高温合金/不锈钢异种材料T型接头激光穿透焊工艺研究

冯威琦; 张云丰; 陶汪; 李俐群

doi:doi:10.3788/cjl201239.1003003

中国激光, 2012, 39 (10): 1003003, 网络出版: 2012-09-10

高温合金/不锈钢异种材料T型接头激光穿透焊工艺研究

Dissimilar Metals Combination of Superalloy/Stainless Steel in T-Shape by Laser Penetration Welding

论文大纲

冯威琦 ^*张云丰陶汪李俐群

作者单位

哈尔滨工业大学先进焊接与连接国家重点实验室，黑龙江哈尔滨 150001

激光技术高温合金不锈钢激光穿透焊裂纹 laser technique superalloy stainless steel laser penetration welding crack

摘要

针对飞行器发动机水冷壁结构，进行了GH3128/06Cr19Ni10异种材料T型接头激光穿透焊试验，主要研究了焊接参数对焊缝成形和焊接裂纹的影响规律，分析了焊接裂纹形成原因，得到了较合理的焊接工艺区间。结果表明，对于GH3128/06Cr19Ni10异种材料T型接头激光穿透焊，连续焊比脉冲焊更易实现稳定焊接，获得良好焊缝成形。焊接裂纹是接头主要缺陷裂纹都在高温合金一侧产生，控制激光功率、保证对中可降低裂纹产生概率。焊接接头的另一种缺陷是表面下塌，保证间隙小于0.2 mm可抑制下塌缺陷的产生。对由41条焊缝组成的模拟件进行了10 MPa，5 min水压测试，每条焊缝都满足要求。

Abstract

GH3128 and 06Cr19Ni10 which are mainly used in water wall of flight vehicle engine are joined together by laser penetration welding. The relationships between welding parameters and welding appearance and cracks are mainly researched. The reason of weld cracks is analyzed. A appropriate welding craft is summarized. The following conclusions are obtained. The continuous laser welding is better than pulse laser welding in terms of welding appearance and welding process stability. If the gap between the two metals is too big, the surface of the welding seam will collapse. The GH3128 plate may crack if the laser power is too high, or if the laser beam deviate from the centre. The welded specimen which contains 41 weld seams preform well at the hydrostatic test (10 MPa, 5 min).

参考文献

[1] 傅宏镇, 陈玉平, 魏育环等. 碳、钨、钼和铁对GH128合金显微组织和性能的影响［J］. 钢铁研究总院学报, 1985, 5(1): 75～82

Fu Hongzhen, Chen Yuping, Wei Yuhuan et al.. Influence of C, W, Mo and Fe on the microstructure and properties of alloy GH128［J］. CISRI Journal, 1985, 5(1): 75～82

[2] 张海泉, 赵海燕, 张彦华等. 镍基高温合金电子束焊接热影响区微裂纹特征分析［J］. 材料工程, 2005, (3): 22～25

Zhang Haiquan, Zhao Haiyan, Zhang Yanhua et al.. Analysis on the microfissuring behavior in the heat-affected zone of electron-beam welded nickel-based superalloy［J］. Journal of Materials Engineering, 2005, (3): 22～25

[3] 熊建钢, 胡乾午, 吴丰顺等. 镍基高温合金激光焊接接头组织及裂纹形成原因［J］. 应用激光, 2001, 21(5): 309～312

Xiong Jiangang, Hu Qianwu, Wu Fengshun et al.. Microstructure characteristics and weld cracking formation in nickel superalloy laser welded joints［J］. Applied Laser, 2001, 21(5): 309～312

[4] O. A. Idowu, O. A. Ojo, M. C. Chaturvedi. Effect of heat input on heat affected zone cracking in laser welded ATI Allvac 718Plus superalloy［J］. Materials Science and Engineering A, 2007, 454: 389～397

