中国激光, 2020, 47 (8): 0802006, 网络出版: 2020-08-17 复制并引用该论文  本文已被引 1 次  被引通知

图 & 表

图 1. AlSi10Mg粉末的粒径分布

Fig. 1. Size distribution of AlSi10Mg powder

下载图片 查看原文

图 2. 不同Sc含量的AlSi10Mg合金的显微组织。(a) 0;(b) 0.1%;(c) 0.2%;(d) 0.3%;(e) 0.4%;(f) 0.5%

Fig. 2. Microstructures of AlSi10Mg alloy with different Sc contents. (a) Mass fraction of Sc is 0; (b) mass fraction of Sc is 0.1%; (c) mass fraction of Sc is 0.2%; (d) mass fraction of Sc is 0.3%; (e) mass fraction of Sc is 0.4%; (f) mass fraction of Sc is 0.5%

下载图片 查看原文

图 3. 不同Sc含量的AlSi10Mg合金的XRD图

Fig. 3. XRD patterns of AlSi10Mg alloy with different Sc contents

下载图片 查看原文

图 4. 不同Sc含量的AlSi10Mg合金的SEM图。(a) 0;(b) 0.1%;(c) 0.2%;(d) 0.3%;(e) 0.4%;(f) 0.5%

Fig. 4. SEM images of AlSi10Mg alloy with different Sc contents. (a) Mass fraction of Sc is 0; (b) mass fraction of Sc is 0.1%; (c) mass fraction of Sc is 0.2%; (d) mass fraction of Sc is 0.3%; (e) mass fraction of Sc is 0.4%; (f) mass fraction of Sc is 0.5%

下载图片 查看原文

图 5. 图4(b)中(AlFeSiSc)相的高倍率图

Fig. 5. High magnification diagram of (AlFeSiSc) phase in Fig. 4(b)

下载图片 查看原文

图 6. 不同Sc含量的AlSi10Mg合金的能谱分析图。(a) 0;(b) 0.3%;(c) 0.4%

Fig. 6. EDS patterns of AlSi10Mg alloy with different Sc contents. (a) Mass fraction of Sc is 0; (b) mass fraction of Sc is 0.3%; (c) mass fraction of Sc is 0.4%

下载图片 查看原文

图 7. Sc含量对AlSi10Mg合金物理性能及力学性能的影响。(a)致密度与显微硬度;(b)压缩应力-应变曲线

Fig. 7. Effects of Sc contents on physical and mechanical properties of AlSi10mg alloy. (a) Densification and micro-hardness; (b) compression stress-strain curves

下载图片 查看原文

图 8. 不同Sc含量的AlSi10Mg合金热处理前后的SEM图。 (a1)~(a6) 0~0.5%,热处理前;(b1)~(b6) 0~0.5%,550 ℃/1 h+180 ℃/8 h;(c1)~(c6) 0~0.5%,550 ℃/1 h+180 ℃/12 h

Fig. 8. SEM images of AlSi10Mg alloy with different Sc contents before and after heat treatment. (a1)--(a6) Mass fraction of Sc is from 0 to 0.5%, before heat treatment; (b1)--(b6) mass fraction of Sc is from 0 to 0.5%, 550 ℃/1 h+180 ℃/8 h; (c1)--(c6) mass fraction of Sc is from 0 to 0.5%, 550 ℃/1 h+180 ℃/12 h

下载图片 查看原文

表 1AlSi10Mg粉末的化学组成

Table1. Chemical composition of AlSi10Mg powder

Element Al Si Mg Fe Cu Mn Other Mass fraction /% Bal. 10.5 0.4 <0.22 <0.013 <0.001 <0.001

查看原文

表 2不同Sc含量AlSi10Mg的压缩性能

Table2. Compressive properties of AlSi10Mg with different Sc contents

Mass fractionof Sc /% Densification /% Micro-hardness /HV Plastic compressionRpc0.2 /MPa Compressive strengthat 25% strain /MPa 0 96.50±0.58 78.9±4.7 117 348 0.1 96.69±0.57 80.3±3.3 122 370 0.2 98.39±0.58 94.2±4.5 144 409 0.3 98.37±0.59 93.4±5.1 131 406 0.4 97.45±0.58 89.8±5.0 130 368 0.5 97.14±0.58 87.1±5.8 128 362

查看原文

张宇杰, 于梅花, 杨瑞霞, 杨维维, 韦景泉, 韦悦周, 李伟洲. 稀土Sc对激光制备AlSi10Mg合金性能的影响[J]. 中国激光, 2020, 47(8): 0802006. Zhang Yujie, Yu Meihua, Yang Ruixia, Yang Weiwei, Wei Jingquan, Wei Yuezhou, Li Weizhou. Effects of Rare Earth Sc on Properties of Laser-Melted AlSi10Mg Alloy[J]. Chinese Journal of Lasers, 2020, 47(8): 0802006.