铥激光器腔镜用高损伤阈值氧化物薄膜的研制

2 μm波段激光器在环境探测、测风雷达、生物组织切割、光电对抗等领域都有重要的应用价值和前景。而此波段的薄膜通常采用折射率较高的硫化物、砷化物等软膜材料来制备, 为了提升该波段薄膜的损伤性能, 采用折射率相对较低但能带隙更宽的氧化物材料来制备。利用傅里叶红外光谱仪和弱吸收测试仪分析表征了薄膜中OH基含量的多少和薄膜整体吸收的大小, 通过优化工艺, 成功制备出了满足2 020 nm的铥(Tm)激光器使用要求的多层介质薄膜。利用微分干涉显微镜观察了经过激光损伤测试薄膜的损伤形貌, 结合薄膜中电场分布和应力测试结果, 分析探讨了此薄膜的损伤机理, 提出进一步优化薄膜损伤特性的方案。

Abstract

Infrared lasers at 2 μm wavelength have great application value and good prospects in the environmental detection, wind-measuring radar, tissue ablation as well as optoelectronic countermeasure. The films at 2 μm wavelength were often prepared by sulphide, arsenide and other soft material which have high refractive index. In order to promote the damage performance of these films, the oxide material was used whose refractive index was relatively lower but the bandgap was wider to prepare the film. The content of OH and the absorption of the film were characterized by using Fourier infrared spectrometer and the weak absorption tester. By optimizing the fabrication process, the multilayers dielectric thin films which satisfy the requirements of the 2 020 nm Tm laser were successfully prepared. The damage morphologies of the films after the laser damage testing were observed by the differential interference microscope, combining with the electric field distribution and the stress in the film, the damage mechanism of the films were analyzed and further optimization method of damage character was put forward.

参考文献

[1] Singh U N, AByrd J, Wi11iams-Byrda N P, et al. Diode pumped 2-μm solid state lidar transmitter for wind measurements[C]//SPIE, 1997, 3104: 173-178.

[2] Koch G J, Dharamsi A N, Fitzgerald C M, et al. Frequency stabilization of Ho:Tm:YLF laser to absorption lines of carbon dioxide[J]. Applied Optics, 2000, 39(21): 3664-3669.

[3] 刘沛沛, 白杨, 任兆玉, 等. 2 μm光纤激光器的研究进展[J]. 红外与激光工程, 2009, 38(1): 45-49.

Liu Peipei, Bai Yang, Ren Zhaoyu, et al. Research and progress of 2 μm fiber lasers[J]. Infrared and Laser Engineering, 2009, 38(1): 45-49. (in Chinese)

[4] 张秀荣, 范瑞英, 吴光照, 等. 波长为2.94 μm激光束对腔膜的损伤[J]. 激光技术, 1991, 15(6): 382-384.

Zhang Xiurong, Fan Ruiying, Wu Guangzhao, et al. The damage of dielectric mirrors from 2.94 μm laser beams in YAG: Er3+ crystal [J]. Laser Technology, 1991, 15(6): 382-384. (in Chinese)

[5] 金涛, 江绍基. 中红外高激光破坏阈值薄膜的研究[J]. 红外与激光工程, 2007, 36(5): 680-683.

Jin Tao, Jiang Shaoji. Laser damage issues of optical coating for the mid-infrared [J]. Infrared and Laser Engineering, 2007, 36(5): 680-683. (in Chinese)

[6] Lewis K L, Pitt A M, Corbett M, et al. Progress in optical coatings for the mid-infrared[C]//SPIE, 1997, 2966: 166-177.

[7] Milward J R, Lewis K, Pitt A M, et al. Laser damage issues for mid-IR optical parametric oscillator mirrors[C]//SPIE, 1994, 2114: 220-230.

[8] 晋云霞, 范瑞瑛, 邵建达, 等. 2 μm波段激光薄膜的研制[J].激光与光电子学进展, 2006, 43(10): 59-63.

Jin Yunxia, Fan Ruiying, Shao Jianda, et al. Optical coatings on laser crystal emitting at 2 μm wavelength region[J]. Laser & Optoelectronics Progress, 2006, 43(10): 59-63. (in Chinese)

[9] 王颖. 中红外激光薄膜的研究与制备[D]. 杭州: 浙江大学, 2009: 9-10.

