterized with X-ray diffractometer (XRD), electron paramagnetic resonance spectrometer (EPR), microscopic Raman spectrometer and photoluminescence spectrometer, respectively. The results show that phosphor prepared using β-Si3N4 as Si source has the optimal luminescence properties. Phosphors with the addition of ZnO were confirmed to be constituted of CaTiO3, Zn2TiO4 and Ca2Zn4Ti16O38, and CaTiO3 is major phase. EPR spectra confirm that the presence of Pr4+ and [Pr4+Ti3+O3]+ clusters remarkably increase with the Lu3+ addition. Increasing local symmetry of TiO6 clusters with the addition of Si4+ and Lu3+ is verified by EPR and Raman spectra, which is beneficial for the energy transfer of luminescent center Pr3+. The obtained phosphor exhibited the intense red emission centered at 612 nm (originated from 1D2→3H4 transition of Pr3+) with an ideal chromaticity coordinate located at (x= 0.670, y=0.330) under 336 nm excitation. Red emission excited by 370 nm remarkably increases with the addition of Si4+ and Lu3+. The synthetic Ca0.8Zn0.2TiO3∶0.2%Pr3+,3.2%Si4+ phosphor has the longest average lifetime.
参考文献

[1] YAMAMOTO H, MATSUZAWA T. Mechanism of long phosphorescence of SrAl2O4∶Eu2+, Dy3+ and CaAl2O4∶Eu2+, Nd3+ [J]. J. Lumin., 1997, 72:287-289.

[2] ZHANG C, DENG C Y. Improved preparation technology of color-tunable long afterglow phosphors Sr1.94-xCaxMgSi2O7∶Eu2+0.01, Dy3+0.05 [J]. J. Lumin., 2017, 192:310-315.

[3] 崔彩娥, 雷星, 黄平, 等. EDTA络合溶胶-凝胶法制备 Y2O2S∶Eu3+,Mg2+,Ti4+红色长余辉材料 [J]. 发光学报, 2013, 34(4):416-420.

    CUI C E, LEI X, HUANG P, et al.. Synthesis of red long lasting phosphors Y2O2S∶Eu3+, Mg2+, Ti4+ by EDTA complexing sol-gel method [J]. Chin. J. Lumin., 2013, 34(4):416-420. (in Chinese)

[4] 王磊, 董杰, 黄平, 等. 碱土金属离子对红色长余辉材料Y2O2S∶Eu3+, M2+(M=Mg,Ca,Sr,Ba),Ti4+纳米阵列发光性能的影响 [J]. 发光学报, 2014, 35(5):553-557.

    WANG L, DONG J, HUANG P, et al.. Influence of alkaline-earth metal ions on the luminescence properties of Y2O2S∶Eu3+, M2+ (M=Mg, Ca, Sr, Ba), Ti4+ nanotube arrays [J]. Chin. J. Lumin., 2014, 35(5):553-557. (in Chinese)

[5] KOJIMA Y, TAKAHASHI A, UMEGAKI T. Synthesis of orange-red-emitting Eu2+, Pr3+ codoped SrS long afterglow phosphor [J]. J. Lumin., 2014, 146(1):42-45.

[6] DIALLO P T, BOUTINAUD P, MAHIOU R, et al.. Red luminescence Pr3+ -doped calcium titanates [J]. Phys. Stat. Sol.(a), 1997, 160:255-263.

[7] VIDYADHARAN V, MOHAN R, JOSEPH C, et al.. Luminescent characteristic of UV excited Sr0.5Ca0.5TiO3∶Pr3+ reddish-orange phosphor [J]. Mater. Chem. Phys., 2016, 170(1):38-43.

[8] SUN H Q, ZHANG Q W, WANG X H, et al.. Strong red emission in Pr3+-doped (K0.5Na0.5)NbO3-CaTiO3 diphase ceramics [J]. J. Am. Ceram. Soc., 2014, 98(2):601-606.

[9] TANG J, YU X, YANG L, et al.. Preparation and Al3+ enhanced photoluminescence properties of CaTiO3∶Pr3+ [J]. Mater. Lett., 2006, 60(3):326-329.

[10] NOTO L L, PITALE S S, GUSOWKI M A, et al.. Afterglow enhancement with In3+ codoping in CaTiO3∶Pr3+ red phosphor [J]. Powder Tech., 2013, 237:141-146.

[11] MAR B, SINGH K C, CEMBRERO-COCA P, et al.. Red emitting MTiO3(M=Ca or Sr) phosphors doped with Eu3+ or Pr3+ with some cations as co-dopants [J]. Displays, 2013, 34:346-351.

[12] ZHANG X, ZHANG J, ZHANG X, et al.. Enhancement of the red emission in CaTiO3∶Pr3+ by addition of rare earth oxides [J]. Chem. Phys. Lett., 2007, 434:237-240.

[13] ZHANG J C, WANG X, YAO X. Enhancement of luminescence and afterglow in CaTiO3∶Pr3+ by Zr substitution for Ti [J]. J. Alloys Compd., 2010, 498(2):152-156.

[14] HOLLIDAY K S, KOHLGRUBER T A, TRAN I C, et al.. Increased fluroescence intensity in CaTiO3∶Pr3+ phosphor due to NH3 treatment and Nb co-doping [J].Opt. Mater., 2016, 60:359-365.

[15] YANG P, TAI B, WU W, et al.. Tailoring lanthanide doping in perovskite CaTiO3 for luminescence applications [J]. Phys. Chem. Chem. Phys., 2017, 19(24):16189-16197.

