使用R-4B和GIrl作为磷光掺杂剂、CBP为主体、BPhen为发光层间隔层, 制备了包含红、绿双发光层的黄色磷光OLED器件。器件结构为ITO/MoO3(40 nm)/NPB(40 nm)/TCTA(10 nm)/CBP: GIrl(14%)(20 nm)/BPhen(x nm)/CBP: R-4B(6%)(10 nm)/BCP(10 nm)/Alq3(40 nm)/LiF(1 nm)/Al(1 000 nm)。BPhen位于两发光层之间, 具有调节载流子复合的功能, 其中x为BPhen的厚度。通过调整x的值, 研究了BPhen厚度对OLED器件发光性能的影响。实验结果表明, 适当厚度的BPhen层可以提高器件的发光亮度和电流效率。BPhen厚度为6 nm的器件性能最佳, 16 V驱动电压下的器件亮度最高可达11 270 cd/m2, 最大电流效率为24.35 cd/A, 而且绿光和红光波峰强度相近, 黄光颜色纯正, 色坐标趋近于(0.5, 0.5)。

Curved illumination is used to improve the performance of ptychographical iterative engine (PIE). Influence of illumination with different curvatures on PIE is studied. Results show that curved illumination can make the algorithm more robust to random noise and quantization error, and enhance the resolution of PIE more than three times. Thus a good reference to the choice of illumination in the PIE experiment is given.