Wang Ying. Research on the fabrication of mid-infrared dielectric coatings for laser system[D]. Hangzhou: Zhejiang University, 2009: 9-10. (in Chinese)

[10] 李丹, 朱自强, 付雄鹰, 等. 光学薄膜的激光诱导损伤与材料带隙的关系[J]. 光电工程, 1999, 26(4): 58-62.

Li Dan, Zhu Ziqiang, Fu Xiongying, et al. Relations between the laser induced damage to optical thin film and the material band-gap[J]. Opto-Electronic Engineering, 1999, 26(4): 58-62. (in Chinese)

[11] Mero M, Liu Jianhua, Zeller J, et al. Femtosecond pulse damage behavior of oxide dielectric thin films[C]//SPIE, 2004, 5273: 8-16.

[12] 胡建平, 马孜, 李伟, 等. 氧化物薄膜抗1 064 nm脉冲激光损伤的特性研究[J]. 光学学报, 2000, 20(2): 262-266.

Hu Jianping, Ma Zi, Li Wei, et al. 1 064 nm pulse laser damage of oxide coatings[J]. Acta Optica Sinica, 2000, 20(2): 262-266. (in Chinese)

[13] 叶晓雯, 丁涛, 程鑫彬, 等. 电子束蒸发 SiO2薄膜残余应力在不同湿度环境下的对比[J]. 红外与激光工程, 2012, 41(3): 713-717.

Ye Xiaowen, Ding Tao, Cheng Xinbin, et al. Contrastive investigation of the residual stress of SiO2 films prepared by electron beam evaporation in different relative humidity environments[J]. Infrared and Laser Engineering, 2012, 41(3): 713-717. (in Chinese)光学学报|2000|20|2|262-266

[14] 刘华松, 王利栓, 姜承慧, 等. SiO2薄膜的可见光与红外波段光学常数的色散特性[J]. 光学学报, 2013, 33(10): 308-313.

Liu Huasong, Wang Lishuan, Jiang Chenghui, et al. Dispersive properties of optical constants of SiO2 films in the visible and infrared regions[J]. Acta Optica Sinica, 2013, 33(10): 308-313. (in Chinese)

[15] 刘华松, 季一勤, 张锋, 等. 金属氧化物薄膜在中波红外光谱区内光学常数色散特性[J]. 光学学报, 2014, 34(8): 0831003.

Liu Huasong, Ji Yiqin, Zhang Feng, et al. Dispersive properties of optical constants of some metallic oxide thin films in the mid-infrared regions[J]. Acta Optica Sinica, 2014, 34(8): 0831003. (in Chinese)

[16] Rahe M, Ristau D, Schmidt H. The effect of hydrogen concentration in conventional and IAD coatings on the absorption and laser induced damage at 10.6 μm[C]//SPIE, 1992, 1848: 335-348.

[17] Ai Wanjun, Xiong Shengming. Characterization of hafnia thin films made with different deposition technologies[C]//SPIE, 2011, 8190: 81900J.

[18] Gross T, Dreschau F, Ristau D, et al. Characterization of laser components for high-power Ho:YAG lasers [C]//SPIE, 1998, 3244: 111-117.

赵阳, 何宇, 焦宏飞, 张锦龙, 程鑫彬, 刘华松, 李刚正, 吴晓鸣. 铥激光器腔镜用高损伤阈值氧化物薄膜的研制[J]. 红外与激光工程, 2016, 45(5): 0521001. Zhao Yang, He Yu, Jiao Hongfei, Zhang Jinlong, Cheng Xinbin, Liu Huasong, Li Gangzheng, Wu Xiaoming. Preparation of oxide films in TM laser cavity mirrors with high damage threshold[J]. Infrared and Laser Engineering, 2016, 45(5): 0521001.

铥激光器腔镜用高损伤阈值氧化物薄膜的研制

关于本站 Cookie 的使用提示

全站搜索

铥激光器腔镜用高损伤阈值氧化物薄膜的研制

相关论文

相关资讯

关于本站 Cookie 的使用提示

全站搜索