[16] ROYCE M R, MATSUDA S, TAMAKI H, et al.. Red emitting long decay phosphors: US, 5650094 [P]. 1997-07-22.

[17] LIAN S X, ZUO C G, YIN D L, et al.. Preparation and characterization of red luminescent Ca0.8Zn0.2TiO3∶Pr3+, Na+ nanophosphor [J]. J. Chin. Rare Earth Soc., 2006, 24(2):158-162.

[18] YU L P, XIA M, CHEN X, et al.. Improvement of luminescence properties of Ca0.8Zn0.2TiO3∶Pr3+ prepared by hydrothermal method [J]. J. Mater. Res., 2013, 28(18):2590-2597.

[19] ZHANG X, ZHANG J, REN X, et al.. The dependence of persistent phosphorescence on annealing temperatures in CaTiO3∶Pr3+ nanoparticles prepared by a coprecipitation technique [J]. J. Sol. State Chem., 2008, 181(3):393-398.

[20] DONG G P, XIAO X D, ZHANG L L, et al.. Preparation and optical properties of red, green and blue afterglow electrospun nanofibers [J]. J. Mater. Chem., 2011, 21(7):2194.

[21] CABELLO G, LILLO L, CARO C, et al.. Synthesis, characterization and optical properties of ATiO3-Pr thin films prepared by a photochemical method (where A= Ba and Ca) [J]. Mater. Res. Bull., 2015, 70:32-39.

[22] CHEN R, CHEN D H. Enhanced luminescence properties of CaTiO3∶Pr3+ phosphor with addition of SiO2 by solid-state reaction [J]. Spectrochim. Acta Part A: Mol. Biomol. Spectrosc., 2014, 127:256-260.

[23] 邾强强, 杨力勋, 季巍巍, 等. Si-N共掺对CaAl2O4∶Eu2+和CaAl2O4∶Eu2+,Sm3+荧光粉荧光和余辉性能的优化 [J]. 中国稀土学报, 2013, 31(1):44-48.

    ZHU Q Q, YANG L X, JI W W, et al.. Optimization on photoluminescence and afterglow performance of CaAl2O4∶Eu2+ and CaAl2O4∶Eu2+, Sm3+ phosphors with Si-N Co-doping [J]. J. Chin. Rare Earth Soc., 2013, 31(1):44-48. (in Chinese)

[24] ABRAGAM A, BLEANEY B. Electron Paramagnetic Resonance of Transition Ions [M]. London: Oxford University Press, 1970.

[25] BOUTINAUD P, PINEL E, DUBOIS A P, et al.. UV-to-red relaxation pathways in CaTiO3∶Pr3+ [J]. J. Lumin., 2005, 111(1-2):69-80.

[26] RIBEIRO G K, VICENTE F S, BERNARDI M I B, et al.. Short-range structure and photoluminescent properties of the CaTiO3∶Pr, La phosphor [J]. J. Alloys Compd., 2016, 688:497-503.

[27] GONALVES R F, LIMA A R F, GODINHO M J, et al.. Synthesis of Pr3+-doped CaTiO3 using polymeric precursor and microwave-assisted hydrothermal methods: a comparative study [J]. Ceram. Inter., 2015, 41:12841-12848.

[28] OLIVEIRA L H, SAVIOLI J, MOURA A P, et al.. Investigation of structural and optical properties of CaTiO3 powders doped with Mg2+ and Eu3+ ions [J]. J. Alloys Compd., 2015, 647:265-275.

[29] ZHENG H, BAGSHAW H, DE GYRGYFALVA G D C C, et al.. Raman spectroscopy and microwave properties of CaTiO3-based ceramics [J]. J. Appl. Phys., 2003, 94(5):2948-2956.

[30] WANG Z W, SAXENA S K, ZHA C S. In situ X-ray diffraction and Raman spectroscopy of pressure-induced phase transformation in spinel Zn2TiO4[J]. Phys. Rev., 2002, 66:024103.

[31] WANG Z W, LAZOR P, SAXENA S K, et al.. High-pressure raman spectroscopyic study of spinel (ZnCr2O4) [J]. J. Solid State Chem., 2002, 165:165-170.

[32] ZHAO X K, FENDLER J H. Size quantization in semiconductor particulate films [J]. J. Phys. Chem., 1991, 95(9):3716-3723.

[33] DEN EECKHOUT K V, SMET P F, POLEMAN D. Persistent luminescence in Eu2+-doped compounds: a review [J]. Materials, 2010, 3:2536-2566.

[34] SAKAI R, KATSUMATA T, KOMURO S, et al.. Effect of composition on the phosphorescence from BaAl2O4∶Eu2+, Dy3+ crystals [J]. J. Lumin., 1999, 85:149-154.

李金银, 彭志雄, 余丽萍, 张吉林, 周文理, 邱忠贤, 李承志, 廉世勋. Si,Lu掺杂Ca0.8Zn0.2TiO3∶Pr3+荧光粉的光学性能改善[J]. 发光学报, 2018, 39(5): 643. LI Jin-yin, PENG Zhi-xiong, YU Li-ping, ZHANG Ji-lin, ZHOU Wen-li, QIU Zhong-xian, LI Cheng-zhi, LIAN Shi-xun. Improved Luminescence Properties of Ca0.8Zn0.2TiO3∶Pr3+ Phosphors Doped with Si and Lu[J]. Chinese Journal of Luminescence, 2018, 39(5): 643.

本文已被 1 篇论文引用
被引统计数据来源于中国光学期刊网
引用该论文: TXT   |   EndNote

相关论文

加载中...

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!