纳米TiC改性对选区激光熔化铜成形的影响 下载: 905次
Effect of Nano-TiC Modification on Selective Laser Melting of Copper
图 & 表
图 1. 15~53 μm球形铜粉的形貌和粒径分布。(a)形貌;(b)粒径分布
Fig. 1. Morphology and particle size distribution of 15-53 μm spherical copper powder. (a) Morphology; (b) size distribution
图 3. 改性铜粉的形貌和EDS面扫描结果。(a)形貌;(b) EDS面扫描结果
Fig. 3. Morphology and EDS result of nano-TiC modified copper powder. (a) Morphology; (b) EDS result
图 4. 纳米TiC、未改性铜粉和纳米TiC改性铜粉的反射率
Fig. 4. Reflectivity of nano-TiC, copper powder and nano-TiC modified copper powder
图 5. 未改性铜粉与纳米TiC改性铜粉成形试样在腐蚀前的形貌。(a) 未改性铜粉成形试样;(b) 纳米TiC改性铜粉成形试样
Fig. 5. Morphologies of formed samples with copper powder and nano-TiC modified copper powder before corrosion. (a) Formed sample with copper; (b) formed sample with nano-TiC modified copper
黎振华, 申继标, 李淮阳, 滕宝仁, 刘静. 纳米TiC改性对选区激光熔化铜成形的影响[J]. 中国激光, 2021, 48(3): 0315001. Zhenhua Li, Jibiao Shen, Huaiyang Li, Baoren Teng, Jing Liu. Effect of Nano-TiC Modification on Selective Laser Melting of Copper[J]. Chinese Journal of Lasers, 2021, 48(3): 0315001.