[5] N. L. Richards, R. Nakkalil, M. C. Chaturvedi. The influence of electron-beam welding parameters on heat-affected-zone microfissuring in INCOLOY 903［J］. Metallurgical and Materials Transactions A, 1994, 25(8): 1733～1745

[6] L. O. Osoba, R. K. Sidhu, O. A. Ojo. On preventing HAZ cracking in laser welded DS Rene 80 superalloy［J］. Mater. Sci. Technol., 2011, 27(5): 897～902

[7] O. A. Ojo, N. L. Richards, M. C. Chaturvedi. Contribution of constitutional liquation of gamma prime precipitate to weld HAZ cracking of cast Inconel 738 superalloy［J］. Scripta Material, 2004, 50(5): 641～646

[8] 姜华, 汤海波, 方艳丽等. 激光熔化沉积DZ408镍基高温合金微细柱晶显微组织及性能［J］. 中国激光, 2012, 39(2): 0203004

Jiang Hua, Tang Haibo, Fang Yanli et al.. Microstructure and mechanical properties of rapid solidified ultra-fine columnar grain Ni-base superalloy DZ408 by laser melting deposition manufacturing［J］. Chinese J. Lasers, 2012, 39(2): 0203004

[9] O. A. Ojo, Y. L. Wang, M. C. Chaturvedi. Heat affected zone liquation cracking in electron beam welded third generation nickel base superalloys［J］. Materials Science and Engineering A, 2008, 476(1-2): 217～223

[10] 钟如涛, 熊征. 连续/脉冲CO2激光熔覆高温合金K403［J］. 中国激光, 2010, 37(3): 852～857

Zhong Rutao, Xiong Zheng. Research on continuous/pulse laser cladding superalloy K403［J］. Chinese J. Lasers, 2010, 37(3): 852～857

[11] 龚伟怀, 陈玉华, 吕榛等. 0.2 mm厚GH4169薄片激光微焊接接头的组织性能［J］. 中国激光, 2011, 38(6): 0603008

Gong Weihuai, Chen Yuhua, Lü Zhen et al.. Microstructure and properties of 0.2 mm thick sheet GH4169 by laser microwelding［J］. Chinese J. Lasers, 2011, 38(6): 0603008

[12] R. K. Sidhu, O. A. Ojo, M. C. Chaturvedi. Microstructural analysis of laser-beam-welded directionally solidified INCONEL 738［J］. Metallurgical and Materials Transactions A, 2007, 38(4): 858～870

[13] R. K. Sidhu, O. A. Ojo, M. C. Chaturvedi. Microstructural response of directionally solidified Rene 80 superalloy to gas-tungsten arc welding［J］. Metallurgical and Materials Transactions A, 2009, 40(1): 150～162

[14] O. A. Ojo, M. C. Chaturvedi. On the role of liquated γ′ precipitates in weld heat affected zone microfissuring of a nickel-based superalloy［J］. Materials Science and Engineering A, 2005, 403(1-2): 77～86

[15] R. K. Sidhu, N. L. Richards, M. C. Chaturvedi. Effect of aluminium concentration in filler alloys on HAZ cracking in TIG welded cast Inconel 738LC superalloy［J］. Mater. Sci. Technol., 2005, 21(10): 1119～1131

冯威琦, 张云丰, 陶汪, 李俐群. 高温合金/不锈钢异种材料T型接头激光穿透焊工艺研究[J]. 中国激光, 2012, 39(10): 1003003. Feng Weiqi, Zhang Yunfeng, Tao Wang, Li Liqun. Dissimilar Metals Combination of Superalloy/Stainless Steel in T-Shape by Laser Penetration Welding[J]. Chinese Journal of Lasers, 2012, 39(10): 1003003.

高温合金/不锈钢异种材料T型接头激光穿透焊工艺研究

关于本站 Cookie 的使用提示

全站搜索

高温合金/不锈钢异种材料T型接头激光穿透焊工艺研究

相关论文

相关资讯

关于本站 Cookie 的使用提示

全站搜索